Marginal gap of zirconia and lithium disilicate frameworks produced by the CAD-CAM technique through a comparator microscope ­ in vitro analysis / Fenda marginal de estruturas de zircônia e dissilicato de lítio produzidas pela técnica CAD-CAM através de um microscópio comparador ­ análise in vitro

Objective: The aim of this study was to evaluate the marginal gap of frameworks produced using the CAD-CAM system, from zirconia and lithium disilicate blocks, adapted to a tooth preparation and a gypsum die. Material and Methods: For this study, a human first molar tooth was used as a master model with a full crown preparation. It was molded 20 times to obtain the gypsum die and randomly divided into 2 groups (n=10) for the fabrication of zirconia and lithium disilicate frameworks. The frameworks were made using pre-sintered zirconia blocks and lithium disilicate blocks, both CAD-CAM systems. The marginal gap was measured in µm at four points (buccal, palatal, mesial, and distal) using a comparator microscope with 30x magnification, with the framework seated on the master model (tooth), and on the gypsum die. Marginal gap data (µm) were evaluated using two-way analysis of variance and Tukey's test with a significance level of 5%. Results: The results showed that there was no statistically significant interaction between the factors studied (p=0.223) or isolated factors (ceramic factor p=0.886 and die factor p=0.786). Conclusion: Both ceramics produced using the CAD-CAM technique did not exhibit statistical differences in marginal adaptation on the two types of substrates, both on tooth preparation and on the gypsum die (AU)

Objetivo: O objetivo deste estudo foi avaliar o espaço marginal de estruturas produzidas usando o sistema CAD-CAM, a partir de blocos de zircônia e dissilicato de lítio, adaptadas a um preparo sobre dente e a um troquel de gesso. Material e Métodos: Para este estudo, um dente molar humano foi utilizado como modelo mestre com preparo para coroa total. Este foi moldado 20 vezes para obter o troquel de gesso e dividido aleatoriamente em 2 grupos (n=10) para a fabricação de estruturas de zircônia e dissilicato de lítio. As estruturas foram feitas usando blocos de zircônia pré-sinterizados e blocos de dissilicato de lítio, ambos sistemas para CAD-CAM. O espaço marginal foi medido em µm, em quatro pontos (bucal, palatal, mesial e distal), utilizando um microscópio comparador com ×30 de ampliação e com a estrutura assentada no modelo mestre (dente) e no troquel de gesso. Os dados de espaço marginal (µm) foram avaliados usando análise de variância bidirecional e teste de Tukey com um nível de significância de 5%. Resultados: Os resultados mostraram que não houve interação estatisticamente significativa entre os fatores estudados (p=0,223) ou isoladamente (fator cerâmica p=0,886 e fator troquel p=0,786). Conclusão: Ambas as cerâmicas produzidas usando a técnica CAD-CAM não apresentaram diferenças estatísticas em relação à adaptação marginal nos dois tipos de substratos, tanto na preparação dentária quanto no troquel de gesso(AU)

Tratamentos de superfície prévios à camada de caracterização: efeitos na resistência adesiva e comportamento mecânico de cerâmicas de óxido de zircônio / Surface treatments prior to the characterization layer: effects on bond strength and mechanical behavior of zirconium oxide ceramics

