RESUMO
Abstract Objective: The aim of this study was to evaluate the shear bond strength (SBS) of brackets bonded to demineralized enamel pretreated with low viscosity Icon Infiltrant resin (DMG) and glass ionomer cement (Clinpro XT Varnish, 3M Unitek) with and without aging. Methods: A total of 75 bovine enamel specimens were allocated into five groups (n = 15). Group 1 was the control group in which the enamel surface was not demineralized. In the other four groups, the surfaces were submitted to cariogenic challenge and white spot lesions were treated. Groups 2 and 3 were treated with Icon Infiltrant resin; Groups 4 and 5, with Clinpro XT Varnish. After treatment, Groups 3 and 5 were artificially aged. Brackets were bonded with Transbond XT adhesive system and SBS was evaluated by means of a universal testing machine. Statistical analysis was performed by one-way analysis of variance followed by Tukey post-hoc test. Results: All groups tested presented shear bond strengths similar to or higher than the control group. Specimens of Group 4 had significantly higher shear bond strength values (p < 0.05) than the others. Conclusion: Pretreatment of white spot lesions, with or without aging, did not decrease the SBS of brackets.
resumo Introdução: o objetivo do presente estudo foi avaliar a resistência ao cisalhamento de braquetes colados ao esmalte desmineralizado e pré-tratado com uma resina infiltrante de baixa viscosidade (Icon, DMG) ou com um selante ionomérico (Clinpro XT Varnish, 3M Unitek), com e sem envelhecimento. Métodos: setenta e cinco (75) amostras de esmalte bovino foram divididas em cinco grupos (n = 15). No Grupo 1 (controle), a superfície do esmalte não foi desmineralizada. Nos outros quatro grupos, as superfícies foram submetidas ao desafio cariogênico e as lesões de manchas brancas foram tratadas previamente à colagem de braquetes. Nos Grupos 2 e 3, as lesões foram tratadas com a resina Icon; nos Grupos 4 e 5, com o selante Clinpro XT Varnish. Após o tratamento, os Grupos 3 e 5 foram envelhecidos artificialmente. Os braquetes foram colados, sobre as lesões tratadas, utilizando-se o sistema adesivo Transbond XT, e a resistência ao cisalhamento foi avaliada em máquina universal de ensaios. A análise estatística foi realizada por meio da análise de variância e, posteriormente, pelo teste post-hoc de Turkey. Resultados: todos os grupos testados apresentaram resistência ao cisalhamento semelhante ou maior do que o grupo controle. As amostras do Grupo 4 apresentaram valores de resistência ao cisalhamento significativamente maiores (p < 0,05) do que as dos demais grupos. Conclusão: o tratamento das manchas brancas, com ou sem envelhecimento, não diminuiu a resistência ao cisalhamento dos braquetes.