Effects of different toothpaste formulations on erosive tooth wear prevention: systematic review / Efeitos de diferentes dentifrícios na prevenção do desgaste dentário erosivo: revisão sistemática de literatura

Objective: erosive tooth wear is a multifactorial condition that results in loss of dental hard tissue, caused by a chemical and mechanical process. This paper aims to carry out a systematic review presenting the effects of different toothpaste formulations on the loss of dental enamel surface in vitro. Material and Methods: the searches were performed in the databases PubMed, Web of Science, LILACS and Scielo. Articles published from 2010 to 2020 were filtered, without language restriction. Articles that included abrasion and erosion protocols were searched, as they were more similar to clinical reality, since toothpaste is applied through tooth brushing. The searches with descriptors and free terms on the topic resulted in 992 articles, however only 12 were within the search criteria. Results: the selected studies appointed that association of conventional fluorides (NaF) with metallic fluorides can be a promising strategy for the reduction of surface loss by erosive tooth wear. Toothpastes containing sodium fluoride, as well as tin without chitosan, showed a reduction in surface loss, considered sufficient for individuals with medium exposure to acids. In children's toothpastes, the one containing sodium fluoride showed a reduction in surface loss when compared to non-fluoride dentifrices. Conclusion: different protocols may result in less or greater loss of enamel surface, and methodological differences should be considered. To clarify the effects of dentifrices on erosive tooth wear, other properties of dentifrices should be investigated. (AU)

Objetivo: o desgaste erosivo é uma condição multifatorial que resulta em perda de tecido duro dentário, causado por um processo químico e mecânico. Este trabalho tem como objetivo realizar uma revisão sistemática de literatura apresentando os efeitos de diferentes formulações de dentifrícios na perda de superfície de esmalte dentário in vitro. Material e Métodos: a busca foi realizada nas bases de dados PubMed, Web of Science, LILACS e Scielo. Foram filtrados artigos publicados no intervalo de 2010 a 2020, sem restrição de idioma. Buscou-se artigos que incluíssem protocolos de abrasão e erosão, por mais se assemelhar a realidade clínica, uma vez que o dentifrício é aplicado através da escovação dentária. A busca com descritores e termos livres sobre o tema encontrou 992 artigos, entretanto somente 12 estavam dentro dos critérios da pesquisa. Resultados: os estudos selecionados apontaram que associação dos fluoretos convencionais (NaF) com os metálicos pode ser uma estratégia promissora para a redução de perda de superfície pelo desgaste dentário erosivo. Dentifrícios contendo fluoreto de sódio, assim como estanho sem quitosana, apresentaram redução na perda de superfície, sendo considerada suficiente para indivíduos com exposição média aos ácidos. Em dentifrícios infantis, aquele que continha fluoreto de sódio apresentou uma redução de perda de superfície quando comparado com dentifrícios sem fluoreto. Conclusão:diferentes protocolos podem resultar em menor ou maior perda de superfície de esmalte e as diferenças (AU)

Development of a sodium fluoride and stannous chloride-containing gel for treatment of dental erosion

Resumo Este estudo desenvolveu e testou géis experimentais contendo íons fluoreto (F-) e estanho (Sn2+) para o controle da erosão dentária. Os espécimes polidos, de esmalte e dentina, foram previamente erodidos (solução de ácido cítrico a 1%, 10 min) e alocados aleatoriamente em 5 grupos (n = 10): Placebo - gel de hidroxipropilmetilcelulose (HMC); F + Sn + HMC - 7.500 ppm F- / 15.000 ppm Sn2+; F + HMC - 7.500 ppm F-; Gel de flúor fosfato acidulado comercial (12.300 ppm F-); e Controle - sem tratamento. Após o tratamento (aplicado por 60 s), os espécimes foram submetidos a uma ciclagem de erosão-remineralização (5 min em solução de ácido cítrico a 0,3%, 60 min em saliva artificial, 4 × / dia, 20 dias). A perda de superfície (SL, em µm) foi determinada após o 5º, 10º e 20º dias de ciclagem (α = 0,05). Para o esmalte, após 5 e 10 dias, o F + Sn + HMC apresentou a menor PS, não diferindo do gel comercial. Após 20 dias, não foram encontradas diferenças entre os grupos comercial, F + HMC e F + Sn + HMC. O placebo não diferiu do controle em nenhum momento, e ambos os grupos apresentaram a maior PS, comparado aos demais grupos. Para dentina, no 5º dia , F + Sn + HMC, F + HMC e comercial não diferiram significativamente, apresentando menor PS que o grupo controle e placebo. No 10º dia, F+Sn+HMC e comercial apresentaram a menor PS comparado ao grupo controle e placebo. No 20º dia, apenas o gel comercial apresentou PS menor que o controle e o placebo. Assim, o gel experimental F + Sn + HMC foi capaz de controlar a progressão da erosão dentária.