Este estudo avaliou o efeito do jateamento com óxido de alumínio prévio à camada de caracterização no comportamento adesivo e mecânico de zircônias de segunda e terceira gerações. Na parte A, foi realizado um estudo de resistência flexural. Para isso, discos de cada zircônia (3Y-TZP, 4Y-PSZ ou 5YPSZ) foram confeccionados. Após polimento e sinterização, os discos foram divididos de acordo com os tratamentos de superfície: Polimento, Jateamento com Al2O3 50 µm e Jateamento com Al2O3 110 µm (n = 30). A superfície tratada de todos os discos recebeu uma fina camada de pigmentação e uma fina camada de glaze. O ensaio de flexão biaxial foi realizado na configuração pistonon-three-balls e as superfícies fraturadas foram observadas em Microscopia Eletrônica de Varredura (MEV). Os dados foram submetidos à Análise de Weibull. Na parte B, avaliou-se o efeito dos diferentes tratamentos de superfície prévio à camada de caracterização no comportamento à fadiga das diferentes zircônias. Discos de 3Y-TZP, 4Y-PSZ e 5Y-PSZ foram confeccionados e distribuídos entre os tratamentos de superfície: Polimento ou Jateamento Al2O3 50 µm (n = 15), que foram realizados conforme a parte A deste estudo. Os discos foram cimentados adesivamente a um análogo de dentina (NEMA G10). Os testes de fadiga foram realizados pelo método stepwise, com aplicação de carga axial por um pistão hemisférico (carga inicial: 400 N, step: 100 N, ciclos/step: 10.000, frequência: 20 Hz). Na parte C, avaliou-se a resistência de união entre as diferentes zircônias e a camada de caracterização. Foram preparados os mesmos grupos descritos na "parte A" (n = 15). Cilindros de stain seguido por glaze foram construídos nas superfícies das zircônias. A resistência de união foi avaliada pelo teste de cisalhamento. Os tipos de falha (adesiva, predominantemente adesiva ou coesiva) foram analisados em estereomicroscópio e MEV. Análises complementares em perfilômetro e goniômetro foram realizadas. Para a parte A, o jateamento com Al2O3 110 µm aos menores valores de resistência à flexão, seguido do jateamento com as partículas de Al2O3 50 µm. Os maiores valores foram observados no grupo que não recebeu jateamento prévio à camada de caracterização. Esses resultados foram observados em todos os materiais. Na parte B, o jateamento com Al2O3 reduziu significativamente a carga e o número de ciclos para falha em fadiga de todos os materiais. Na parte C, os melhores valores de resistência de união foram atribuídos para o tratamento de superfície com Al2O3 110 µm, seguido de jateamento com Al2O3 50 µm e polimento. Dessa forma, o jateamento prévio à camada de caracterização reduz a resistência mecânica de zircônias de segunda geração e melhora a resistência de união entre os dois materiais (AU)

This study evaluated the effect of aluminum oxide sandblasting prior to the characterization layer on the adhesive and mechanical behavior of second- and third-generation zirconia. Part A consisted of a flexural strength study. Discs of each zirconia (3Y-TZP, 4Y-PSZ, or 5Y-PSZ) were prepared. After polishing and sintering, the discs were divided according to the surface treatments: Polishing, Sandblasting with Al2O3 50 µm and Sandblasting with Al2O3 110 µm (n = 30). The treated surface of all discs received a thin layer of stain and a thin layer of glaze. The biaxial bending test was performed in a piston-on-three-balls set-up. The fractured surfaces were observed by Scanning Electron Microscopy (SEM). Data were subjected to Weibull Analysis. In part B, the effect of different surface treatments prior to the characterization layer on the fatigue behavior of different zirconia was evaluated. Discs of 3Y-TZP, 4Y-PSZ and 5Y-PSZ were prepared and divided among the surface treatments: Polishing or Sandblasting Al2O3 50 µm (n = 15), which were performed according to part A of this study. The discs were adhesively cemented to a dentin-analogue (NEMA G10). Fatigue tests were performed using the stepwise method, with an axial load application by a hemispherical piston (initial load: 400 N, step: 100 N, cycles/step: 10,000, frequency: 20 Hz). Part C evaluated the bond strength between the different zirconia and the characterization layer. The same groups described in part A (n = 15) were prepared. Stain cylinders followed by glaze were built on the zirconia surfaces. The bond strength was evaluated by the shear test. The types of failure (adhesive, predominantly adhesive or cohesive) were analyzed using a stereomicroscope and SEM. Complementary analyzes in profilometer and goniometer were carried out. In part A, sandblasting with Al2O3 110 µm led to the lowest flexural strength results, followed by sandblasting with Al2O3 50 µm. Polishing group achieved the highest values. These results were observed in all tested ceramics. In part B, sandblasting with Al2O3 50 µm significantly reduced the fatigue failure load and the number of cycles for fatigue failure. In part C, the highest bond strength results were reached by sandblasting with Al2O3 110 µm, followed by sandblasting with Al2O3 50 µm, and polishing. Therefore, aluminum oxide particles sandblasting diminishes the mechanical behavior of second- and third-generation zirconias and improves the bond strength between the two materials. (AU)

