RESUMO
Context: The effect of different curing units on bond strength of orthodontic brackets is still unclear when utilizing nanofilled composites in comparison with traditional Transbond-XT. Aim: To evaluate the influence of two adhesive promoters and two curing-light units on the shear bond strength (SBS) of orthodontic brackets. Settings and Design: The factors under study were adhesive promoters (nanofilled composite - Filtek-Z350 flowable restorative and conventional orthodontic adhesive - Transbond XT) and curing-light units (halogen lamp - Ultralux and LED device - Radii-Call). Material and Methods: Forty lower bovine incisors were utilized. The teeth were distributed in four groups (n = 10) according to the combination between adhesive promoters and curing-light units. Scotchbond Multipurpose-Plus and Transbond-XT primer were used to bond Filtek-Z350 Flowable Restorative and Transbond-XT, respectively. After storage in distilled water for 24 h, the brackets were subjected to SBS test at a speed of 0.5 mm/min until bracket debonding. The Adhesive Remnant Index (ARI) was assigned at fractured specimens. Statistical analysis used: Analysis of variance and Tukey test were utilized. The Kruskal-Wallis test was used to compare ARI scores between the groups (p<0.05). Results: There was statistically significant difference between the adhesive promoters tested. Transbond-XT showed higher SBS means than Filtek-Z350. There was no statistically significant difference between both curing-light units tested in this study, neither between ARI scores. Conclusions: The conventional orthodontic adhesive presented higher bond strength than the nanofilled composite, although both materials interacted similarly to the teeth. The curing-light devices tested did not influence on bond strength of orthodontic brackets.
RESUMO
Due to the improvement of the composite resin and esthetic desire of the patient, amalgam restoration has been replaced by composite resin. However, still there are many unsolved problems, for example, technique sensitivity, polymerization shrinkage stress and limited mechanical properties. These factors results in fracture of the restoration and secondary caries of the tooth. Also the use of the dental bonding system should be used for the retention of the restoration. In this paper, I want to talk about the present and the future of the remineralizing component released from dental composite resin to overcome the secondary caries and there possibility in the clinical use.