Microfiltración marginal de resinas de relleno masivo y nanohíbrida en molares deciduos / Marginal microleakage of bulk fill and nanohybrid resins in deciduous teeth

Introducción: En la atención odontológica a niños es crucial seleccionar materiales restaurativos con buen rendimiento clínico y corto tiempo de aplicación, especialmente en pacientes con capacidad de atención limitada. Las resinas compuestas, con el mejoramiento de sus propiedades físicas y mecánicas, constituyen hoy uno de los materiales de mayor elección por el odontopediatra. Las resinas de relleno masivo son una alternativa atractiva para las restauraciones en el sector posterior. Objetivo: Comparar el grado de microfiltración marginal de resinas de relleno masivo y nanohíbrida en molares deciduos. Métodos: Estudio experimental, in vitro, en cuarenta molares deciduos; exodonciados por motivos terapéuticos, divididos en dos grupos. Grupo I: resina nanohíbrida con técnica incremental (Tetric® N Ceram - Ivoclar Vivadent) y Grupo II: resina de relleno masivo con técnica monoincremental (Tetric® N Ceram bulk fill - Ivoclar Vivadent). Se realizó un proceso de termociclado manual de 500 ciclos, entre 5 ºC ± 2 ºC y 55 ºC ± 2 ºC. Las muestras fueron sumergidas en azul de metileno al 0,5 por ciento durante 24 horas a 37 ºC. Se analizaron con el microscopio estereoscópico de luz a 40X. Resultados: Todas las muestras presentaron microfiltración. Con el uso de resina nanohíbrida, el 25 presentó microfiltración leve; el 30 por ciento, moderada; y el 45 por ciento, severa. En el grupo de la resina de relleno masivo, el 30 por ciento presentó microfiltración leve; el 35 por ciento, moderada; y el 35 por ciento, severa. No se encontró diferencia significativa entre ambos grupos (p = 0,55). Conclusiones: Ambas resinas, de relleno masivo y nanohíbrida, presentaron similar microfiltración marginal in vitro, en molares deciduos; por lo que la técnica de relleno masivo, por su fácil y rápida aplicación en un solo tiempo, es una buena alternativa en la rehabilitación dental odontopediátrica(AU)

Introduction: In children's dental care it is crucial to select restorative materials of proven clinical quality and a short application period, particularly with patients of limited attention capacity. Due to their improved physical and mechanical properties, composite resins are currently one of the materials of choice for children's dental care. Bulk fill resins are an attractive alternative for posterior restorations. Objective: Compare the degree of marginal microleakage of bulk fill and nanohybrid resins in deciduous teeth. Methods: An experimental in vitro study was conducted of 40 deciduous teeth extracted for therapeutic reasons, which were divided into two groups. Group I: nanohybrid resin by incremental technique (Tetric® N Ceram - Ivoclar Vivadent) and Group II: bulk fill resin by monoincremental technique (Tetric® N Ceram bulk fill - Ivoclar Vivadent). A manual 500-cycle thermocycling procedure was performed at 5ºC ± 2ºC to 55ºC ± 2ºC. The samples were soaked in 0.5 percent methylene blue at 37ºC for 24 hours and analyzed under a light stereo microscope at 40X. Results: Microleakage was present in all the samples. In the nanohybrid resin group, microleakage was mild in 25 percent, moderate in 30 percent and severe in 45 percent. In the bulk fill resin group, microleakage was mild in 30 percent, moderate in 35 percent and severe in 35 percent. No significant difference was found between the groups (p = 0.55). Conclusions: Both resins, bulk fill and nanohybrid, presented similar in vitro marginal microleakage in deciduous molars. The bulk fill technique is therefore a good alternative for children's dental rehabilitation, due to its easy and fast application in a single session(AU)

Tratamiento Rehabilitador Estético-Oclusal con Resinas Compuestas en una Paciente con Mordida Profunda y Desgaste Severo / Aesthetic-Occlusal Rehabilitation Treatment with Composite Resins in a Patient with Deep Bite and Dental Wear

RESUMEN: La rehabilitación oral tradicional del paciente con mordida profunda y braquifacial puede ser muy compleja e invasiva, sin embargo, podría involucrar muchas especialidades para su resolución ideal. Un análisis integral estético-oclusal es necesario antes de empezar el tratamiento para hacer propuestas con el menor costo biológico, de tiempo y económico. La odontología adhesiva permite una propuesta aditiva y no invasiva como un tratamiento de mediano plazo o transitorio. Este artículo presenta un caso de una paciente de 46años de edad con mordida profunda anterior y desgaste dental severo en las caras palatinas de los dientes antero-superiores, sin disfunción temporomandibular, ni compromisos sistémicos. Se destaca la rehabilitación estética- oclusal con el mínimo compromiso biológico (ultra-conservadora), mediante restauraciones adhesivas semi-indirectas de resina compuesta con acompañamiento de 12meses. Esta propuesta rehabilitadora con resinas compuestas representa una alternativa de tratamiento para el manejo del paciente con mordida profunda anterior. El control a un año de tratamiento demostró que se siguió una secuencia y resolución que aseguró los principios de la rehabilitación oral, al mismo tiempo, se procedió de la manera menos invasiva posible.