Efeito do envelhecimento hidrotérmico e mecânico na performance à fadiga de zircônias de alta translucidez / Effect of hydrothermal and mechanical aging on the fatigue performance of high-translucency zirconias

O objetivo deste trabalho foi avaliar a resistência à fadiga e ciclos até a falha de 3 zircônias odontológicas após envelhecimento hidrotérmico isolado e um novo protocolo alternado. Discos de zircônia "Y"Z T (VITA), INCORIS "T"ZI (Dentsply Sirona) e "K"ATANA UTML (Noritake Kuraray) (N=135) ­ 1ª, 2ª e 3ª gerações, respectivamente ­, foram divididos em 9 grupos (n=15), com 3 tratamentos para cada zircônia: CF ­ Controle, somente com fadiga mecânica; EF ­ Envelhecido em reator hidrotérmico a 134 ºC por 20 h + Fadiga; EFA: 4 passos de envelhecimentos de 5h alternados com fadiga. O teste de fadiga em flexão biaxial foi realizado com configuração de pistão sob 3 esferas, utilizando o método step-stress (carga inicial: 100 Mpa, step: 50 MPa/10.000 ciclos, frequência: 20 Hz). Os dados foram analisados através de teste Kaplan-Meir e Mantel-Cox com α=0,05, além da análise de Weibull. Discos fraturados foram analisados em estereomicroscópio, Microscopia Eletrônica de Varredura (MEV) e Difratômetro de Raios-X (DRX). O envelhecimento isolado com fadiga aumentou a resistência do grupo TEF (810 ± 76 MPa), enquanto diminuiu a do YEF (516 ± 38 MPa), o protocolo alternado aumentou a resistência apenas para a YZ T (730 ± 59 MPa). A KATANA UMTL não apresentou diferenças para ambos os tratamentos. Igualmente, foi a única a não sofrer transformação de fase T-M. O grupo TEF apresentou maior taxa sobrevivência à fadiga (147,000.00 ciclos). A origem de fratura para todos os espécimes deu-se no lado de tração em defeitos pré-existentes. Zircônias de 2ª geração possuem melhor comportamento mecânico e longevidade pós-envelhecimento e fadiga. Embora seja menos resistente, a KATANA UTML não sofreu degradação

This study aimed to evaluate the fatigue strength and cycles for failure of 3 dental zirconias after isolated and a novel hydrothermal and mechanical fatigue cycling aging protocol. "Y"Z T (VITA), INCORIS "T"ZI (Dentsply Sirona) and "K"ATANA UTML (Noritake Kuraray) zirconia discs (N=135), were divided into 9 groups (n=15), according to 3 proposed treatments for each zirconia: CF (control ­ only mechanical fatigue cycling); AF (aging in hydrothermal reactor at 134°C for 20 h + mechanical fatigue cycling ); AFA (Alternating protocol: 4 steps of 5 h of hydrothermal aging intercalated with mechanical fatigue cycling). Mechanical fatigue aging was performed according to the step stress approach through biaxial flexural setup (piston-on-3-balls, initial strength: 100 MPa, step: 50 MPa/ci000, frequency: 20 Hz) until failure. Data were analyzed using KaplanMeier and Mantel-Cox test (α=0.05), in addition to Weibull analysis. Fractured discs were analyzed in stereomicroscope, Scanning Electron Microscopy and XRay Diffraction. Continuous hydrothermal and mechanical fatigue cycling decreased the fatigue strength of YAF group (516 ± 38 MPa), while the alternating protocol increased it (730 ± 59 MPa). KATANA UTML showed no differences for both treatments and did not undergo T-M phase transformation. The TAF group showed the highest fatigue strength (810 ± 76 MPa) and cycles for failure (147,000.00 cycles). The fracture origin for all specimens was on the tensile side in pre-existing defects. INCORIS TZI zirconia have higher fatigue strength after hydrothermal and mechanical fatigue aging. Although less resistant, KATANA UTML did not suffer chemical degradation

