RESUMO
Objective: to evaluate the effect of material type and veneer thickness on the final color and shear bond strength of PEEK bilayered restorations. Material and Methods: sixty-four square-shaped core specimens (7×7×2), were fabricated by CAD/CAM technology from two high-strength polymers, BioHPP (High-Performance Polymer, group B n=32), and Pekkton® ivory (PolyEtherKetoneKetone, group P n=32) then were veneered with resin composite (crea.lign dentin A3). Specimens from each group were divided (n=16) according to the veneer layer thickness (0.5 & 1 mm), then according to the test applied (n=8), either ΔE or shear bond strength (SBS). Specimen surfaces were treated according to the manufacturer's instructions. Specimens were veneered according to the manufacturer's instructions.The mode of failure was evaluated under a stereomicroscope at 40 x magnification after the shear bond strength test. Results: data showed parametric distribution and variance homogeneity and were analyzed using two-way ANOVA. The significance level was set at p<0.05 for all tests. Statistical analysis was performed with the R statistical analysis software version 4.3.1.Results of two-way ANOVA showed that material types and veneer thicknesses had an individual significant effect on the color change. For the shear bond strength, only the sample thickness (1mm) had a significant effect (p=0.033). The majority of samples in different groups presented a mixed failure mode with all the differences being not statistically significant (p>0.05). Conclusion: the thickness of the resin composite veneer can significantly affect the final esthetic outcome and shear bond strength of a bilayered restoration.(AU)
Objetivo: avaliar o efeito do tipo de material e da espessura do revestimento na cor final e na resistência ao cisalhamento de restaurações em duas camadas de PEEK. Material e Métodos: foram fabricados 64 espécimes com núcleo de formato quadrado (7x7x2) usando tecnologia CAD/CAM a partir de dois polímeros de alta resistência, BioHPP (Polímero de Alto Desempenho, grupo B n=32) e Pekkton ivory (Polieterecetona cetona, grupo P n=32), que foram então revestidos com resina composta (crea.lign dentin A3). Os espécimes de cada grupo foram divididos (n=16) de acordo com a espessura do revestimento (0,5 e 1 mm), e depois de acordo com o teste aplicado (n=8), seja ΔE ou resistência ao cisalhamento (SBS). As superfícies dos espécimes foram tratadas de acordo com as instruções do fabricante. Os espécimes foram revestidos de acordo com as instruções do fabricante. O modo de falha foi avaliado sob um estereomicroscópio com ampliação de 40x após o teste de resistência ao cisalhamento. Resultados: os dados apresentaram distribuição paramétrica e homogeneidade de variância e foram analisados por ANOVA de duas vias. O nível de significância foi estabelecido em p<0,05 para todos os testes. A análise estatística foi realizada com o software de análise estatística R, versão 4.3.1. Os resultados da ANOVA de duas vias mostraram que os tipos de materiais e as espessuras do revestimento tiveram um efeito significativo individual na mudança de cor. Para a resistência ao cisalhamento, apenas a espessura da amostra (1mm) teve um efeito significativo (p=0,033). A maioria das amostras em diferentes grupos apresentou um modo de falha misto, com todas as diferenças não sendo estatisticamente significativas (p>0,05). Conclusão:a espessura do revestimento de resina composta pode afetar significativamente o resultado estético final e a resistência ao cisalhamento de uma restauração em duas camadas.(AU)
Assuntos
Polímeros , Resinas Compostas , Resistência ao CisalhamentoRESUMO
Objective: This study aims to compare the strain induced in the supporting structures of unilateral mandibular removable partial denture frameworks retained by extra-coronal attachments fabricated with three different materials. Material and Methods: Three mandibular class II digitally designed and printed acrylic models with detachable abutments were used to fabricate three removable partial denture framework with extra coronal attachments from three different materials. A total of 33 models were prepared for strain testing (n=11). Models were divided into three groups according to framework's material: porcelain fused to cobalt chromium (PFM), polyetherketoneketone (PEKK) and polyetheretherketone (PEEK) group. Unilateral load of 60 N was applied in the three groups and strains were measured around the main abutment and saddle area using strain gauge. Results: Statistical analysis was performed using Shapiro-Wilk's test and by checking data distribution. Data were found to be non-parametric