ABSTRACT: The traditional oral rehabilitation of the patient with deep bite and brachifacial can be very complex and invasive, however, a number of treatments could be considered to improve rehabilitation. A comprehensive aesthetic-occlusal analysis is necessary prior to starting treatment in order to consider the best procedure, time involved, and economic cost. Adhesive dentistry allows an additive and non-invasive proposal as a medium-term or transitory treatment. A case of a 46-year-old patient is presented, with anterior deep bite and severe dental wear on palatal surfaces of the antero-superior teeth, without temporomandibular dysfunction, or systemic compromises. The objective was to emphasize the aesthetic and occlusal rehabilitation with the least biological commitment (ultraconservative), through semi-indirect adhesive restorations of composite resin with 12 months follow-up. This restorative proposal with composite resins represents an alternative treatment for patient management with anterior deep bite. Control at one year of treatment showed that a sequence and resolution was followed, that ensured adequate oral rehabilitation in the least invasive manner possible.

Avaliação do desempenho de duas resinas compostas e dois sistemas adesivos em um novo protocolo cirúrgico-restaurador para tratamento de lesões cervicais não-cariosas associadas à recessão gengival: estudo clínico controlado randomizado / Evaluation of two resin composites and two adhesives for a novel surgical-restorative protocol for the treatment of non-carious cervical lesions associated with gingival recession: a randomized controlled clinical trial

A recessão gengival está frequentemente associada à lesão cervical não-cariosa. Quando as duas lesões estão associadas, dão origem a uma lesão combinada (LC) que tem um prognóstico de tratamento diferente de quando as duas lesões se apresentam sozinhas. A literatura apresenta alguns estudos que avaliaram uma abordagem multidisciplinar para otimizar o tratamento dessa LC. No entanto, as abordagens propostas possuem limitações de técnicas e materiais, sem um protocolo clínico ideal estabelecido. Dessa forma, o objetivo do presente estudo foi avaliar um novo protocolo multidisciplinar, com duas resinas compostas e dois sistemas adesivos distintos através de estudo clínico randomizado. Foram selecionadas 80 lesões combinadas, alocadas aleatoriamente em um dos seguintes grupos: AC+NP (n=20) - restauração parcial da lesão cervical com resina nanoparticulada e sistema adesivo de condicionamento total em 2 passos e cirurgia para recobrimento radicular, AU+NP (n=20) - restauração parcial da lesão cervical com resina nanoparticulada e sistema adesivo autocondicionante e cirurgia para recobrimento radicular, AC+MH (n=20) - restauração parcial da lesão cervical com resina microhíbrida e sistema adesivo de condicionamento total em 2 passos e cirurgia para recobrimento radicular, AU+MH (n=20) - restauração parcial da lesão cervical com resina microhíbrida e sistema adesivo autocondicionante e cirurgia para recobrimento radicular. Foram realizadas avaliações das restaurações pelo método USPHS após 1 semana, 6 meses e 12 meses. A análise de sobrevivência das restaurações foi realizada através do teste de Kaplan-Meier. Os protocolos restauradores foram comparados para cada parâmetro pelo teste exato de Fisher, considerando tipo de adesivo e tipo de resina empregados. Teste de Qui-Quadrado foi utilizado para comparação das taxas após 6 e 12 meses entre os grupos testados. A avaliação da normalidade foi realizada pelo teste de Shapiro-Wilks. As medidas clínicas de RGR, PS, NIC, ETQ, ATQ, Hipersensibilidade Dentinária e Estética (VAS) foram comparadas tanto intra como intergrupo por teste de variância de medidas repetidas ANOVA de dois fatores e Tukey com teste post-hoc. IP, IS foram avaliados pelo teste de Qui-Quadrado. Os parâmetros de DC, Porcentagem de recobrimento e RecRed foram analisados pelo ANOVA 1 fator. Pôde-se observar uma taxa de sucesso geral cumulativo do tratamento de 98,7% aos 6 primeiros meses e 92,4% aos 12 meses de acompanhamento, sem diferença estatisticamente significativa entre os tempos e grupos avaliados. Todos os grupos apresentaram melhora estética e redução de hipersensibilidade significativa em relação ao baseline (p<0,001) após 6 meses. Houve redução significativa da recessão gengival relativa (p<0,05) após 12 meses de acompanhamento. Dentro dos limites do presente estudo, pode-se concluir que os materiais utilizados apresentaram desempenho clínico similares, sendo que as diferentes combinações de materiais restauradores adesivos estudados associados às técnicas cirúrgicas utilizadas podem ser empregadas no tratamento das lesões cervicais não-cariosas associadas a recessão gengival(AU)