Laminados cerâmicos: técnica não invasiva / Laminate veneer: non-invasive technique

Atualmente, o cuidado com a estética vem sendo valorizado de tal forma que, além de ser um referencial de saúde, ter um sorriso bonito significa também estar em harmonia consigo mesmo e ser uma pessoa bem sucedida. Dentro da Odontologia, a procura por um sorriso harmonioso e bonito vem crescendo a cada dia. Essa busca está diretamente relacionada a fatores sociais, culturais e psicológicos, que se alteram em função do tempo, dos valores de vida e da idade do indivíduo. Uma alternativa para a correção de imperfeições nos dentes é a utilização dos laminados cerâmicos que restabelecem a forma, cor, função e harmonia do sorriso, além de proporcionar longevidade do tratamento e satisfação plena do cliente. Os laminados cerâmicos são indicados para a correção de imperfeições dentárias, fraturas e dentições desgastadas pelas forças mastigatórias, substituindo estruturas defeituosas por um esmalte artificial integrado funcional e biologicamente aos tecidos dentários e periodontais. O estudo da resistência à fratura e à fadiga dos laminados cerâmicos fornece dados relativos ao reforço, estabilidade e a manutenção da estrutura dentária, prevenindo o preparo total da coroa dental. O presente relato apresenta, com base na literatura, uma reabilitação estética do sorriso usando laminados cerâmicos sem realização de preparo ou desgaste dos dentes. A comunicação harmônica entre o cirurgião dentista, TPD e os critérios científicos de planejamento são de fundamental importância para a obtenção resultados estéticos e funcionais com longevidade clínica.

Nowadays, the care with aesthetics aspects has been valued in such a way that, besides being an indicator of health, a beautiful smile is also associated to be in harmony with yourself and being a successful person. In Dentistry, the search for a beautiful and harmonious smile is increasing each day. This search is directly related to social, psychological and cultural factors that change with time, as with life values and age of the person. An alternative to correct dental imperfections is the use of laminate veneers that restore the shape, color, function and harmony of the smile, as well as provide longevity to the treatment and the complete satisfaction of the patient. The laminate veneers are indicated for the correction of dental imperfections, fractures and teeth worn by chewing forces, replacing defective structures by artificial enamel functionally and biologically integrated to the dental and periodontal tissues. The study on fracture and fatigue resistance of the laminate veneer provides data on the reinforcement, stability and maintenance of the dental structure, preventing the total preparation of the dental crown. This report is based on the literature and presents an aesthetical rehabilitation of the smile using laminate veneers without the realization of preparation or wear of the teeth. An effective communication between dentist surgeon, dental technician and the scientific criteria of planning are fundamental for obtaining aesthetic and functional results with clinical longevity.

Odontologia assistida por computação – utilização datecnologia CAD/CAM para confecção de restauraçõescerâmicas / Computer assisted dentistry – using CAD/CAM technology to fabricate ceramic restorations

A Odontologia, de maneira geral, se vale gradualmentede processos manuais para a consecuçãode seus objetivos de tratamento e prevenção. A especialidadede prótese, em particular, dada à suapeculiaridade da necessidade de intervenção deum técnico de laboratório, acentua a fase artesanalda Odontologia. Não obstante, processos informatizadosde produção de restaurações protéticasvêm sendo incorporados, acompanhando o desenvolvimentode novas tecnologias. O processo deinformatização de produção de coroas, conhecidopela sigla CAD/CAM, está mudando não somentea tríade de relacionamento entre dentista/técnico/paciente, como também os materiais envolvidosnos tratamentos odontológicos. Neste contexto, énecessário conhecer profundamente as características,vantagens e desvantagens de cada sistema,para garantir longevidade estética e funcional dasrestaurações protéticas.

Dentistry, in general, relies heavily on manualprocesses to achieve its goals of treatmentand prevention. The specialty of prosthesis,in particular, given the peculiarity of the needfor intervention by a lab technician, emphasizesthe craft stage of dentistry. Nevertheless,computing processes of production ofprosthetic restorations have been incorporatedfollowing the development of newtechnologies. The computerized process ofproducing crowns, known by the acronymCAD / CAM, is changing not only the triadrelationship between dentist / technician /patient, but the materials involved in dentaltreatment. In this context, it is necessary toknow in depth the characteristics, advantagesand disadvantages of each system, toensure longevity of esthetic and functionalprosthetic restorations.

