RESUMO
The aim of this study was to evaluate the color stability of composites subjected to different periods of accelerated artificial aging (AAA). A polytetrafluorethylene matrix (10 x 2 mm) was used to fabricate 24 test specimens of three different composites (n=8): Tetric Ceram (Ivoclar/Vivadent); Filtek P90 and Z250 (3M ESPE), shade A3. After light activation for 20 s (FlashLite 1401), polishing and initial color readout (Spectrophotometer PCB 687; BYK Gardner), the test specimens were subjected to AAA (C-UV; Comexim), in 8-h cycles: 4 h exposure to UV-B rays at 50°C and 4 h condensation at 50°C. At the end of each cycle, color readouts were taken and the test ended when the mean value of ΔE attained a level ≥3.30. Tetric Ceram presented alteration in ΔE equal to 3.33 in the first aging cycle. For Filtek P90 and Z250, two (ΔE=3.60) and four (ΔE=3.42) AAA cycles were necessary. After each cycle, there was a reduction of luminosity in all the samples (ΔL). It was concluded that a short period of AAA was sufficient to promote clinically unacceptable color alteration in composites, and that this alteration was material-dependent.
O objetivo deste estudo foi avaliar estabilidade de cor de compósitos submetidos a diferentes períodos de envelhecimento artificial acelerado (EAA). Foram confeccionados, em matriz de teflon (10x2 mm), 24 corpos-de-prova de três compósitos (n=8): Tetric Ceram (Ivoclar/Vivadent); Filtek P90 e Z250 (3M ESPE), cor A3. Após fotoativação por 20 s (FlashLite 1401), polimento e leitura inicial de cor (espectrofotômetro PCB 687; BYK Gardner), os corpos-de-prova foram submetidos ao EAA (C-UV, Comexim), com ciclos de 8 h: 4 h de exposições a raios UV-B a 50°C e 4 h de condensação a 50°C. Ao final de cada ciclo, leituras de cor eram realizadas e quando o valor médio de ΔE atingisse índice ≥3,30, o ensaio era encerrado. Observou-se que Tetric Ceram apresentou alteração de ΔE igual a 3,33 já no primeiro ciclo de envelhecimento. Com Filtek P90 foram necessários dois ciclos de EAA (ΔE=3,60) e para Z250 quatro (ΔE=3,42). Observou-se que a cada ciclo ocorria diminuição na luminosidade de todas as amostras (ΔL). Concluiu-se que um curto período de EAA já é suficiente para que compósitos apresentem alteração de cor inaceitável clinicamente e que esta alteração é material dependente.