Non-carious cervical lesion is frequently associated with gingival recession, resulting in a combined lesion (CL) that has a different treatment prognosis when the two lesions appear alone. The literature presents few studies that evaluate a multidisciplinary approach to optimize the treatment of this CL. The previously proposed approaches and materials have limitations and an optimal clinical protocol has not been established yet. Thus, the aim of this study was to evaluate a novel multidisciplinary protocol with two resin composites and two different adhesive systems by a randomized clinical. Eighty combined lesions were randomly assigned to one of the following groups: NP + TE (n = 20) - partial restoration of cervical lesions with nanofilled composite and total-etch adhesive system and periodontal surgery for root coverage, NP + UA (n =20) - partial restoration of cervical lesions with nanofilled composite and self-etching adhesive system and periodontal surgery for root coverage, MH + TE (n = 20) - partial restoration of cervical lesions with microhybrid composite and total-etch adhesive system and periodontal surgery for root coverage, MH + UA (n = 20) - partial restoration of cervical lesions with microhybrid composite and selfetching adhesive system and periodontal surgery for root coverage. Restorations were assessed using the USPHS criteria after one week, six months and twelve months. Survival rate was assessed by Kaplan-Meier test. Restorative protocols were compared for each parameter by Fisher's exact test, considering type of adhesive and type of composite used. Chi-square test was used to compare the rates at 6 and 12 months between the groups tested. Normality evaluation was assessed by Shapiro-Wilks test. Clinical measures of RGR, PS, NIC, KTW, KTH, Hipersensitivity and Esthetics (VAS) were compared both intra and inter-group by analysis of variance of repeated measures Two-Way ANOVA and Tukey posthoc test. IP, IS were evaluated by Chi-square test. CD parameter, Coverage percentage and RecRed were evaluated by One-Way ANOVA. It was observed a successful cumulative rate of 98.7 % at 6 months and 92.4 % at 12 months with no significant difference between groups. When compared to baseline, all groups presented significant improvement in esthetics and reduction of hipersensitivity at 6 months (p<0.001). Significant reduction of gingival recession was recorded after 12 months (p<0.05). It can be concluded that there is no difference between the tested materials, and different combinations of adhesive restorative materials associated with periodontal surgical techniques can be used to treat non-carious cervical lesions associated with gingival recession(AU)

Effect of Home Bleaching on the Color Matching of Composite Resin Restorations

Objective: To investigate the effect of home bleaching on color matching between the dental restoration and the adjacent tooth structure after the staining process. Material and Methods: Ten intact maxillary central incisors were used. After preparation (semimesial restoration of the specimens), the specimens were immersed in a colored solution for 14 days and then were washed and the bleaching process was there after performed. A spectrophotometer apparatus was used to determine the color of the specimens in the part of the tooth filled with restorative material three times, including before the staining process, fourteen days after the staining process and immediately after the bleaching process. Paired t-test was employed to compare the color of the intact tooth and the dental restoration before and after the staining and bleaching processes. The level of significance was set at 5%. Results: Pre-bleaching E color of the teeth was 68.1, which increased to 78.8% after bleaching, and this increase was also statistically significant (p<0.001). Pre and Post-bleaching E color of composite restorations was 65% and 77.6%, respectively. This increase was also statistically significant (p<0.001). Postbleaching E color of the tooth and composite material was 78.8% and 77.6%, respectively. This difference was not statistically significant (p=0.342). Conclusion: The staining and bleaching processes had a significant effect on the discoloration of the dental restoration and the tooth; however, the application of bleaching on the teeth and composite improved the tooth composite color-match.

Efeito da termociclagem em diferentes soluções nas propriedades físicas e químicas dos materiais resinosos / Effect of thermocycling on different solutions on the physical and chemical properties of resinous materials

Os estudos em laboratório devem ser realizados para verificar e comprovar a eficácia destes novos materiais, equipamentos, técnicas e tecnologias, e sendo considerados aprovados, uma outra etapa in vivo deverá ser realizada. O advento da odontologia adesiva já causou profundas mudanças na prática da odontologia. A proposta deste trabalho foi avaliar in vitro, o efeito da termociclagem, em diferentes temperaturas (5°C, 55°C), soluções (água destilada, óleo mineral), quantidade de ciclos (500, 5.000, 10.000), utilizando um material restaurador universal nanohíbrido fotopolimerizável contendo carga inorgânica em uma matriz de metacrilato e um sistema de cimentação à base de resina composta de polimerização dual. A finalidade da termociclagem é o envelhecimento dos materiais pelo mecanismo do "choque térmico". O objetivo deste trabalho foi demonstrar se a termociclagem interfere ou não nas propriedades físicas e químicas destes materiais. Foram confeccionados 90 corpos de prova (cp) de cada material, cinco de cada grupo, (cpCRc = corpos de prova do cimento resinoso com YTZP, cpCRs= corpos de prova do cimento resinoso sem Y-TZP, e cpRC= corpos de prova da resina composta), que foram armazenados em água destilada, até o início da termociclagem. Estes espécimes receberam o tratamento térmico (nas distintas soluções) e após este evento foram realizadas as mensurações de massa, rugosidade, nanodureza e avaliações em MEV/ EDS, FTIR/UATR. Os dados obtidos foram submetidos ao teste Anova três fatores (α = 0,05). Os grupos cpCRc, cpCRs, cpRC não apresentaram alterações e ou modificações nas propriedades físicas e químicas dos materiais, independentemente do tipo de ciclagem, solução, temperatura e número de ciclos. Portanto, o uso da termociclagem, nas temperaturas de (5°C, 55°C), diferentes soluções (água destilada, óleo mineral), quantidade de ciclos (500, 5.000, 10.000) não foi observado o envelhecimento térmico para estes materiais(AU0