Avaliação da retenção de coroas de ytrio-zircônia cimentadas a diferentes substratos, com quatro agentes cimentantes, após termociclagem / Evaluation of the tensile strength of all-ceramic crowns on different substrates and cementing agents after thermal cycling

Este trabalho teve a finalidade de avaliar o efeito do tipo de substrato coronário (dentina e resina composta) na retenção de coroas cerâmicas de zircônia estabilizada por óxido de ítrio e comparar a retenção em função de diferentes protocolos. Para tanto, 144 molares recém-extraídos foram embutidos em resina acrílica, perpendicular ao seu longo eixo e preparados para coroa total, 72 permaneceram com o preparo em dentina e os demais, a parte coronáriapreparada foi removida e reconstruída em resina composta + pinos de fibracom dimensões idênticas à dentina preparada. Os preparos foram moldadoscom silicona de adição e dos troqueis foram obtidos 144 copings em YTZP, osquais apresentaram uma configuração especial para o ensaio de tração. Paraambos substratos, foi utilizado como grupo controle (n=12) um cimento à base de fosfato de zinco (sem condicionamento do substrato e da cerâmica). Os outros cimentos utilizados foram: um cimento à base de ionômero de vidro, um cimento resinoso da geração auto-condicionate (ambos sem condicionamento do substrato e da cerâmica) e um cimento Dual contendo monômeros fosfatados (MDP). Neste ultimo grupo, os remanescentes (dentina ou resina) foram condicionados com o adesivo correspondente do sistema e a cerâmica foi submetida a 3 tratamentos de superfície: álcool isopropílico, silicatização/silanização ou Vitrificação. Após 24h, todos os conjuntos foram submetidos a termocilagem (6000 ciclos) e incluídos em um dispositivo especial para o teste de tração em uma máquina de ensaio universal, para testar a retenção das infra-estruturas. Os modos de falha de todos os conjuntos foram analisados em estereomicroscópio e MEV para avaliar as possíveis causas de falha Os dados foram analisados estatisticamente. Osresultados mostraram na dentina, que o cimento à base de ionômero de vidroe o cimento à base de MDP, independente do tratamento de superfície, resultaram em maiores valores de retenção. Na resina, o cimento à base ...(AU)

The aim of this study was to evaluate the effect of the crown substratetype (dentine and composite resin) in the retention of stabilized zirconiaceramic crowns by yttrium oxide (YTZP) and to compare the retention function of four types of cements, four treatments of the substrate surface and three treatments of the ceramic surface. For this purpose, 144 freshly extracted molars were embedded in acrylic resin, perpendicular to the long axis and prepared for full crowns, 72 remained with the preparation in dentin and the other, the crown part was removed and reconstructed with composite resin + fiber pins with dimensions identical to the prepared dentin. The preparations were moulded with addition silicone and 144 YTZP copings were obtained, which presented a special setup for thetensile test. For the remainin, a phosphate-based cement zinc (unprimedsubstrate and ceramics) (n = 12) was used as the control group. The otherused cements were: a glass-ionomer based cement, a resin cement fromself-condicionating generation (unprimed substrate and ceramic) and aDual cement containing phosphate monomer. In the latter groups, theremaining (dentin or resin) was conditioned with the adhesive system and the corresponding ceramic was subjected to three surface treatments:isopropyl alcohol, silica coating / silanization or Overglaze. After 24 hours,all sets were submitted to thermocycling (6000 cycles) and included in aspecial device for the tensile test in a universal testing machine to test theretention of the infrastructure. The failure modes of all sets were analyzedunder a stereomicroscope and SEM to evaluate possible causes of failure.Data was analyzed statistically. The results showed that in dentin, theglass-ionomer based cement and the MDP-based cement, regardless thesurface treatment, resulted in higher retention values. In the resin, theMDP-based cement, associated with the...