and were analysed using Kruskal-Wallis test followed by Dunn's post hoc test with Bonferroni correction. PFM group showed significantly the highest strain values around abutment, slot 1 (1mm distal to the socket of the last abutment) and slot 2 (1 cm away from slot 1) respectively (843.00±23.08, 91.00±6.52 and 1274.00±65.71) than the other tested groups (p<0.05) at same tested sites respectively followed by PEKK group (384.00±37.48, 81.00±2.24 and 135.00±0.00) and PEEK group (29.00±4.18, 63.00±4.47 and 52.00±5.70). Conclusions: PEEK and PEKK for partial denture framework with extra coronal attachments are adequate alternative to PFM due to their good mechanical response applying less strain on supportive structures in free-end cases. PEEK induces lower strain magnitude on the supporting structures when compared to PEKK. (AU)
Objetivo: Este estudo tem como objetivo comparar a tensão induzida nas estruturas de suporte de estruturas de próteses parciais removíveis mandibulares unilateraisretidas por encaixes extracoronários fabricados com três materiais diferentes. Material e Métodos: Três modelos mandibulares de classe II digitalmente projetados e impressos em acrílico com pilares destacáveis foram usados para fabricar três estruturas de próteses parciais removíveis com encaixes extracoronários de três materiais diferentes. Um total de 33 modelos foram preparados para testes de deformação (n=11). Os modelos foram divididos em três grupos de acordo com o material da estrutura: porcelana fundida com cobalto-cromo (PFM), poliétercetonacetona (PEKK) e polieteretercetona (PEEK). Carga unilateral de 60 N foi aplicada nos três grupos e as deformações foram medidas em torno do pilar principal e área de sela usando medido de tensão. Resultados: A análise estatística foi realizada por meio do teste de Shapiro-Wilk e com a verificação da distribuição dos dados. Os dados mostraram-se não paramétricos e foram analisados pelo teste de Kruskal-Wallis seguido pelo de Dunn com correção de Bonferroni. O grupo PFM mostrou significativamente os maiores valores de tensão ao redor do pilar, slot 1 (1mm distal do último pilar) e slot 2 (1 cm de distância do slot 1) respectivamente (843,00±23,08, 91,00±6,52 e 1274,00±65,71) do que os outros grupos testados (p<0,05) nos mesmos locais testados, respectivamente, seguido pelo grupo PEKK (384,00±37,48, 81,00±2,24 e 135,00±0,00) e grupo PEEK (29,00±4,18, 63,00±4,47 e 52,00±5,70). Conclusão: PEEK e PEKK para estrutura de prótese parcial com encaixes extracoronários são alternativas adequadas ao PFM devido à sua boa resposta mecânica aplicando menos tensão nas estruturas de suporte em casos de extremidade livre. O PEEK induz menor magnitude de deformação nas estruturas de suporte quando comparado ao PEKK (AU)
Assuntos
Prótese Parcial , Prótese Parcial Removível , Encaixe de Precisão de DentaduraRESUMO
Objective: was to evaluate the retentive force, fatigue resistance and deformity of clasps made from two materials cobalt chromium and poly ether ether ketone (PEEK). Material and Methods: sixteen models were fabricated,each one having lower 1st molar. Models were divided into two groups according to materials,group I (GI) for cobalt chromium (Co-Cr) and group II (GII) for PEEK. Each testing models and its clasps were mounted inside universal testing machine, the retention was measured by applying withdrawal force to it by this machine at 5 mm/min. The Fatigue resistance is measured by the reduction in retention through repeated insertion and removal cycles using robota chewing simulator. Removal and insertion cycling of clasps was carried out for 360, 730, 1080, 1,440, 2,116 and 2,880 cycles (corresponding to 3, 6, 9, 12, 18 and 24 months of simulated clinical use of a RPD) to simulate the fatigue resistance test. Deformity was measured before and after each cycling using a digital micrometer. Statistical analysis was done by 2-way-ANOVA test to detect significance effects of each variable. Results: Retention and fatigue resistance, after 360, 730, 1080, 1,440, 2,116 and 2,880 cycles totally the difference between Co-Cr and PEEK groups was statistically non-significant (P = 0.0980> 0.05) where (Co-Cr > PEEK). Deformation results, regardless to evaluation time, Co-Cr group recorded statistically significant higher deformation mean value than PEEK group (P = 0.008 < 0.05).Regardless to material group, deformation mean value changed nonsignificantly by time (P = 0.2882> 0.05). Conclusion: PEEK clasps (1.0 mm in cross section diameter) engage 0.50 mm undercut provide sufficient retention nearly similar that of Co-Cr clasps.(AU)