Abstract: This study synthesized and tested experimental gels containing fluoride (F-) and stannous (Sn2+) ions for the control of dental erosion. Enamel and dentin polished specimens were eroded (1% citric acid solution, 10 min) and randomly allocated into 5 groups (n=10): Placebo - Hydroxypropyl Methylcellulose (HMC) gel; F+Sn+HMC - 7,500 ppm F- / 15,000 ppm Sn2+; F+HMC - 7,500 ppm F-; Commercial acidulated phosphate fluoride gel (12,300 ppm F-); and Control - no treatment. After treatment (applied for 60 s), specimens underwent an erosion-remineralization cycling (5 min in 0.3% citric acid solution, 60 min in artificial saliva, 4×/day, 20 days). Surface loss (SL, in µm) was determined after the 5th, 10th and 20th days of cycling (α=0.05). For enamel, after 5 and 10 days, F+Sn+HMC presented the lowest SL, which did not differ from the commercial gel. After 20 days, no differences were found between commercial, F+HMC, and F+Sn+HMC groups. Placebo did not differ from the control at any time points, and both groups presented the highest SL when compared to the other groups. For dentin, on the 5th day, F+Sn+HMC, F+HMC and commercial did not differ significantly, showing lower SL than the control and the placebo. On the 10th day, F+Sn+HMC and commercial presented the lowest SL compared to control and placebo. After 20 days, only the commercial gel showed lower SL than the control and placebo. Thus, the experimental F+Sn+HMC gel was able to control the progression of tooth erosion.

Collagen cross-linking agents + dimethyl sulfoxide improving the adhesive properties of erosive lesion dentin

Abstract To investigate the effect of the dimethyl sulfoxide combined with cross-linking agents on microtensile bond strength, silver nitrate penetration and in situ degree of conversion analysis of adhesives to the erosive dentin treatment with Cola-based soft drink. One hundred and sixty-six molars were assigned to 20 groups: (1) Treatment: Sound dentin; Erosive dentin; Erosive dentin treated with primer of dimethyl sulfoxide; Erosive dentin treated with DMSO primer containing proanthocyanidin and rivoflavin; (2) Adhesive systems: iBond Universal and Scotchbond Universal; and (3) adhesive strategy: etch-and-rinse or self-etch strategy. After restoration, specimens were sectioned into sticks to be tested. The data from microtensile bond strength (MPa), silver nitrate penetration (%) and in situ degree of conversion (%) were analyzed by (three- and two-factor ANOVA; Tukey's test α=5%). The application of dimethyl sulfoxide combined of not with cross-linkers improved all properties evaluated when compared to only erosive dentin treatment with Cola-based soft drink. However, only when dimethyl sulfoxide was combined to cross-linkers, the values of the microtensile bond strength, silver nitrate penetration and in situ degree of conversion in erosive dentin treatment with Cola-based soft drink was similar to sound dentin, for both adhesives and adhesive strategies. The application of dimethyl sulfoxide combined with the collagen cross-linking agent contributed to increasing the bond strength and degree of conversion in erosive lesion dentin, at the same time that significantly reduction of nanoleakage in this substrate.