Laboratory studies should be performed to verify and prove the efficacy of these new materials, equipment, techniques and technologies, and being considered approved, another in vivo step should be performed. The advent of adhesive dentistry has already caused profound changes in the practice of dentistry. The determination of bond strength of dentin adhesives is a matter of great importance and interest in our profession. The purpose of this work is to evaluate in vitro the effect of thermocycling at different temperatures (5 °C, 55 °C), solvents (distilled water, mineral oil), number of cycles (500, 5.000, 10.000) and a universal nano-hybrid restorative light-curing material with contains inorganic fillers in a methacrylate matrix and a dual-curing composite-based luting system for permanent adhesive luting. The purpose of thermocycling is thermal and hydrolytic degradation; and the objective of this work is to demonstrate if the thermocycling interferes or not in the study in the physical and chemical properties. A metal matrix was produced to make the specimens (sp). A total of 90 (sp) from each material, five from each group, were prepared (BFX-C = YTZP with resin cement sp, BFX-S = YTZP without resin cement sp, and GRD = composite resin specimens) which were stored in distilled water until the beginning of the thermocycling. The sp received the thermal treatment (the different solvents) and after this event were reached the messages of mass, roughness, hardness. and evaluations in SEM / EDS, FTIR / UATR. Data were obtained from the Anova test (α = 0.05). The groups BFX-C, BFX-S, GRD are the parameters keys and physical properties of the materials, regardless of the type of cycling, solvent, temperature and number of cycles. Therefore, the use of thermocycling, at temperatures of 5 °C, 55 °C, different solvents, mineral oil, amount of heat (500, 5,000, 10,000) was not observed in the thermal heat for these materials(AU)

Influência da aplicação de um sistema adesivo na resistência de união entre resinas bulk fill flow e resina nanoparticulada em reparos / Adhesive system influence on bond strength between bulk fill flow and conventional nanoparticulated cover resin on a repair procedure

O objetivo desta pesquisa foi avaliar a influência da utilização ou não do bond do sistema adesivo Adper Scotchbond Multiuso(A) e o bond Gluma da Heraeus(G) na resistência de união entre as resinas do tipo flow Filtek Bulk Fill Flow(F) e X-tra base (X) como base e uma convencional nanoparticulada Z350 XT(Z)) como cobertura. Simulando assim seu uso em reparos de restaurações diretas em dentes posteriores. Foram confeccionados 120 espécimes em resina composta do tipo flow no formato tronco-cônico com as dimensões de 2mm base menor, 4mm de altura e 4 mm de base maior. 60 Filtek Bulk Fill(F) e 60 Xtra base (X). Metade de cada grupo (n=30) foi envelhecida por termociclagem 5.000 ciclos de 5°C a 55°C, (FE, XE), a outra metade não sofreu envelhecimento (FN e XN). Esses espécimes foram divididos em 3 subgrupos (n=10), sobre a base menor dessas 10 amostras foi aplicado o Bond de cada sistema adesivo após condicionadas pelos seus respectivos ácidos nos tempos preconizados pelos fabricantes. As outras 10 unidades de cada grupo não receberam qualquer sistema adesivo. Na simulação do reparo as duas primeiras metades em teflon foram invertidas ficando a área menor voltada pra cima. Sobre essa face foram colocadas outras duas metades em teflon com a área menor voltada para baixo. Foi inserida então a resina Z350 pela técnica incremental e fotopolimerizada por 20s a 800mw/cm². Após 24h de armazenamento em água destilada, em estufa bacteriológica os espécimes, agora com formato de ampulheta, foram tracionados na máquina de ensaios universais (EMIC). Todos os espécimes fraturados tiveram o tipo de falha analisados ao estereomicroscópio e também ao microscópio eletrônico de varredura (MEV). Os dados coletados no ensaio de tração foram analisados através de ANOVA 3- fatores e teste de Tukey (p<5%). Houve diferença significativa (p<5%) para a variável aplicação de sistema adesivo para a resina Filtek Bulk Fill flow que apresentou médias maiores (24,99 ± 4,3 MPa) quando comparadas ao grupo no qual não foi aplicado adesivo (18,20 ± 5,31 MPa). O mesmo não ocorreu com a resina X-tra base, na qual o fator adesivo não interferiu significantemente. Quando comparado o desempenho das resinas Filtek Bulk Fill flow e X-tra base (26,99 ± 6,11 MPa) sem aplicação de sistema adesivo, também se verificou diferença significativa, o que não ocorreu para a resina X-tra base quando comparados ambos os subgrupos. As falhas foram 100% adesivas para todos os grupos(AU)

