Influence of masticatory fatigue on the fracture resistance of the pulpless teeth restored with quartz-fiber post-core and crown / 国际口腔科学杂志·英文版

To investigate whether masticatory fatigue affects the fracture resistance and pattern of lower premolars restored with quartz-fiber post-core and full crown, 44 single rooted lower premolars recently extracted from orthodontic patients were divided into two groups of 22 each. The crowns of all teeth were removed and endodontically treated and then restored with quartz-fiber post-core and full crown. Twenty-two teeth in one group were selected randomly and circularly loaded at 45° to the long axis of the teeth of 127.4 N at a 6 Hz frequency, and the other group was not delivered to cyclic loading and considered as control. Subsequently, all teeth in two groups were continually loaded to fail at 45° to the long axis of the teeth at a crosshead speed of 1 mm⋅min(-1). The mean destructive force values were (733.88±254.99) and (869.14±280.26) N for the experimental and the control group, respectively, and no statistically significant differences were found between two groups (P>0.05). Bevel fracture and horizontal fracture in the neck of root were the major fracture mode of the specimens. Under the circumstances of this study, it seems that cyclic loading does not affect the fracture strength and pattern of the quartz-fiber post-core-crown complex.

Influence of bone quality on the stress distribution for three-posterior immediately loaded implants: a three-dimensional finite element analysis / 中华口腔医学杂志

<p><b>OBJECTIVE</b>To assess and compare the peri-implant stress distribution of three posterior implants under immediate loading with 4 different bone qualities using three dimensional (3D) finite element (FE) analysis.</p><p><b>METHODS</b>A 3D finite element model representing three implants in a portion of mandible at the 654 region was developed, and three implants received a crown each. Four types of bone qualities (B1, B2, B3 and B4) were designed for the model. Load of 100 N was applied on the occlusal surfaces of the crowns at a 45° angle to the vertical axis of the implants.</p><p><b>RESULTS</b>Von Mises stresses in the peri-implant bone of 4 in bone quality from B1 to B4 were (13.17 ± 9.32), (12.95 ± 9.14), (15.00 ± 9.44), and (16.81 ± 10.74) MPa, and those of 5 were (15.51 ± 10.32), (14.73 ± 8.96), (16.79 ± 8.40), and (18.34 ± 8.45) MPa. Stress in bone quality B4 showed the highest value, followed by B3 bone, the lowest stress were found in B1 and B2 bone. It was significantly different (P < 0.05). However, von Mises stresses in different quality of bone around 6 [(42.45 ± 25.71), (41.66 ± 25.29), (42.70 ± 23.24), (42.06 ± 23.66) MPa] were close to each other, and were as twice or three times as those of 4 and 5, irrespective of different bone qualities.</p><p><b>CONCLUSIONS</b>The stress distribution around implant under immediate loading was not only affected by different bone qualities, but also by the direction of loading, and the latter may have a greater impact when a severe load delivered.</p>