Adaptación de cofias metálicas confeccionadas con dos técnicas: cera pérdida colado por centrifugación convencional e inducción / Adaptation of metallic copings made with two techniques: loss wax cast conventional centrifugation and induction

RESUMEN

Nuevas técnicas nos están permitiendo migrar de la técnica de cera perdida colado por centrifugado convencional (CPCC) a técnicas como la cera perdida colado por inducción (CPCI). Objetivos: Comparar la discrepancia marginal e interna de cofias unitarias de aleación Cobalto-Cromo (Co-Cr) sobre una línea de terminación chamfer, confeccionadas con dos técnicas: CPCC y CPCI, determinando cual técnica tuvo mejor adaptación marginal e interna. Material y Métodos: Se fabricaron13 cofias metálicas unitarias de aleación Co-Cr para cada técnica a evaluar. Se utilizó la réplica de silicona para evaluar las discrepancias marginales e internas, cada muestra fue seccionada en cruz en sentido vestíbulo-palatino y en sentido mesio-distal, luego con un estéreomicroscopio se evaluó la zona cervical, axial y oclusal. Resultados: Se evaluó los supuestos de normalidad con la prueba de Shapiro-Wilk. Los análisis estadísticos fueron la prueba t de Student y U Mann-Whitney. La CPCI obtuvo una menor discrepancia marginal e interna en comparación con la CPC pero no se encontró diferencias estadísticamente significativas (p>0,05) entre ambas técnicas. Conclusiones: Aunque en la mayoría de los puntos de evaluación las cofias realizadas mediante la CPCI presento mejores valores de adaptación marginal e interna en comparación con la CPCC estos resultados sólo son valores descriptivos que no fueron concluyentes, ya que en la mayoría de los puntos evaluados no existió diferencia estadísticamente significativa (p>0,05). Observamos que la mayoría de los valores de ambas técnicas se encuentran dentro del rango clínicamente aceptable.

ABSTRACT

New techniques are allowing us to migrate from the technique of lost wax cast by conventional centrifugation (CPCC) to techniques such as lost wax cast by induction (CPCI). Objectives: To compare the marginal and internal discrepancy of cobalt-chromium (Co-Cr) alloy unit copes on a chamfer termination line, made with two techniques: CPCC and CPCI, determining which technique had better marginal and internal adaptation. Material and Methods: 13 Co-Cr alloy unit copings were fabricated for each technique to be evaluated. Silicon replication was used to evaluate the marginal and internal discrepancies. Each sample was cross-sectioned in the vestibular-palatine and mesio-distal directions, then the cervical, axial and occlusal zones were evaluated with a stereomicroscope. Results: 13 unitary Co-Cr alloy metal cops were manufactured for each technique to be evaluated. The silicone replica was used to evaluate the marginal and internal discrepancies, each sample was cross-sectioned in the vestibulo-palatal direction and in the mesio-distal sense, then with a stereomicroscope, the cervical, axial and occlusal areas were evaluated. Conclusions: The assumptions of normality were evaluated with the Shapiro-Wilk test. The statistical analyzes were Student s t test and U Mann-Whitney test. The CPCI obtained a lower marginal and internal discrepancy compared to the CPC, but no statistically significant differences were found (p >0.05) between both techniques. Conclusions: Although in most of the evaluation points the copings made by the CPCI presented better values of marginal and internal adaptation compared to the CPCC, these results are only descriptive values that were not conclusive, since in most of the evaluated points there was no statistically significant difference (p >0.05). We observed that most of the values of both techniques are within the clinically acceptable range.