RESUMO
Abstract This study aimed to evaluate the influence of different ethanol concentrations on dentin roughness, surface free energy, and contact angle between AH Plus and the root canal dentin. One hundred human maxillary anterior teeth were split longitudinally and 200 dentin specimens were polished to make the surface flatter and smoother. An acrylic bar was positioned between two dentin specimens and impression material was added to create a block, simulating an instrumented root canal space. Specimens were removed from the mold and cleaned in an ultrasonic bath for 10 min. Thereafter, dentin specimens were divided into four groups (n = 50) according to the drying methods used: a) wet: vacuum only, b) paper points: vacuum + absorbent paper points, c) 70% alcohol: 70% alcohol (1 min) + vacuum + absorbent paper points, and d) 100% alcohol: 100% alcohol (1 min) + vacuum + absorbent paper points. A rugosimeter and a goniometer were used to verify the roughness (Ra) and to measure the surface free energy and the contact angle between the AH Plus sealer and the root canal dentin. ANOVA and Tukey tests (α = 0.05) were used for statistical analysis. The 70% and 100% ethanol groups showed significantly decreased roughness as well as increased surface free energy in the root canal dentin when compared to the wet and paper point groups. In addition, ethanol significantly reduced the contact angle between the AH Plus sealer and the root canal dentin. Ethanol solutions (70% and 100%) provide better wettability of AH Plus sealer on dentin surfaces.
Assuntos
Humanos , Dentina/química , Dentina/efeitos dos fármacos , Resinas Epóxi/química , Etanol/química , Materiais Restauradores do Canal Radicular/química , Raiz Dentária/química , Raiz Dentária/efeitos dos fármacos , Análise de Variância , Colagem Dentária/métodos , Dentina/ultraestrutura , Teste de Materiais , Reprodutibilidade dos Testes , Propriedades de Superfície/efeitos dos fármacos , MolhabilidadeRESUMO
Abstract Sonic vibrations may improve the bond strength and durability of fiberglass posts by improving adhesive penetration into dentin as well as the cement flow. The objective of this study was to evaluate the effect of sonic vibrations on the bond strength between fiberglass posts and root dentin using the pull-out test. Bovine roots were endodontically treated and divided randomly into four groups (n=12): Group C - conventional cementation (control); Group SA - sonic vibration (Smart Sonic Device, FGM) of the adhesive system and conventional post accommodation; SP group - conventional adhesive application and sonic vibration of the post during accommodation; and SASP - sonic vibration of the system adhesive and the post during accommodation. The posts were cleaned, treated with a silane and adhesive system (Ambar, FGM), and cemented with a dual-cured resin cement (Allcem Core, FGM). After 24 h, the specimens were subjected to mechanical tests and failure analyses. Representative specimens were analyzed by a scanning electron microscope to observe the cementation line. The results were analyzed using ANOVA and Tukey's test (a=5%). The bond strengths were as follows: SASP (90.9±27.1 N), C (121.4±60.6 N), SA (127.6±31.8 N) and SP (156.4±41.3 N). The use of sonic vibrations during the application of adhesive or post cementation separately did not affect the bond strength but had a negative effect when used for both procedures.
Resumo Vibrações sônicas podem melhorar a resistência e a durabilidade da união de pinos de fibra de vidro, melhorando a penetração do sistema adesivo à dentina, bem como o escoamento do cimento. O objetivo deste estudo foi avaliar o efeito da vibração sônica na resistência de união de pinos de fibra de vidro à dentina radicular, através de ensaio pull out. Raízes bovinas tratadas endodonticamente foram preparadas e divididas aleatoriamente em quatro grupos (n=12): Grupo C - cimentação convencional, (controle); Group SA - vibração sônica (Smart Sonic Device(r), FGM) do sistema adesivo e assentamento convencional do pino; grupo SP - aplicação convencional do sistema adesivo e vibração sônica no assentamento do pino; e SASP - vibração sônica do sistema adesivo e no assentamento do pino. Os retentores foram limpos, tratados com silano e sistema adesivo (Ambar, FGM) e cimentados com cimento resinoso dual (Allcem Core, FGM). Após 24 h as amostras foram submetidas ao teste mecânico e análise de falha. Amostras representativas foram avaliadas sob microscópio eletrônico de varredura, para avaliação da linha de cimentação. Os resultados foram analisados por meio de análise de variância e teste de Tukey (a=5%). Os resultados obtidos foram: SASP (90,9±27,1 N, C (121,4±60,6 N), SA (127,6±31,8 N) e SP (156,4±41,3 N). A vibração sônica para aplicação apenas do sistema adesivo ou pino não afetou a resistência de união, entretanto interferiu negativamente quando utilizada para ambos procedimentos.
Assuntos
Animais , Bovinos , Dentina/química , Vidro , Técnica para Retentor Intrarradicular , Raiz Dentária/química , Vibração , Adesivos Dentinários/química , Técnicas In Vitro , Microscopia Eletrônica de VarreduraRESUMO
The cure time of endodontic sealers may influence the bond strength of fiber posts to root dentin. Forty teeth were selected and endodontically filled using calcium hydroxide cement and then divided into 2 groups according to the time elapsed between endodontic filling and post luting (n = 20): Immediately - glass fiber post luting immediately after endodontic filling; and Delayed - post luting performed 7 days after endodontic filling. The roots were also subdivided according to resin cement used for post luting (RelyX ARC and RelyX Unicem). The specimens were stored at 37°C for 24 h and sectioned in six 1-mm-thick slices from cervical, middle and apical thirds. The slice specimens were submitted to a push-out test at a crosshead speed of 0.5 mm/min, and the bond strength values obtained (MPa) were submitted to two-way ANOVA in a split-plot arrangement and Tukey's test (α=0.05). For both RelyX ARC and Unicem, the bond strength was significantly higher when the posts were cemented 7 days after the endodontic treatment. RelyX Unicem showed significantly higher bond strength values than RelyX ARC for both cementation periods. It was concluded that post luting should be made after the complete setting of the root canal sealer. Self-adhesive resin cement should be preferred for fiber post luting.