Avaliação da retenção de coroas de ytrio-zircônia cimentadas a diferentes substratos, com quatro agentes cimentantes, após termociclagem / Evaluation of the tensile strength of all-ceramic crowns on different substrates and cementing agents after thermal cycling

Este trabalho teve a finalidade de avaliar o efeito do tipo de substrato coronário (dentina e resina composta) na retenção de coroas cerâmicas de zircônia estabilizada por óxido de ítrio e comparar a retenção em função de diferentes protocolos. Para tanto, 144 molares recém-extraídos foram embutidos em resina acrílica, perpendicular ao seu longo eixo e preparados para coroa total, 72 permaneceram com o preparo em dentina e os demais, a parte coronáriapreparada foi removida e reconstruída em resina composta + pinos de fibracom dimensões idênticas à dentina preparada. Os preparos foram moldadoscom silicona de adição e dos troqueis foram obtidos 144 copings em YTZP, osquais apresentaram uma configuração especial para o ensaio de tração. Paraambos substratos, foi utilizado como grupo controle (n=12) um cimento à base de fosfato de zinco (sem condicionamento do substrato e da cerâmica). Os outros cimentos utilizados foram: um cimento à base de ionômero de vidro, um cimento resinoso da geração auto-condicionate (ambos sem condicionamento do substrato e da cerâmica) e um cimento Dual contendo monômeros fosfatados (MDP). Neste ultimo grupo, os remanescentes (dentina ou resina) foram condicionados com o adesivo correspondente do sistema e a cerâmica foi submetida a 3 tratamentos de superfície: álcool isopropílico, silicatização/silanização ou Vitrificação. Após 24h, todos os conjuntos foram submetidos a termocilagem (6000 ciclos) e incluídos em um dispositivo especial para o teste de tração em uma máquina de ensaio universal, para testar a retenção das infra-estruturas. Os modos de falha de todos os conjuntos foram analisados em estereomicroscópio e MEV para avaliar as possíveis causas de falha Os dados foram analisados estatisticamente. Osresultados mostraram na dentina, que o cimento à base de ionômero de vidroe o cimento à base de MDP, independente do tratamento de superfície, resultaram em maiores valores de retenção. Na resina, o cimento à base...

The aim of this study was to evaluate the effect of the crown substratetype (dentine and composite resin) in the retention of stabilized zirconiaceramic crowns by yttrium oxide (YTZP) and to compare the retention function of four types of cements, four treatments of the substrate surface and three treatments of the ceramic surface. For this purpose, 144 freshly extracted molars were embedded in acrylic resin, perpendicular to the long axis and prepared for full crowns, 72 remained with the preparation in dentin and the other, the crown part was removed and reconstructed with composite resin + fiber pins with dimensions identical to the prepared dentin. The preparations were moulded with addition silicone and 144 YTZP copings were obtained, which presented a special setup for thetensile test. For the remainin, a phosphate-based cement zinc (unprimedsubstrate and ceramics) (n = 12) was used as the control group. The otherused cements were: a glass-ionomer based cement, a resin cement fromself-condicionating generation (unprimed substrate and ceramic) and aDual cement containing phosphate monomer. In the latter groups, theremaining (dentin or resin) was conditioned with the adhesive system and the corresponding ceramic was subjected to three surface treatments:isopropyl alcohol, silica coating / silanization or Overglaze. After 24 hours,all sets were submitted to thermocycling (6000 cycles) and included in aspecial device for the tensile test in a universal testing machine to test theretention of the infrastructure. The failure modes of all sets were analyzedunder a stereomicroscope and SEM to evaluate possible causes of failure.Data was analyzed statistically. The results showed that in dentin, theglass-ionomer based cement and the MDP-based cement, regardless thesurface treatment, resulted in higher retention values. In the resin, theMDP-based cement, associated with the...