The aim of our paper was to analyse the bonding influence of Adper Scotchbond Multipurpose Adhesive (A) and Heraeus Gluma universal bond (G), or no bond application, on bond strength between microhibrid Filtek Bulk Fill Flow (F) and nanohibrid X-tra base (X) as based composite resin and the conventional nanoparticulate Z350 XT (Z)) as cover. Simulating non-invasive repairs of direct restorations on posterior teeth. A total of 120 specimens were made from flow composite resin in the conical trunk format with the dimensions of 2x4x4, for 40s with Led-5 (N/S LD51803005) at 800mw/cm². Sixty Filtek bulk fill (F) and sixty X-tra base (X) were made. Half of each group (n=30) was aged by thermocycling 5,000 cycles from 5° C to 55° C, (FE, XE), the other half were not subjected to any aging procedure (FN, XN). These specimens were randomly divided into 3 subgroups (n = 10), on the smaller diameter of the 10 samples the Bond of each adhesive system were applied after conditioned by their respectively acids at the time recommended by the manufacturers. The other 10 units of each group did not receive any adhesive system. In the sequency of repair simulation the first two Teflon halves were turned up with the smaller diameter turned upwards. Above this face were placed two other halves in Teflon with the smaller diameter facing down. The Z350 repair composite resin were inserted by incremental technique and photopolymerized for 20s at 800mw/cm². After 24h of storage in distilled water in a bacteriological oven, the now hourglass-shaped specimens were drawn in the universal testing machine EMIC. All the fractured specimens had the type of failure analyzed in stereomicroscope. The most significant faulting specimens were evaluated with electronic microscope (MEV). The data collected at the traction test were analyzed through 3-factor ANOVA and Tukey's test (p <5%). There was a significant difference (p <5%) for the variable adhesive system application for Filtek Bulk Fill flow resin that presented averages (24.99 ± 4.3 MPa) when compared to the group in which no adhesive was applied (18.20 ± 5.31 MPa). The same did not occur with X-tra base resin, in which the adhesive factor did not interfere significantly. When comparing the performance of Filtek Bulk Fill Flow resins and X-tra base (26.99 ± 6.11 MPa) without application of adhesive system, a significant difference was also observed, which did not occur for X-tra base resin when compared both subgroups. Most of the failures were adhesive for all groups. Scanning electron microscopy images do not reveal any traces of discontinuity between the layers of the materials used (resin x resin or resin x adhesive)(AU)

Técnicas para reduzir os efeitos da contração de polimerização das resinas compostas fotoativadas / Techniques for reducing the effects of polymerization shrinkage of composites photoactivated resins

Introdução: uma complicação inerente a todas as resinas compostas é o stress gerado pela contração de polimerização. As resinas compostas da atualidade, após a polimerização, perdem entre 2% a 3% de todo o seu volume. Essa perda pode acarretar em alterações fortemente comprometedoras a nível micro e macroscópico. Objetivo: abordar a importância do uso de técnicas e manobras clínicas, que visam diminuir a contração de polimerização das resinas compostas, reduzindo seus efeitos na cavidade, para que se tenha um procedimento restaurador com elevado índice de sucesso clínico e boa aceitação pelos pacientes. Material e Métodos: foi realizada uma revisão da literatura por meio de uma busca bibliográfica nas seguintes bases de pesquisa online: PUBMED/MEDLINE, LILACS, BBO e SCIENCE DIRECT, através do rastreio de artigos relevantes publicados entre o período de 2000 a 2015. Resultados: comparando as formas de ativação dos compósitos, os compósitos fotopolimerizáveis possuem um menor escoamento e maior stress de contração se comparados a compósitos com ativação química, isso se dá devido à fotoativação que se destaca por ser uma reação rápida quando comparada a outros métodos, não dispondo de tempo para a resina se acomodar na cavidade e ter uma boa interação com o sistema adesivo previamente aplicado, levando a grande parte dos problemas clínicos das restaurações. Conclusão: questionamentos sobre os efeitos da contração de polimerização, ainda não foram completamente elucidados no meio científico, por isso algumas técnicas como a escolha de fotopolimerizadores a LED, manutenção da fase pré gel, manutenção do Fator C e técnica de inserção incremental, podem ser usadas para minimizar os efeitos dessa contração nas restaurações feitas com resina, afim de reduzir insucessos como, sensibilidade pós operatória, infiltração marginal e riscos de agressão pulpar levando a uma maior longevidade dos procedimentos restauradores com materiais resinosos. (AU)

Introduction: a complication inherent in all composite resins is the stress generated by the polymerization contraction. The present composite resins, after polymerization, lose between 2% and 3% of their entire volume. This loss can lead to strongly compromising micro and macroscopic changes. Objective: to address the importance of using technical and clinical maneuvers, which aim to reduce polymerization shrinkage of composite resins, reducing its effects in the cavity, in order to have a restorative procedure with high clinical success rate and good patient acceptance. Material and Methods: a review of the literature through a literature search in the following search online databases was performed: PubMed/MEDLINE, LILACS, BBO and SCIENCE DIRECT, through the screening of relevant articles published between 2000 to 2015. Results: comparing both activation of composites, the dental composites have a lower flow and higher stress of contraction compared to composites with chemical activation, this is the due to photoactivation that stands out for being a quick reaction when compared to other methods, not providing time for the resin to settle in well and have a good interaction with the previously applied adhesive system, leading to much of the clinical problems of restorations. Conclusion: questions about the effects of polymerization shrinkage have not been fully elucidated in the scientific community, so some techniques such as the choice of curing lights to LED, the pre gel phase maintenance, maintenance of Factor C and incremental insertion technique can It is used to minimize the effects of this contraction in restorations made with resin in order to reduce failures as post-operative sensitivity, microleakage and pulp assault risks leading to increased longevity of restorative procedures with resinous materials. (AU)

