Avaliação das propriedades de painéis aglomerados produzidos com resíduos de serrarias de nove espécies de madeiras tropicais da Amazônia / Evaluation of the properties of particleboard made from sawmill waste of nine tropical wood species of Amazon

Esta pesquisa teve como objetivo avaliar a qualidade de painéis aglomerados produzidos com resíduos de processamento em serraria de nove espécies de madeiras tropicais da Amazônia. As espécies estudadas foram: Scleronema micranthum Ducke (Cardeiro), Ecclinusa guianensis Eyma (Caucho), Scleronema sp. (Castanha-de-paca), Copaifera multijuga Hayne (Copaíba), Ocotea sp. (Louro), Ocotea guianensis Aubl (Louro-espinho), Caryocar villosum Pers. (Piquiarana), Couratari oblongifolia Ducke & R. Knuth (Tauari) e Virola surinamensis Rol. Warb (Virola). Foram produzidos painéis experimentais com densidade nominal de 0,75 g.cm-3, utilizando a resina uréia-formaldeído na proporção de 8 por cento de sólidos - base peso seco das partículas. Os painéis foram prensados com pressão específica de 4,0 MPa, temperatura de 160 ºC e tempo de prensagem de oito minutos. As avaliações dos resultados de ensaios obtidos nesta pesquisa indicam a viabilidade técnica de utilização das nove espécies provenientes de florestas tropicais da Amazônia na produção de painéis de madeira aglomerada, com destaque para Ecclinusa guianensis Eyma (Caucho) que, de uma forma geral, apresentou melhores resultados de propriedades físico-mecânicas.

This research was developed to evaluate the quality of particleboards manufactured from sawmill waste of nine tropical wood species of Amazônia. The following species were studied: Scleronema micranthum Ducke (Cardeiro), Ecclinusa guianensis Eyma (Caucho), Scleronema sp. (Castanha-de-paca), Copaifera multijuga Hayne (Copaíba), Ocotea sp. (Louro), Ocotea guianensis Aubl (Louro-espinho), Caryocar villosum Pers. (Piquiarana), Couratari oblongifolia (Tauari) e Virola surinamensis Rol. Warb (Virola). The experimental boards were manufactured with the nominal density of 0.75 g.cm-3, using the urea-formaldehyde resin in the proportion of 8 percent of solid content based on oven dried wood particles. The boards were pressed at the specific pressure of 40 kgf/cm², temperature of 160 ºC and press time of eight minutes. The evaluations of test results obtained in this study indicate the potential use of the nine species from Amazon rainforest in the production of particleboard, highlighting Ecclinusa guianensis (Caucho) that, in general, showed better results of physical and mechanical properties.

Efeito da incorporação de casca de café nas propriedades físico-mecânicas de painéis aglomerados de Eucalyptus urophylla S. T. Blake / Effect of the incorporation of coffee husks on the physico-mechanical properties of Eucalyptus urophylla S. T. Blake particleboards

Neste trabalho objetivou-se avaliar a influência da incorporação de casca de café nas propriedades físico-mecânicas de painéis aglomerados produzidos com Eucalyptus urophylla S.T. Blake. Os painéis foram produzidos com incorporação de 25, 50 e 75 por cento de casca de café, em três teores da resina fenol-formaldeído (6, 9 e 12 por cento) e 1 por cento de parafina. A densidade nominal dos painéis foi de 0,7 g/cm³ e o ciclo de prensagem compreendeu uma pressão de 3,92 MPa e temperatura de 180ºC por 8 minutos. Pelos resultados obtidos foi possível observar que: as propriedades físicas dos painéis aglomerados apresentam relação linear decrescente com o aumento do teor de resina, e crescente com a porcentagem de casca de café, apresentando maiores valores de absorção de água e inchamento em espessura. As propriedades mecânicas apresentam relação linear crescente com o aumento do teor de resina, e decrescente com a porcentagem de associação de casca de café. Do modo que a pesquisa foi conduzida, a incorporação da casca de café prejudica a qualidade dos painéis produzidos.