Resumo Este estudo investigou o efeito do dimetil sulfóxido combinado a agentes de reticulação de colágeno na resistência de união à microtração, infiltração de nitrato de prata e análise do grau de conversão por Micro-Raman de sistemas adesivos universais para a dentina erosionada por refrigerante a base de Cola. Cento e sessenta molares foram divididos em 20 grupos: (1) Tratamento: Dentina sadia; Dentina erosionada; Dentina erosionada tratada com primer de dimetil sulfóxido; Dentina erosionada tratada com primer contendo 6,5% de proantocianidina e; Dentina erosionada tratada com primer contendo 0,1% de rivoflavina; (2) Sistemas adesivos: iBond Universal e Scotchbond Universal; e (3) estratégia adesiva: estratégia condicionamento e lavagem ou autocondicionate. Após a restauração, os espécimes foram seccionados em palitos e testados. Os dados dos três testes foram analisados estatisticamente (ANOVA de 2 e 3 fatores e teste de Tukey; α = 5%). A aplicação de dimetil sulfóxido combinado ou não agentes de reticulação de colágeno melhorou todas as propriedades avaliadas quando comparado a dentina erosionada. Entretanto, apenas quando o dimetil sulfóxido foi combinado com agentes de reticulação de colágeno, os valores de adesão a dentina, infiltração de nitrato de prata e grau de conversão em dentina erosionada foi semelhante a dentina sadia, para os dois adesivos e estratégias adesivas. A aplicação de dimetil sulfóxido combinado com agentes de reticulação de colágeno contribuiu para aumentar a resistência de união e o grau de conversão dentro da camada híbrida na dentina erodida, ao mesmo tempo que reduziu significativamente a nanoinfiltração neste substrato.

A Survey on Knowledge and Practices in Erosive Tooth Wear Among Dental Practitioners in Kuantan, Pahang: A Preliminary Study

@#Introduction: Erosive tooth wear (ETW) is an emerging dental condition worldwide. However, most dental practitioners overlooked the early stages of the condition due to vague clinical appearance of tooth surface loss. Therefore, this study was aimed to determine the knowledge of ETW and treatment given amongst dental professionals in private clinics in Kuantan, Pahang. Method: Several private dental clinics in Kuantan, Pahang, involved in this cross-sectional study. Dental practitioners were volunteering to participate in this research. A validated self-administered questionnaire was distributed, and a descriptive analysis was conducted. Results: The overall response rate was 75%. Results revealed that most participants obtained a structured education on ETW (79.2%). Through continuous dental education, about half of the participants learnt further. All participants agreed that carbonated drink caused ETW, and most reported that gastroesophageal reflux diseases and pickles had related to the ETW. The majority of participants favoured case note (79%) with regards to ETW records. Nevertheless, 40.9% and 36.4% are recorded at the tooth surface and individual level, respectively. Surprisingly, 79% of them did not know about special scores when assessing ETW. Most participants prefer to give instruction on oral hygiene and diet counselling as preventive measures, but the use of fluoride was not given priority. 77% have not ever referred the case to a dental specialist and preferred to treat the patient on their own. Conclusion: ETW knowledge among recruited PDPs is adequate; however, no specific indices were used for ETW scoring and insufficient treatment strategies..

Effect of erosive challenges on deciduous teeth undergoing restorative procedures with different adhesive protocols - an in vitro study

ABSTRACT Objective: To evaluate the effect of erosive challenges on the tooth- restoration interface of deciduous teeth treated with different adhesive protocols. Material and Methods: Deciduous molars were cut mesiodistally, then embedded, abraded and polished (n=80). Samples were randomly divided according to the adhesive system used into: G1 (Adper Single Bond2®, etch-and-rinse), G2 (Universal Single Bond®, self-etching), G3 (OptibondFL®, etch-and-rinse with Fluoride) and G4 (BondForce®, self-etching with Fluoride). After standardized cavity preparation (2 mm diameter x 2 mm depth), adhesive systems were applied and samples were restored (composite resin Z350®). Half of the samples were exposed to erosive/abrasive cycles (n = 10, each adhesive group), and the other half (control group; n = 10) remained immersed in artificial saliva. For microleakage analysis, samples were submersed in methylene blue and analyzed at 40x magnifications. Cross-sectional microhardness (CSMH) was carried out (50 g/5 s) at 25 μm, 50 μm, and 100 μm from the eroded surface and at 25 μm, 75 μm, and 125 μm from the enamel bond interface. Results: Regarding microleakage, 7.5% of the samples showed no dye infiltration, 30% showed dye infiltration only at the enamel interface, and 62.5% showed dye infiltration through the dentin-enamel junction, with no difference between groups (p≥0.05). No significant difference was observed in CSMH at different depths (two-way ANOVA, p≥0.05). Conclusions: We did not observe significant changes in microleakage or CSMH after erosive/abrasive challenges in deciduous teeth treated with different adhesive protocols (etch-and-rinse and self-etching adhesives, with and without fluoride).