Restaurações endocrown em pré-molares: influência das paredes remanescentes da estrutura dentária e materiais restauradores na resistência à fadiga / Endocrown restorations in premolars: influence of remaining axial walls of tooth structure and restorative materials on fatigue resistance

Este estudo teve como objetivo avaliar o efeito da estrutura dentária remanescente e dois materiais diferentes de restauração CAD/CAM no desempenho à fadiga e no modo de falha de pré-molares tratados endodonticamente restaurados por endocrowns. Um total de 90 pré-molares superiores foram tratados endodonticamente e divididos aleatoriamente de acordo com o número de paredes axiais remanescentes, e os materiais restauradores foram divididos em 6 grupos (n = 15); quatro paredes restantes restauradas com zircônia ultratranslúcida 5Y-PSZ (grupo Fo-Z) e dissilicato de lítio (grupo Fo-L), três paredes restantes restauradas com 5Y-PSZ (grupo Th-Z) e dissilicato de lítio (grupo Th-L) e duas paredes restantes restauradas com 5YPSZ (grupo Tw-Z) e dissilicato de lítio (Tw-L). As restaurações foram cimentadas adesivamente e os espécimes foram submetidos a cargas de fadiga gradual em seu longo eixo (carga inicial: 200 N, frequência: 20 Hz). Uma carga incremental de 100 N por 10.000 ciclos foi aplicada com um pistão metálico de Ø 6 mm até a falha. A carga de falha por fadiga (FFL) e o número de ciclos de falha (CFF) no momento da falha foram registrados e analisados estatisticamente por ANOVA 2 fatores e teste de Kaplan-Meier (α = 0,05). Os espécimes fraturados foram examinados em estereomicroscópio em 8× e 25× e os modos de falha foram determinados como reparáveis ou catastróficos. FFL e CFF foram significativamente influenciados pelo material restaurador (p < 0,05). As restaurações de 5Y-PSZ apresentaram FFL (Fo-Z = 1487 N, Tw-Z = 1427 N, Tw-Z = 1533 N) e probabilidade de sobrevivência significativamente maiores quando comparadas com dissilicato de lítio (Fo-L = 1060 N, Th-L = 940 N, TwL = 1000 N). O número de paredes remanescentes não afetou o comportamento de fadiga ou modo de falha dos corpos de prova. Das restaurações de dissilicato de lítio, 51% tiveram falhas reparáveis, enquanto 95% das restaurações de zircônia ultratranslúcida 5Y-ZP tiveram falhas catastróficas. Endocrowns de zircônia apresentaram melhor desempenho em fadiga do que endocrowns de dissilicato de lítio, independentemente do número de paredes remanescentes do eixo. Endocrowns de pré-molares de dissilicato de lítio e 5Y-PSZ apresentaram maior FFL do que as cargas mastigatórias normais (AU)

This study aimed to evaluate the effect of the remaining tooth structure and two different CAD/CAM restoration materials on the fatigue performance and failure mode of endodontically treated premolars restored with endocrowns. A total of 90 maxillary premolars were endodontically treated and divided randomly according to the number of remaining axial walls, and the restorative materials were divided into 6 groups (n = 15); four remaining walls restored with ultratranslucent zirconia 5Y-PSZ (group Fo-Z) and lithium disilicate (group Fo-L), three remaining walls restored with 5Y-PSZ (group Th-Z) and lithium disilicate (Group Th-L), and two remaining walls restored with 5Y-PSZ (group Tw-Z) and lithium disilicate (Tw-L). The restorations were cemented adhesively and the specimens were subjected to stepwise fatigue loading along the long axis (initial load: 200 N, frequency: 20 Hz). An incremental step load of 100 N per 10,000 cycles was applied with a Ø6-mm metallic piston until failure. The fatigue failure load (FFL) and number of failure cycles (CFF) at the time of failure were recorded and statistically analyzed with two-way ANOVA and the Kaplan-Meier test (α = 0.05). Fractured specimens were examined under a stereomicroscope at 8× and 25× and failure modes determined as reparable or catastrophic. FFL and CFF were significantly influenced by restorative material (p < 0.05). 5Y-PSZ endocrowns showed significantly higher FFL (Fo-Z = 1487 N, Th-Z = 1427 N, Tw-Z = 1533 N) and survival probability when compared with lithium disilicate (Fo-L = 1060 N, Th-L = 940 N, Tw-L = 1000 N). The number of remaining walls did not affect the fatigue behavior or failure mode of the specimens. Of the lithium disilicate restorations, 51% had repairable failures, while 95% of ultratranslucent zirconia 5Y-ZP restorations had catastrophic failures. Zirconia endocrowns showed better fatigue performance than lithium disilicate endocrowns, regardless of the number of remaining axis walls. Lithium disilicate and 5Y-PSZ premolar endocrowns showed higher FFL than the normal masticatory loads (AU)

A 3-Year Retrospective Evaluation of the Clinical Performance of Fiber Posts

This retrospective study evaluated the clinical outcome of 139 teeth restored with carbon fiber posts after 3 years of placement, considering the amount of remaining dentin as the main variable. Eighty-one patients received the fiber posts within a period of 16 months and were recalled after 3 years. The tooth type, amount of remaining dentin, and prosthetic crown material were evaluated. No loss of post or core retention was detected after 3 years of follow up. During the observed time, root or post fracture and secondary caries were not recorded. Only one failure concerning endodontic treatment was detected. The amount of remaining dentin was not an important characteristic in the restorative failure of endodontically treated teeth restored with carbon fiber posts within 3 years.

Resumo Este estudo avaliou de forma retrospectiva o desfecho clínico de 139 dentes restaurados com pinos de fibra de carbono após 3 anos em função, considerando a quantidade de dentina coronária remanescente como principal variável. Oitenta e um indivíduos receberam a cimentação dos pinos entre Janeiro de 2004 e Janeiro de 2005, e foram chamados para reavaliação após 3 anos. O tipo de dente restaurado, quantidade de dentina remanescente e material restaurador coronário foram avaliados. Nenhum caso de perda de retenção do pino e/ou núcleo foi encontrado durante o período de avaliação. Fraturas na raiz ou no pino e cáries secundárias também não foram registrados. Uma única falha foi encontrada em relação ao tratamento endodôntico. A quantidade de dentina remanescente não foi um fator importante para falha na restauração de dentes tratados endodonticamente, restaurados com pinos de fibra de carbono, após 3 anos de serviço clínico.