Effect of Er: YAG laser and diamond drill on hybrid layer morphology obtained with self-etch adhesive - analysis by SEM and confocal laser scanning microscopy (CLSM)

ABSTRACT Introduction and Objective: This study aimed to evaluate the effect of Er:YAG (L) and diamond drills (DD) on: 1) the microshear bond strength (MPa); 2) the adhesive interface of two-step (TS) - Adper Scotchbond Multipurpose and one-step (OS) adhesives - Adper EasyOne, both from 3M ESPE. Material and methods: According to the preparation condition and adhesives, the samples were divided into four groups: DD_TS (control); DD_OS; L_TS and L_OS. 60 bovine incisors were randomly divided into experimental and groups: 40 for microshear bond strength (n = 10) and 20 for the adhesive interface morphology [6 to measure the thickness of the hybrid layer (HL) and length of tags (t) by CLSM (n = 3); 12 to the adhesive interface morphology by SEM (n = 3) and 2 to illustrate the effect of the instruments on dentine by SEM (n = 1)]. To conduct the microshear bond strength test, four cylinders (0.7 mm in diameter and 1 mm in height with area of adhesion of 0.38 mm) were constructed with resin composite (Filtek Z350 XT - 3M ESPE) on each dentin surface treated by either L or DD and after adhesives application. Microshear bond strength was performed in universal testing machine (EMIC 2000) with load cell of 500 kgf and a crosshead speed of 0.5 mm / min. Adhesive interface was characterized by thickness of hybrid layer (HL) and length of tags (t) in nm, with the aid of UTHSCSA ImageTool software. Results: Microshear bond strength values were: L_TS 34.10 ± 19.07, DD_TS 24.26 ± 9.35, L_OS 33.18 ± 12.46, DD_OS 21.24 ± 13.96. Two-way ANOVA resulted in statistically significant differences only for instruments (p = 0.047). Mann-Whitney identified the instruments which determined significant differences for HL thickness and tag length (t). Concerning to the adhesive types, these differences were only observed for (t). Conclusion: It can be concluded that 1) laser Er:YAG results in higher microshear bond strength values regardless of the adhesive system (TS and OS); 2) the tags did not significant affect the microshear bond strength; 3) the adhesive interface was affected by both the instruments for cavity preparation and the type of adhesive system used.

Efeito do laser ER:YAG e ponta diamantada na morfologia da camada híbrida obtida com um adesivo autocondicionante: resistência de união ao microcisalhamento análise por MEV e MLCF / Effect of laser ER: YAG and a diamond bur in the morphology of the hybrid layer obtained with a self-etching adhesive. SEM analysis and MLCF and bond strength microshear

Este estudo tem como objetivo avaliar o efeito de laser de Er: YAG (L) e ponta diamantada (B) sobre a força de resistência ao microcisalhamento (MPa) e o efeito sobre a interface adesiva de adesivos condiciona e lava (CL) ­ Adper Scotchbond Multiuso e autocondicionante (CS) ­ Adper EasyOne, ambos da 3M ESPE. Foram constituídos 4 grupos segundo instrumentos e adesivos: B_CL (controle); B_CS; L_CL e L_CS. 60 incisivos bovinos foram randomicamente divididos nos experimentos e grupos: 40 para força de resistência ao microcisalhamento (n=10) e 20 para morfologia da interface adesiva (6 para mensuração da espessura da camada hibrida (CH) e comprimento de tags (t) por MLCF (n=3); 12 para morfologia da interface adesiva por MEV (n=3) e 2 para ilustração o efeito dos instrumentos sobre dentina por MEV (n=1). Para o ensaio de microcisalhamento foram confeccionados 4 cilindros de resina composta Filtek Z350 XT ­ 3M ESPE (0,7 mm de diâmetro por 1 mm de altura e área de adesão de 0,38 mm2 ) sobre cada superfície de dentina tratada pelos instrumentos e adesivos. O ensaio de resistência de união ao microcisalhamento foi realizado em máquina de ensaio universal EMIC 2000, com célula de carga de 500 Kgf e velocidade de 0,5 mm/min. A interface adesiva foi caracterizada pela espessura da camada hibrida (CH) e comprimento de tags (t) em µm, com o software UTHSCSA Imagetool. Os valores de resistência adesiva ao microcisalhamento foram L_CL 34,10 ± 19,07 MPa, B_CL 24,26 ± 9,35 MPa, L_CN 33,18 ± 12,46 MPa, B_CN 21,24 ± 13,96 MPa. Anova two-way resultou em diferença estatisticamente significativa somente para instrumentos (p=0,047). Teste de Mann-Whitney identificou os instrumentos determinam diferenças significativas para de espessura de CH e comprimento de (t). Para adesivos estas diferenças só foram observadas para (t). Pode-se concluir que 1) Laser de Er:YAG resulta em maiores valores de resistência adesiva ao microcisalhamento, independente do sistema adesivo utilizado (CL ou CS). 2) Os tags não tem efeito significativo na resistência adesiva ao microcisalhamento. 3) A interface adesiva é afetada tanto pelos instrumentos utilizados para o preparo cavitário como pelo tipo de sistema adesivo empregado