Sistemas cerâmicos atuais: revisão de literatura / Current ceramic systems: literature review

A fabricação de restaurações em cerâmica está se tornando cada vez mais popular, devido ao crescente avanço na qualidade desse material e na tecnologia empregada na confecção dessas restaurações. Essa evolução ocorreu graças, principalmente, à tecnologia CAD/CAM, que possibilitou o uso de cerâmicas de alta resistência na fabricação de próteses sem metal, com qualidade e uniformidade, padronizando os processos e reduzindo custos. O objetivo deste trabalho é realizar uma revisão da literatura dos sistemas cerâmicos existentes, bem como descrever os aspectos relacionados à estética, propriedades mecânicas, adaptação marginal, caracteristicas dos pônticos e conectores, e modo de cimentação, procurando mostrar as vantagens, desvantagens, indicações e contra-indicações da cada sistema.

Comportamento mecânico de cerâmicas utilizadas na confecção de próteses parciais fixas / Mechanical behavior of ceramic materials used for fixed partial dentures

Objetivos: determinar a resistência à flexão em três pontos (f), módulo de Weibull (m), coeficiente de susceptibilidade ao crescimento subcrítico de trinca (n) e tenacidade à fratura (KIC) de três cerâmicas usadas para confecção de infraestrutura (IE) de próteses parciais fixas (PPFs) (YZ- zircônia tetragonal parcialmente estabilizada por óxido de ítrio; IZ- cerâmica a base de alumina infiltrada por vidro e reforçada com zircônia; AL alumina policristalina) e duas porcelanas (VM7 e VM9); avaliar o efeito da configuração (uma, duas ou três camadas) nos valores de f e modo de fratura dos corpos-de-prova (CP); avaliar a influência do material de IE, do tamanho dos conectores e da ciclagem mecânica (CM) na carga de fratura (CF) e distribuição de tensões de PPFs; relacionar o comportamento mecânico dos materiais cerâmicos testados na configuração de barra e de PPF. Material e Método: Foram produzidos três tipos de CP em forma de barra (2mm x 4mm x 16mm): monolítico, duas camadas e três camadas. As IE das PPFs foram confeccionadas utilizando o sistema CAD-CAM e recobertas com porcelana. Os ensaios de f foram realizados em saliva artificial a 37ºC. Os valores de m e n foram determinados pela análise de Weibull e ensaio de fadiga dinâmica, respectivamente. As PPFs foram carregadas no centro do pôntico até a fratura. Oito PPFs de cada grupo foram submetidas a CM com freqüência de 2 Hz e carga de 140 N durante 106 ciclos e, posteriormente, ensaiadas até a fratura. A distribuição de tensões nas PPFs foi avaliada com análise de elementos finitos (AEF). Os princípios da fractografia foram utilizados para determinar o padrão de fratura e os valores de KIC. Os dados de f e CF foram analisados estatisticamente com Kruskal-Wallis e Tukey (95%)...

Objectives: to determine the flexural strength (f), Weibull modulus (m), slow crack growth coefficient (n) and fracture toughness (KIC) of three ceramics used as framework materials for fixed partial dentures (FPDs) (YZ- yttria partially stabilized zirconia tetragonal polycrystals; IZ- alumina-based zirconia-reinforced glass infiltrated ceramic; AL alumina polycrystals) and two veneering porcelains (VM7 and VM9); to evaluate the effect of the specimen design (one, two or three layers) in the f and fracture mode; to evaluate the influence of the framework material, connector size and mechanical cycling (MC) in the fracture load (FL) and stress distribution of FPDs; to relate the mechanical behavior of the ceramic materials tested using bar-shaped specimens and FPDs. Materials and Methods: Bar-shaped specimens (2mm x 4mm x 16mm) were produced in three different designs: monolithic, bilayer and trilayer. FPD frameworks were built using CAD-CAM system and veneered with porcelain. Specimens were tested for three point bending in 37ºC artificial saliva. Weibull analysis and dynamic fatigue testing were used to determine m and n values, respectively. FPDs were tested with a load applied in the middle of the pontic. Eight FPDs of each group were subjected to MC using a frequency of 2Hz and load of 140N for 106 cycles and were subsequently loaded to failure. Stress distribution for FPDs was evaluated using finite element analysis (FEA). Fractography principles were used to determine the fracture mode and KIC values. f and FL data were analyzed using Kruskal-Wallis and Tukey (95%)...

