Comparison of Bio-degradation for Ridge Preservation Using Silk Fibroin-based Grafts and a Collagen Plug

A material for ridge preservation should have dimensional stability to resist bio-degradation. This study was designed to compare bio-degradation of ridge preservation materials. Collagen plug was used as a positive control. Untreated, ethanol-treated, and 4-hexylresorcinol (4HR)-treated silk plugs were used for the experimental group. Each material underwent a scanning electron microscopic exam and a Fourier transform infrared (FT-IR) spectroscopic exam. Bio-degradation was evaluated by analyzing cylindrical bony defects in rabbit tibias. There were no prominent differences in microstructure among the silk plug groups. FT-IR exam demonstrated that the ethanol- and 4HR-treated silk plug groups had enhanced β-sheet structure. All silk plug groups exhibited significantly higher residual graft than the collagen plug group 4 weeks postoperative (p<0.05). In conclusion, silk fibroin-based ridge preservation material was less bio-degradable than a collagen plug until at least 4 weeks after grafting.

The effect of 4-hexylresorcinol on xenograft degradation in a rat calvarial defect model / 대한악안면성형재건외과학회지

BACKGROUND: The objective of this study was to evaluate xenograft degradation velocity when treated with 4-hexylresorcinol (4HR). METHODS: The scapula of a cow was purchased from a local grocery, and discs (diameter 8 mm, thickness 1 mm) were prepared by trephine bur. Discs treated with 4HR were used as the experimental group. Untreated discs were used as the control. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), antibacterial test, endotoxin test, and scanning electron microscopy (SEM) were performed on the discs. In vivo degradation was evaluated by the rat calvarial defect model. RESULTS: The XRD and FT-IR results demonstrated successful incorporation of 4HR into the bovine bone. The experimental disc showed antibacterial properties. The endotoxin test yielded results below the level of endotoxin contamination. In the SEM exam, the surface of the experimental group showed needle-shaped crystal and spreading of RAW264.7 cells. In the animal experiments, the amount of residual graft was significantly smaller in the experimental group compared to the control group (P = 0.003). CONCLUSIONS: In this study, 4HR was successfully incorporated into bovine bone, and 4HR-incorporated bovine bone had antibacterial properties. In vivo experiments demonstrated that 4HR-incorporated bovine bone showed more rapid degradation than untreated bovine bone.