This study aims to evaluate the effect of Er: YAG (L) and bur (B) on the strength of resistance microshear (MPa) and the effect on the interface adhesive stickers and wash conditions (CL) - Adper Scotchbond Multipurpose and self (CS) - Adper EasyOne, both from 3M ESPE. Were formed 4 groups according tools and adhesives: B_CL (control); B_CS; L_CL and L_CS. 60 bovine incisors were randomly divided into experimental and groups: 40 to force microshear resistance (n = 10) and 20 for the adhesive interface morphology (6 to measure the thickness of the hybrid layer (CH) and length of tags (t) by MLCF (n = 3); 12 to the adhesive interface morphology by SEM (n = 3) and 2 to illustrate the effect of the instruments on dentine by SEM (n = 1). Microshear For testing four cylinders were fabricated composite Filtek Z350 XT - 3M ESPE (0.7 mm in diameter and 1 mm in height and area of adhesion of 0.38 mm) on each dentin surface treated by tools and adhesives. Testing of bond strength was performed in microshear FDMS universal testing machine 2000 with a load cell of 500 kgf and a speed of 0.5 mm / min. Adhesive interface was characterized by layer thickness hybrid (HC) and length of tags (t) in nm, with software UTHSCSA ImageTool. Values of bond strength to microshear L_CL were 34.10 ± 19.07, 24.26 ± 9.35 B_CL, L_CN 33.18 ± 12.46, 21.24 ± 13.96 B_CN. Anova two- way resulted in statistically significant only for instruments (p = 0.047). Mann-Whitney identified instruments to determine significant differences CH thickness and length (t). adhesives for these differences were only observed for (t). It can be concluded that 1) Laser Er: YAG results in higher bond strength to the microshear, regardless of the adhesive system (CL and CS). 2) The tags have no significant effect on bond strength to microshear. 3) The adhesive interface is affected by both instruments for cavity preparation and the type of adhesive system used

In vitro potential cytotoxicity of an adhesive system to alveolar macrophages

The purpose of this study was to evaluate the potential cytotoxicity of Adper Single Bond 2 (SB) simplified etch-and-rinse adhesive system in alveolar macrophage cultures, as a function of the post-polymerization time and duration of immersion in the culture medium for preparation of extracts, by observing the levels of nitric oxide (NO) release and cell survival rate (MTT assay). Wistar rat alveolar macrophages were exposed to 200 μL of extracts obtained from 24- or 72-h immersion of adhesive samples in culture medium (RPMI), immediately or 24 h after polymerization. Fresh RPMI and E. coli lipopolysaccharides were used as negative and positive controls, respectively. The cells were placed in a humidified incubator for 24 h. The results were analyzed by the Student's-t test (α=5 percent). The amount of NO produced and viable cells were significantly different (p<0.05) between the experimental and the control groups, showing that, irrespective of the post-polymerization time and duration of immersion in the culture medium, the adhesive system caused intense cytotoxicity to the macrophages. The cytotoxic effects were not statistically different (p<0.05) among the experimental groups. In conclusion, chemical components released from SB in aqueous environment were highly toxic to cell culture and thus an inflammatory pulpal response should be considered during the clinical application of dental adhesives.

