Fracture strength of tie wings in a newly-developed polycarbonate bracket / 대한치과교정학회지

OBJECTIVE: With an increasing demand for esthetic orthodontic appliances, the interest in polycarbonate brackets has also increased. However, polycarbonate bracket wings are prone to fracture. The purpose of this study was to evaluate the clinical usefulness of a newly-developed polycarbonate bracket by measuring the fracture strength of bracket tie wings. METHODS: Alice (K.M. Daicom, Seoul, Korea) and Spirit MB (Ormco, Glendora, CA, USA) brackets were used as an experimental and control bracket respectively. Each bracket group was divided into halves. One half was untreated and the other half was treated with 2,000 times of thermocycling between 5 degrees C and 55 degrees C. The fracture strength of the wing was measured by a universal testing machine. RESULTS: Alice bracket wings showed significantly higher strength than Spirit MB bracket wings in both untreated and thermocycled bracket cases. CONCLUSION: Alice brackets may be used clinically in terms of the strength of bracket wings.

The Effect of Surface Treatment on Bond Strength of Polycarbonate Bracket / 대한치과교정학회지

OBJECTIVE: The purpose of this study was to evaluate whether the bond strength of polycarbonate brackets can be increased through surface treatment. METHODS: One hundred polycarbonate brackets (Alice) were bonded to bovine incisors with light-cured adhesive. The bracket bases were treated with one of three methods; sandblasting, plastic conditioner application, and combined treatment with sandblasting and plastic conditioner. The brackets without any surface treatment served as the control. The shear bond strength was tested with a universal testing machine, and failure pattern was assessed with the adhesive remnant index. RESULTS: The shear bond strength in all experimental groups was higher than that of the control group (p < 0.001). The group treated with plastic conditioner after sandblasting showed statistically higher shear bond strength than the sandblasting only group (p < 0.05). The group treated with plastic conditioner after sandblasting showed higher shear bond strength than plastic conditioner only group, but the difference was not statistically significant. CONCLUSION: The above results suggest that the surface treatments of polycarbonate bracket is mandatory to improve bond strength, and the most effective method is an application of plastic conditioner after sandblasting.