Bonding brackets on white spot lesions pretreated by means of two methods

Abstract Objective: The aim of this study was to evaluate the shear bond strength (SBS) of brackets bonded to demineralized enamel pretreated with low viscosity Icon Infiltrant resin (DMG) and glass ionomer cement (Clinpro XT Varnish, 3M Unitek) with and without aging. Methods: A total of 75 bovine enamel specimens were allocated into five groups (n = 15). Group 1 was the control group in which the enamel surface was not demineralized. In the other four groups, the surfaces were submitted to cariogenic challenge and white spot lesions were treated. Groups 2 and 3 were treated with Icon Infiltrant resin; Groups 4 and 5, with Clinpro XT Varnish. After treatment, Groups 3 and 5 were artificially aged. Brackets were bonded with Transbond XT adhesive system and SBS was evaluated by means of a universal testing machine. Statistical analysis was performed by one-way analysis of variance followed by Tukey post-hoc test. Results: All groups tested presented shear bond strengths similar to or higher than the control group. Specimens of Group 4 had significantly higher shear bond strength values (p < 0.05) than the others. Conclusion: Pretreatment of white spot lesions, with or without aging, did not decrease the SBS of brackets.

resumo Introdução: o objetivo do presente estudo foi avaliar a resistência ao cisalhamento de braquetes colados ao esmalte desmineralizado e pré-tratado com uma resina infiltrante de baixa viscosidade (Icon, DMG) ou com um selante ionomérico (Clinpro XT Varnish, 3M Unitek), com e sem envelhecimento. Métodos: setenta e cinco (75) amostras de esmalte bovino foram divididas em cinco grupos (n = 15). No Grupo 1 (controle), a superfície do esmalte não foi desmineralizada. Nos outros quatro grupos, as superfícies foram submetidas ao desafio cariogênico e as lesões de manchas brancas foram tratadas previamente à colagem de braquetes. Nos Grupos 2 e 3, as lesões foram tratadas com a resina Icon; nos Grupos 4 e 5, com o selante Clinpro XT Varnish. Após o tratamento, os Grupos 3 e 5 foram envelhecidos artificialmente. Os braquetes foram colados, sobre as lesões tratadas, utilizando-se o sistema adesivo Transbond XT, e a resistência ao cisalhamento foi avaliada em máquina universal de ensaios. A análise estatística foi realizada por meio da análise de variância e, posteriormente, pelo teste post-hoc de Turkey. Resultados: todos os grupos testados apresentaram resistência ao cisalhamento semelhante ou maior do que o grupo controle. As amostras do Grupo 4 apresentaram valores de resistência ao cisalhamento significativamente maiores (p < 0,05) do que as dos demais grupos. Conclusão: o tratamento das manchas brancas, com ou sem envelhecimento, não diminuiu a resistência ao cisalhamento dos braquetes.

Efeito da aplicação imediata e tardia de diferentes sistemas de acabamento/polimento sobre a rugosidade de superfície, microdureza e microinfiltração de uma resina composta à base de silorano / Effect of immediate and delayed application of different systems of finishing/polishing on the surface roughness, hardness and microleakage of composite resi-based silorane

O acabamento e polimento adequado das restuarações de resina composta são passos importantes na odontologia restauradora, que favorecem a estética, a saúde dos tecidos periodontais e a longevidade das restaurações. A hipótese testada neste estudo foi de similaridade entre os sistema de acabamento/polimento e do momento de sua aplicação sobre a rugosidade de superfície, microdureza e microinfiltração de uma resina de baixa contração à base de silorano. Os fatores em estudo neste experimento in vitroforam os sistemas de acabamento/polimento, em quatro níveis...

Resistência à fratura de dentes com restuarações MOD: efeito da matriz resinosa e do método de fotoativação / Fracture resistance of teeth with MOD restorations: effect of the resin matrix and the photoactivation methods

Objetivo: Avaliar o efeito de dois compósitos, de diferentes matrizes poliméricas, e da técnica defotoativação, sobre a resistência à fratura, por compressão, de pré-molares superiores com restaurações de classe II. Materiais e Métodos: Cavidades MOD foram preparadas em 56 pré-molares superiores, simulando tratamentos endodônticos. Os dentes foram divididos em quatro grupos (n=14): G1 - fotoativação convencional, restauração com Filtek Z350XT (3M ESPE) e adesivo Adper Single Bond 2 (3M ESPE); G2 - fotoativação pulso tardio, restauração Filtek Z350XT e adesivo Adper Single Bond2; G3 - fotoativação convencional, restauração Filtek P90 (3M ESPE) e adesivo próprio da Filtek P90 (3M ESPE); e G4 - fotoativação pulso tardio, restauração Filtek P90 e adesivo próprio da Filtek P90. No G1 e G3 (fotoativação convencional), a aplicação de compósito foi em incrementos de 2 mm, cada incremento fotoativado por 40 segundos, com aparelho LED, intensidadede 500 mW/cm2, aferida com radiômetro (Demetron). No G2 e G4 (fotoativação por pulso tardio) aplicação de compósito também foi com incrementos de 2mm, porém, cada incremento fotoativado, inicialmente durante 5s., com 300 mW/cm2. Após um período de 5 minutos foi realizada fotoativação, por 40s., intensidade de 500 mW/cm2. A fotoativação foi repetida para cada incremento. Após 24 horas, os espécimes foram polidose submetidos ao teste de compressão, com ponta ativa de formato cilíndrico/arredondado (Instron-0,5mm/min)...