The objective of this study was to evaluate the influence of the incorporation of Coffee husks in the production of particleboard with Eucalyptus urophylla S.T. Blake. The panels were produced incorporating 25 percent, 50 percent, and 75 percent of Coffee husks at three levels of resin phenol-formaldehyde (6, 9 and 12 percent) and 1 percent of paraffin. The nominal density of the panels was 0.7 g/cm³ and the cycle of pressing consisted in a pressure of 3.92 MPa under a temperature of 180°C for 8 minutes. By the results it was possible to observe that the physical properties of the particleboard have a linear relationship decreasing with the increase in the level of resin, and increasing with the increase in the percentage of coffee husks, showing higher values of water absorption and thickness swelling. The mechanical properties show a linear relationship growing with the increase of resin level, and decreasing with a reduction the percentage of coffee husk association. The way that the search was conducted, the incorporation of the Coffee husks harms the quality of the panels produced.

Avaliação do potencial de utilização da madeira de Schizolobium amazonicum "Paricá" e Cecropia hololeuca "Embaúba" para produção de painéis aglomerados / Evaluation of potential use of the wood of Schizolobium amazonicum "Paricá" and Cecropia hololeuca "Embaúba" to particleboard manufacture

Esta pesquisa teve por objetivo avaliar o potencial de utilização de madeira de Schizolobium amazonicum (Paricá) e Cecropia hololeuca (Embaúba) para produção de painéis aglomerados. Foram produzidos painéis experimentais com densidade nominal de 0,70 g/cm³, utilizando a resina uréia-formaldeído e partículas de madeira de Paricá e Embaúba, e mistura destas, em proporções de 75, 50 e 25%. A madeira de Pinus taeda foi utilizada como testemunha. Os painéis foram prensados com pressão específica de 40 kgf/cm², temperatura de 160ºC e tempo de prensagem de 8 minutos. Os resultados das avaliações de propriedades de absorção de água, inchamento em espessura, ligação interna, módulo de elasticidade e módulo de ruptura, indicaram que as madeiras de Schizolobium amazonicum (Paricá) e Cecropia hololeuca (Embaúba) são tecnicamente viáveis para produção de painéis aglomerados.

This research was developed to evaluate the potential use of the woods Schizolobium amazonicum (Paricá) and Cecropia hololeuca (Embaúba) for manufacturing particleboard. Were made panels with the densities of 0.70 g/cm³, using mixtures of urea-formaldehyde resin and wood particles of Paricá and Embaúba, in proportions of 75, 50 and 25%. The Pinus taeda wood was used as the reference. The panels were pressed at the temperature of 160ºC, pressure of 40 kgf/cm², for 8 minutes. The evaluations of the properties of water absorption, thickness swelling, internal bond, modulus of elasticity and modulus of ruptures, showed that the woods of Schizolobium amazonicum (Paricá) e Cecropia hololeuca (Embaúba) are technically feasible for particleboard manufacture.

Chemical composition of tomato (Solanum lycopersicum) stalk and suitability in the particleboard production.

This study examined chemical composition of tomato stalks and their possible feasibility in the production of particleboard. Three-layer experimental particleboards with density of 0.53, 0.63, and 0.73 g cm-3 were manufactured from tomato stalks using certain ratios of urea formaldehyde (UF) and melamine urea formaldehyde (MUF) adhesives. Modulus of elasticity (MOE), modulus of rupture (MOR), internal bond strength (IB), thickness swelling (TS) properties of the boards were evaluated, and a statistical analysis was performed in order to examine possible feasibility of these stalks in commercial particleboard manufacturing. The experimental results have shown that production of general purpose particleboard used in dry conditions using tomato stalks is technically viable. The results of the study demonstrate that tomato stalks can be an alternative raw material source for particleboard industry. Use of agricultural waste such as tomato stalk can help solving waste management problems and contribute conservation of natural resources.