Crescimento de trinca subcrítico em cerâmicas odontológicas: efeito do material (microestrutura) e do método de ensaio / Growth of crack subcrítico in dental ceramics: effect of the material (Microstructure) and the test method

O objetivo deste trabalho foi realizar a caracterização microestrutural e das propriedades mecânicas de diferentes cerâmicas odontológicas para entender sua influência nos parâmetros de crescimento de trinca subcrítico (SCG), n (coeficiente de susceptibilidade ao SCG) e ?f0 (parâmetro escalar), determinados por diferentes métodos. Cinco cerâmicas foram avaliadas: porcelanas VM7 (Vita) e D (d.Sign, Ivoclar), vitrocerâmicas E1 (IPS Empress, Ivoclar) e E2 (IPS Empress 2, Ivoclar) e compósito IC (In-Ceram Alumina, Vita). Espécimes em forma de disco (12 mm x 1 mm) foram confeccionados segundo as recomendações dos fabricantes. A caracterização microestrutural dos materiais foi realizada. A tenacidade à fratura (KIc) foi determinada pelo método da fratura por indentação (IF) e indentation strength. Os parâmetros de SCG foram determinados por fadiga dinâmica (com diferentes taxas de tensão constante), fadiga estática (com diferentes níveis de tensão constante) e fadiga por IF. Os resultados mostraram que todas as cerâmicas constituíram-se de fase vítrea e cristalina, com exceção da VM7, composta somente por fase amorfa. D e E1 apresentaram partículas de leucita, em frações volumétricas iguais a 0,16 e 0,29, sendo que E1 apresentou distribuição homogênea destes cristais, enquanto que D apresentou distribuição heterogênea, formando aglomerados. E2 apresentou cristais alongados de dissilicato de lítio, em fração volumétrica de 0,58, que apresentaram tendência de alinhamento com seu maior eixo alinhado perpendicularmente à direção de compactação, que variou angularmente a partir do ponto de injeção. O compósito IC apresentou-se constituído de cristais de alumina parcialmente sinterizados (65% em volume), infiltrados por vidro de baixa fusão. Independentemente do método, IC apresentou maior tenacidade (2,81 MPa.m1/2), seguido por E2 (1,81 MPa.m1/2) e E1 (0,96 MPa.m1/2) e, por último pelas porcelanas D (0,84 MPa.m1/2) e VM7 (0,67 MPa.m1/2)...

The objective of this study was to determine the mechanical properties and the microstructure of different dental ceramics in order to understand their influence on the slow crack growth (SCG) parameters, n (crack growth exponent) and ?f0, (scaling parameter), determined by different methods. The five ceramics tested were: porcelains VM7 (Vita) and D (d.Sign, Ivoclar), glass-ceramics E1 (IPS Empress, Ivoclar) e E2 (IPS Empress 2, Ivoclar) and composite IC (In-Ceram Alumina, Vita). Disc specimens (12 mm x 1 mm) were prepared according to manufacturers' instructions. The microstructure of the materials was carried out. The fracture toughness (KIc) was determined by means of the indentation fracture technique (IF) and indentation strength. The slow crack growth parameters were determined by dynamic fatigue test (constant stress rate), static fatigue test (constant stress) and the indentation fracture method. The results showed that all ceramic materials were composed by glassy matrix and crystalline phases, except for VM7 (vitreous porcelain). D and E1 presented leucite particles, in volume fractions of 0.16 and 0.29. For E1, the leucite crystals were homogeneously distributed in the glassy matrix, while in D, leucite formed agglomerates. E2 presented lithium dissilicate crystals (58% in volume) that presented an alignment tendency, with their major axis oriented perpendicularly to the pressing direction, which varied angularly from the injection point. IC presented alumina crystals (65% in volume) partially sintered, infiltrated by a lanthanum glass. Regardless of the method, the fracture toughness values were higher for IC (2.81 MPa.m1/2), followed by E2 (1.81 MPa.m1/2) and E1 (0.96 MPa.m1/2), and were lower for the porcelains D (0.84 MPa.m1/2) and VM7 (0.67 MPa.m1/2). Crack deflection was the main toughening mechanism observed for the ceramics containing crystalline phases. Regarding the dynamic fatigue test, the n values depended...