Avaliação da atividade de osteogênica da DOX em uma matriz de compósito biodegradável de poli (e-caprolactona), poli (ácido lático-co-glicólico) e biocerâmica in vitro

Compósitos de polímeros biodegradáveis e biocerâmicas são uma alternativa na área de engenharia de tecidos para regeneração óssea, visto que combinam a bioatividade das biocerâmicas com a flexibilidade dos polímeros. A doxiciclina (DOX) é uma antibiótico de largo espectro, tem amplo uso como um auxiliar na terapia periodontal. DOX pode sofrer degradação sob oscilação do pH, calor e umidade, e efeitos tóxicos. Para superar estes problemas, sistemas de encapsulamento com B-ciclodextrina (BCD) permitem...

Avaliação da resistência de união de restaurações de compósito confeccionadas pela técnica direta ou indireta / Bond strength evaluation of direct and indirect composite restorations

The purpose of this study was to evaluate the bond strength of direct or indirect composite restorations to dentine. Thirty bovine teeth were flattened in order to obtain a plain dentine area. The teeth were divided in 3 groups of 10, according to the restoration fixing methods: 1) Direct technique using Single Bond Adhesive System; 2) Indirect technique using Rely-X resin cement; 3) Indirect technique using high viscosity Filtek Flow composite. For group 1, Z-250 composite discs were fixated (6mm diameter by 2 mm height) directly on the treated area. For groups 2 and 3, composite discs were made 24 hours before being cemented, with the same dimensions of group 1, and according to the Rely-X (group 2) and Filtek Flow (group 3) manufacturer's recommendations. After 24h of water storage, the speciments were submitted to a shear bond test on Instron at a speed of 0.5 mm/min. The data were submitted to ANOVA and Tukey's test (5 por cento)...

Estudo do conteúdo de partícula inorgânica de resinas compostas diretas e indiretas / Study of the direct and indirect composite resin's inorganic contents

O propósito deste estudo foi avaliar o conteúdo de partícula inorgânica em massa e volume de resinas compostas de aplicação direta e indireta. Para a avaliação das partículas inorgânicas foram confeccionados cinco corpos-de-prova cilíndricos, com 5x2mm para cada material. Foram ativados por 40 segundos e pesados em balança analítica (Sartorius) à seco e imersos em água destilada. Após a eliminação da matriz orgânica realizada em forno elétrico a 700ºC por 3 horas, foram pesados à seco e armazenados em água destilada, por 7 dias para nova pesagem em imersão. O conteúdo por massa foi baseado na aplicação do Princípio de Arquimedes...

Influência do prazo de validade de resinas compostas na resistência à compressão / The influence of the composite resins' expiration time on its compression resistance

O objetivo desse trabalho foi avaliar a influência do prazo de validade de resinas compostas na resistência à compressão. As resinas foram divididas em 6 grupos: G1 Esthet X (Dentsply/Caulk), G3 Charisma (Heraeus Kulzer), G5 Durafil VS (Heraeus Kulzer), com prazo de validade vencido e G2 Esthet X, G4 Charisma, G6 Durafil VS, dentro do prazo de validade...

Influência das técnicas de inserção de resina composta condensável sobre a infiltração marginal / Influence of insertion techniques of condensable composite resin on marginal leakage

O objetivo deste trabalho foi avaliar a influência da técnica de inserção da resina composta condensável sobre a microinfiltração marginal. Foram preparadas 120 cavidades classe II em dentes bovinos, com margem gengival em dentina/cemento, que foram divididas em quatro grupos: G1 - inserção única; G2 - inserção em incrementos horizontais; G3 - inserção em incrementos oblíquos; G4 - inserção mista em incrementos vestíbulo-linguais. Todas as cavidades foram restauradas utilizando o sistema adesivo Prime & Bond 2.1 (Dentsply) e a resina composta Surefil (Dentsply). Os dentes foram submetidos à termociclagem (5+/- 2 C e 55+/-2 C, durante 1000 ciclos) e, em seguida, imersos em solução aquosa de azul de metileno a 2 por cento pH 7, por 4 horas. A avaliação da microinfiltração marginal foi realizada por dois examinadores, segundo o critério de escores de 0 a 4. As médias de microinfiltração para cada grupo foram: G1 = 3,0; G2 = 3,3; G3 = 2,6; G4 = 3,3; e o teste Kruskal-Wallis demonstrou não haver diferença estatisticamente significante na microinfiltração entre as diferentes técnicas ao nível de significância de 5 por cento. Nenhuma das técnicas de inserção foi capaz de eliminar a microinfiltração e não diferiram entre si

Avaliaçäo in vitro da microinfiltraçäo marginal em restauraçöes indiretas com resina composta, em funçäo da localizaçäo das margens e dos agentes cimentantes / In vitro evaluation of marginal microleakage in inlay composite resin restorations in terms of marginal localization and luting agents