O objetivo deste estudo foi avaliar o potencial de citotoxicidade do sistema adesivo Adper Single Bond 2 (SB), em função dos tempos pós-polimerização e imersão no meio de cultura para preparação dos extratos, observando-se os níveis de liberação de óxido nítrico (NO) e taxa de sobrevivência celular (MTT assay). Macrófagos alveolares de ratos Wistar foram expostos a 200 μL de extratos obtidos a partir da imersão de amostras do adesivo em meio de cultura (RPMI), imediatamente ou 24 h após sua polimerização, onde permaneceram durante 24 ou 72 h. RPMI puro e lipopolissacarídeos de E. coli foram utilizados como controles negativo e positivo, respectivamente. As células foram levadas à incubadora umidificada por 24 h. Os resultados foram submetidos ao teste "t" de Student (α=5 por cento). As quantidades de NO produzido e células sobreviventes foram significativamente diferentes entre os grupos experimentais e grupos controle, mostrando que, independente do tempo pós-polimerização e tempo de elaboração dos extratos, o sistema adesivo causou uma intensa citotoxicidade sobre os macrófagos. Os efeitos citotóxicos não foram estatisticamente diferentes entre os grupos experimentais. Componentes químicos do SB liberados em meio aquoso podem ser altamente citotóxicos para as células em cultura e, portanto, uma resposta inflamatória pulpar deve ser considerada durante a aplicação clínica de adesivos dentinários.

Influência da espessura dentinária remanescente sobre a resistência ao cisalhamento do amálgama aderido. Estudo morfométrico em dentes decíduos / The influence of the remaining dentinal thickness on the shear bonding strength of the bonded amalgam. Morphometric study in primary teeth

O presente estudo teve por finalidade comparar a espessura da dentina remanescente restaurada com amálgama aderido à estrutura dentária utilizando Scotchbond Multi-Uso Plus (Grupo I) e All Bond 2 (Grupo II), com os valores obtidos em ensaios de cisalhamento. Após os testes mecânicos, os exemplares dos Grupos I e II, e 10 outros dentes (Grupo III) foram seccionados longitudinalmente no sentido mésio-distal e levados a uma lupa estereomicroscópica. Com auxílio de uma ocular cariométrica foram realizadas duas medidas referentes à menor e à maior espessura entre a superfície e a câmara pulpar, e obtida a média dos valores obtidos para cada grupo. Essas médias foram comparadas com os valores de cisalhamento anteriormente obtidas, e os corpos de prova foram devidamente preparados e levados para análise ao MEV. Após análise estatística, verificou-se que (1) não houve diferenças significantes entre os Grupos I e II, entretanto estes grupos apresentaram diferenças estatisticamente significantes com o Grupo III, obtendo este último média inferior. (2) Não foi observada correlação estatisticamente significativa entre a espessura de dentina remanescente e os valores encontrados no ensaio de cisalhamento tanto para o Grupo I quanto para o Grupo II. (3) Ao MEV foi observada presença de grande quantidade de material adesivo sobre a dentina (tanto no Grupo I quanto Grupo II), muitas vezes preenchendo a luz dos túbulos dentinários. Para ilustrar, no Grupo III, as superfícies dentinárias foram tratadas com ácido fosfórico a 35%, apresentaram uma granulaçao abundante que permaneceu após aplicação do primer. Com o mesmo ácido a 32%, este aspecto não foi observado. Destacamos o grande número de túbulos dentinários com diâmetros regulares e amplos, e dentina intertubular com aspecto liso e homogêneo

The aim of this study was to compare the thickness of remaining dentine restored with amalgam bonded using Scotchbond Multi-Uso Plus (Group I) and All Bond 2 (Group II) adhesives and shear bonding values. After the shear bonding tests, the samples from Groups I and II and a third Group with 10 teeth without adhesive application were cut longitudinally in a mesial-distal direction, and then they were taken to a stereomicroscopic. Two measurements related to the smallest and the biggest thickness between the surface and the pulpal chamber were performed using a cariometric ocular, and then the average for the values of each group was achieved. These measurements were compared to the shear bonding values previously obtained, and the samples were submitted to SEM analysis. After statistic analysis, it was verified that (1) there were no significant differences between Group I and II, however these groups have shown statistically significant differences with Group III, because this one obtained a lower average (2) It was not observed statistically significant correlation between the thickness of remaining dentin and the values achieved during the shear bonding tests either in Group I or Group II. (3) The presence of a great amount of adhesive material was observed upon the dentin when using SEM (in Group I and II), and in many cases it filled the light of the dentinal tubules. To illustrate, in Group III, the dentinal surfaces was treated with a 35% phosphoric acid, presented an abundant granulation that remained after primer application. Using the same acid at 32% , this aspect was not observed. It was observed a great number of dentinal tubules with regular and extensive diameter and the intertubular dentine had a smooth and homogenous aspect