The effect of bur preparation on the surface roughness and reline bond strength of urethane dimethacrylate denture base resin.

Background: The clinical success of relining depends on the ability of reline resin to bond to denture base. Surface preparations may influence reline bond strength of urethane-based dimethacrylate denture base resin. Aim: To investigate the effect of bur preparation on the surface roughness (R a ) of eclipse denture base resin and its shear bond strength (SBS) to an intra-oral self-curing reline material. The mode of reline bonding failure was also examined. Materials and Methods: Twenty-four cylindrical Eclipse™ specimens were prepared and separated into three groups of eight specimens each. Two groups were subjected to mechanical preparation using standard and fine tungsten carbide (TC) burs and the third group (control) was left unprepared. The R a of all specimens was measured using a contact stylus profilometer. Subsequently, relining was done on the prepared surface and SBS testing was carried out a day later using a universal testing machine. Results: One-way ANOVA revealed significant differences (P<0.05) in R a and SBS values for all the groups. Post-hoc Tukey's HSD test showed significant differences (P<0.05) between all the groups in the R a values. For SBS also there were significant differences (P<0.05), except between standard bur and control. Conclusions: 1) There was a statistically significant difference in the R a of Eclipse™ specimens prepared using different carbide burs (P<0.05). 2) There was a statistically significant difference in the relined SBS (P<0.05) when prepared using different burs, but the difference between the standard bur and the control group was not statistically significant.

Effect of cavity preparation on the flexural strengths of acrylic resin repairs

OBJECTIVE: To investigate the effect of cavity preparation on the flexural strength of heat-curing denture resin when repaired with an auto-curing resin. MATERIAL AND METHODS: Ninety-six rectangular specimens (64x10x2.5 mm) prepared from heat-curing denture base resin (Meliodent) were randomly divided into four groups before repair. One group was left intact as control. Each repair specimen was sectioned into two; one group was repaired using the conventional repair method (Group 1). Two groups had an additional transverse cavity (2x3.5x21.5 mm) prepared prior to the repair; one repaired with (Group 2) and one without glass-fiber reinforcement (Group 3). A three-point flexural bending test according to the ISO 1567:1999 specification8 for denture base polymers was carried out on all groups after 1, 7 and 30 days of water immersion. Statistical analysis was carried out using two-way ANOVA, Kruskal Wallis and post-hoc Mann Whitney tests. RESULTS: The highest flexural strength was observed in the control group. Control and conventional repairs group (Group 1) showed reduction in the flexural strength 30 days after water immersion. No significant change in the strength was observed for Groups 2 and 3 where the repair joints were similarly prepared with additional transverse cavity. CONCLUSION: Repaired specimens showed lower flexural strength values than intact heat-curing resin. Cavity preparation had no significant effect on the flexural strength of repair with water immersion.