Objetivo: o objetivo foi avaliar a força de retenção, a resistência à fadiga e a deformidade dos grampos fabricados com dois materiais diferentes: cromo-cobalto (Co-Cr) e poliéter-éter-étercetona (PEEK). Materiais e métodos: dezesseis modelos foram confeccionados, cada um com 1º molar inferior. Os modelos foram divididos em dois grupos de acordo com o material: grupo I Co-Cr e grupo II para PEEK. Cada modelo de teste universal e seus grampos foram montados em uma máquina de teste universal. A retenção foi medida aplicando força de retirada por esta máquina a 5 mm/min. A resistência à fadiga foi medida pela redução na retenção através de ciclos repetidos de inserção e remoção usando um simulador do ciclo de mastigação. O ciclo de remoção e inserção dos grampos foi realizado por 360, 730, 1080, 1.440, 2.116 e 2.880 ciclos (correspondendo a 3, 6, 9, 12, 18 e 24 meses de uso clínico simulado de um RPD) para simular o teste de resistência à fadiga. A deformidade foi medida antes e após cada ciclo, usando um micrômetro digital. A análise estatística foi realizada pelo teste ANOVA de 2 fatores para detectar os efeitos de significância de cada variável. Resultados: A retenção e a resistência à fadiga após 360, 730, 1080, 1.440, 2.116 e 2.880 ciclos entre os grupos Co-Cr e PEEK não mostrou diferença estatisticamente significativa (p = 0,0980> 0,05), onde (Co-Cr> PEEK). Para os resultados da deformação, independentemente do tempo de avaliação, o grupo Co-Cr registrou um valor médio de deformação maior, com diferença estatística significativa, quando comparado com o grupo PEEK (p= 0,008 < 0,05). Independentemente do grupo de material, o valor médio da deformação foi alterado de forma não significativa pelo tempo (p= 0,2882> 0,05). Conclusão: os grampos PEEK (1,0 mm de diâmetro da seção transversal) engatam 0,50 mm retenção quase semelhante à dos grampos Co-Cr (AU)
Assuntos
Resinas Sintéticas , Ligas de Cromo , Prótese ParcialRESUMO
Introducción: La reconstrucción de los huesos del cráneo es un procedimiento complejo y representa un reto para el grupo médico tratante; generalmente se realiza en pacientes con pérdida de la bóveda craneana secundaria a procesos infecciosos crónicos no controlados o por osteorradionecrosis, lo que implica mayor posibilidad de fracaso o rechazo de los materiales utilizados para la reparación del defecto. La selección del material para sustituir la bóveda craneana es difícil debido a la diversidad de productos existentes; el material debe ser inerte, ligero, fácil de colocar y adaptable al defecto, con lo cual se ofrece mejores resultados estéticos y funcionales. Con el diseño por computadora del implante es posible ofrecer un implante individual y específico para cada defecto y paciente. Caso clínico: Mujer con diagnóstico de estesioneuroblastoma tratada con resección craneofacial anterior y radioterapia; como complicación presentó osteomielitis y osteorradionecrosis y, consecuentemente, pérdida de la bóveda craneana en la región frontal; este defecto fue reconstruido con un implante de poli-éter-éter-cetona diseñado por computadora con base en el defecto evaluado por tomografía computarizada. Se muestran los resultados obtenidos. Conclusiones: El implante diseñado por computadora realizado con poli-éter-éter-cetona es una alternativa segura, fácil de usar y con gran adaptabilidad a los defectos de la bóveda craneana.
BACKGROUND: Reconstruction of the bones of the skull is a complex procedure and represents a challenge for the surgical team. It is generally performed in patients who have loss of the cranial vault secondary to chronic infection or uncontrolled osteoradionecrosis, indicating a greater chance of failure or rejection of the materials used for repair of the defect. Selection of material to replace the cranial vault is complex due to the diversity of existing products. The ideal material is inert, lightweight, easy to fit and adaptable to the defect, offering the best aesthetic and functional results. Computer design of the implant makes this process easier by providing an implant specific to each individual patient and defect. CLINICAL CASE: We report the case of a patient who was diagnosed with esthesioneuroblastoma and was treated with anterior craniofacial resection and radiotherapy. Osteomyelitis and osteoradionecrosis were consequent complications with loss of the cranial vault in the frontal region. The defect was reconstructed with a polyetheretherketone (PEEK) computer-designed implant based on the defect evaluated by computed tomography. Results obtained are shown below. CONCLUSIONS: The PEEK computer-designed implant is a safe and easy to use alternative with great adaptability to cranial vault defects.