O objetivo deste trabalho foi analisar a microinfiltraçäo marginal nas paredes em esmalte e em dentina, de cavidades de classe V, restauradas com inlays de resinas composta e cimentadas com cimento do tipo dual e cimento híbrido de ionômero de vidro resinoso. Foram utilizados 40 dentes recém-extraídos, que receberam preparos padronizados e foram restaurados com inlays de resina composta e cimentados com Dual Cement, Cimento Resinoso Scotchbond MR, Enforce e Fuji Duet. Foi feita ciclagem térmica e os dentes foram colocados em soluçäo evidenciadora de Rodamina B a 0,2 por cento e depois seccionados. Foram utilizados os testes estatísticos de Kruskall-Wallis e Man-Whitney. Encontramos microinfiltraçäo em todos os sistemas cimentantes, e nas margens cervicais em dentina, a microinfiltraçäo foi significativamente maior que nas margens oclusais em esmalte

Aparelhos de fotopolimerizaçäo e o comportamento clínico das restauraçöes / Curing units equipments and the restorations clinical conduct

A resinas restauradoras fotopolimerizáveis permitiram uma revoluçäo na forma de restaurar os dentes, entretanto, a utilizaçäo de um aparelho de fotopolimerizaçäo, indispensável para o processo de "endurecimento" do material, trouxe outras preocupaçöes para o dia-a-dia do consultório. Realizamos uma coleta de dados junto a um grupo de Cirurgiöes Dentistas de origem heterogênea, onde foi possível perceber um certo descaso ou desconhecimento das variáveis envolvidas neste processo (técnica de polimerizaçäo, aparelho de polimerizaçäo e material utilizado). É objetivo deste artigo revisar a Literatura com respeito a essas variáveis, destacando o controle da intensidade de luz do aparelho como fator prepoderante dentro deste processo e demonstrar como estas variáveis podem afetar negativamente a performance clínica das restauraçöes realizadas com resinas compostas

Tratamento de perfuraçöes de furca materiais e selamento / Evaluation of the sealing ability of some materials used in furcation perforations

Vinte e quatro molares inferiores humanos extraídos e colhidos ao acaso foram perfurados na regiäo da furca e obturados com seis combinaçöes de materiais a saber: cimento de N-Rickert; cimento de N-Rickert servindo como base à resina composta fotopolimerizável; Cianocrilato de Etila (Super Bonder); resina composta fotopolimerizável isoladamente e finalmente o Hidróxido de Cálcio P.A. servido como base ao cimento de Ionômero de Vidro. Logo após as obturaçöes, os dentes foram imersos no corante azul de metileno por 36 horas sendo mantidos em estufa à 37 graus Celsius. Após desgaste longitudinal, a área de penetraçäo do corante foi calculada através do uso da computaçäo gráfica. Os resultados mostraram que o cimento de ionômero de vidro em conjunto com o Hidróxido de Cálcio exibiu as menores áreas de penetraçäo, sendo seguido pelo cimento de N-Rickert

In vitro caries inhibition by different restorative materials containing fluoride

O propósito deste estudo foi avaliar a capacidade de inibiçäo de cárie artificial do cimento de ionômero de vidro e adesivo/resina com e sem flúor: Confeccionaram-se 20 cavidades de Classe V por vestibular e lingual, com as paredes em esmalte e cemento, de dentes incisivos e caninos humanos recentemente extraídos. Os dentes foram divididos aleatoriamente em 4 grupos com 5 cavidades cada. Os grupos de dentes foram restaurados com 4 diferentes técnicas: I - Optibond foto + Herculite (Kerr); II - Optibond Dual + Herculite; III - Optibond Foto + Heliomolar (Vivadent) e IV - Vitremer (3M). Os materiais foram utilizados de acordo com as orientaçöes do fabricante. Após 48 horas da confecçäo da restauraçäo foram feitos o acabamento e o polimento. Os corpos-de-prova foram colocados em um recipiente contendo um gel de ácido láctico, pH 4,5. Os dentes foram estocados nessa soluçäo por 14 dias á temperatura ambiente. Após o período de estocagem, os dentes foram lavados, seccionados, preparados e analisados em microscopia óptica, sendo entäo fotografados com aumento final de 100x. As profundidades de desmineralizaçäo para os diferentes grupos (em milímetros) foram, em cemento e esmalte, respectivamente: G.I - 0,2650 (ñ0,0165) e 0,1880 (ñ0,0454); G.II - 0,2638 (ñ0,0172) e 0,1140 (ñ0,0395); G.III - 0,2530 (ñ0286) e 0,1060 (ñ0,0261); G.IV - 0,1600 (ñ0,0442) e 0,0130 (ñ0,0179). Os resultados foram submetidos a análise de variância (ANOVA) e teste Tukey, os quais possibilitaram concluir que: o cemento apresentou maior grau de desmineralizaçäo que o esmalte (p,01); os dentes restaurados com Vitremer apresentaram valores de desmineralizaçäo estatisticamente menores (p,01) tanto em esmalte quanto em cemento; os dentes restaurados com resina Heliomolar apresentaram desmineralizaçäo estatisticamente inferior que aquela da combinaçäo Optibond foto/Herculite (p< 0.01). No entanto, os materiais restauradores utilizados nos grupos I, II e III apresentaram desmineralizaçäo semelhante em cemento