O tempo de presa de cimentos endodônticos pode afetar a resistência de união de pinos de fibra de vidro à dentina radicular. Quarenta dentes foram selecionados e tratados endodonticamente com cimento à base de hidróxido de cálcio. Em seguida, os mesmos foram divididos em dois grupos de acordo com o tempo decorrido entre o tratamento endodôntico e a cimentação definitiva (n=20): Imediato - pinos de fibra de vidro cimentados após o tratamento endodôntico; e Mediato - cimentação do pino realizada 7 dias após o tratamento endodôntico. As raízes foram subdivididas de acordo com o cimento resinoso (RelyX ARC e RelyX Unicem). As amostras foram armazenadas a 37 °C durante 24 h e seccionadas em seis fatias de 1 mm de espessura relacionadas com terços cervical, médio e apical. Os espécimes foram submetidos a teste de push-out a uma velocidade de 0,5 mm/min e os valores de resistência de união obtidos (MPa) foram submetidos à análise de variância em esquema de parcelas subdivididas e teste de Tukey (α=0,05). Para os cimentos RelyX ARC e Unicem, a resistência de união foi maior quando os pinos foram cimentados 7 dias após o tratamento endodôntico. RelyX Unicem apresentou valores de resistência de união superiores ao RelyX ARC para os períodos de cimentação. Concluiu-se que a cimentação do pino de fibra de vidro deve ser feita após o completo tempo de presa do cimento endodôntico. Cimentos resinosos auto-adesivos devem ser preferidos para cimentação de pinos de fibra.
Assuntos
Humanos , Colagem Dentária , Dentina/química , Raiz Dentária/química , Materiais Restauradores do Canal Radicular , Fatores de TempoRESUMO
Objective: This study evaluated the hydrophobicity of dentin surfaces that were modified through chemical silanization with octadecyltrichlorosilane (OTS). Material and Methods: An in vitro experimental study was performed using 40 human permanent incisors that were divided into the following two groups: non-silanized and silanized. The specimens were pretreated and chemically modified with OTS. After the chemical modification, the dentin hydrophobicity was examined using a water contact angle measurement (WCA). The effectiveness of the modification of hydrophobicity was verified by the fluid permeability test (FPT). Results and Conclusions: Statistically significant differences were found in the values of WCA and FPT between the two groups. After silanization, the hydrophobic intraradicular dentin surface exhibited in vitro properties that limit fluid penetration into the sealed root canal. This chemical treatment is a new approach for improving the sealing of the root canal system.
Assuntos
Humanos , Cavidade Pulpar/efeitos dos fármacos , Dentina/efeitos dos fármacos , Interações Hidrofóbicas e Hidrofílicas/efeitos dos fármacos , Tratamento do Canal Radicular/métodos , Silanos/química , Infiltração Dentária , Cavidade Pulpar/química , Permeabilidade da Dentina/efeitos dos fármacos , Dentina/química , Microscopia Eletrônica de Varredura , Reprodutibilidade dos Testes , Camada de Esfregaço , Propriedades de Superfície/efeitos dos fármacos , Fatores de Tempo , Raiz Dentária/química , Raiz Dentária/efeitos dos fármacosRESUMO
O presente estudo determinou in vitro a difusão da calcitonina sintética de salmão, como medicação intracanal, até a superfície externa radicular, com e sem a presença de cemento radicular. Foram utilizados cinqüenta e quatro incisivos centrais humanos, divididos em dois grupos com 21 dentes cada e dois grupos com 6 dentes cada (controle negativo). Após o preparo endodôntico, os dentes receberam 10 ml de calcitonina como medicação intracanal. Feitos o selamento e a impermeabilização externa da raiz, os espécimes foram acondicionados em tubos com solução salina tamponada com fosfatos e incubados em estufa a 37°C. Foram colhidas amostras da solução salina nos períodos de 1, 4 e 7 dias. Para a análise das soluções teste, utilizou-se teste ELISA. Os resultados mostram que existe a difusão da medicação testada até a superfície externa radicular em todas as amostras dos grupos teste. O fator ausência de cemento radicular permite a passagem de maiores quantidades de calcitonina, dados estatisticamente significantes ao nível de 5%. Os maiores valores de difusão foram encontrados no sétimo dia, tanto para o grupo com cemento como para o grupo sem cemento, mostrando uma relação direta entre tempo e difusão da medicação intracanal testada.
Assuntos
Animais , Humanos , Calcitonina/química , Cimentos Dentários , Dentina/química , Técnicas In Vitro , Irrigantes do Canal Radicular/química , Raiz Dentária/química , Permeabilidade da Dentina , Dentina/ultraestrutura , Ensaio de Imunoadsorção Enzimática , Microscopia Eletrônica de Varredura , Preparo de Canal Radicular , Fatores de TempoRESUMO
O condicionamento da superfície radicular com ácidos vem sendo proposto há algum tempo, mas os resultados dos estudos säo inconclusivos e contraditórios. Neste trabalho, os autores discutem a importância do condicionamento radicular através do ácido cítrico para a regeneraçäo periodontal. A concentraçäo, o pH e a técnica de aplicaçäo da substância mais aceitas atualmente estäo também abordados