Síntese, caracterização e atividade antimicrobiana de nanofibras de policaprolactona - nistatina produzidas por eletrofiação / Synthesis, characterization and antimicrobial properties of nanofibers polycaprolactane - nystatin produced by electrospinning

RESUMO

O objetivo desse estudo foi sintetizar um scaffold de nanofibras (NFs) de Policaprolactona (PCL) com adição de nistatina (NYS), caracterizar e avaliar a atividade antimicrobiana. NFs foram sintetizadas pela técnica da eletrofiação, utilizando-se solução de PCL puro e PCL adicionado de NYS. Para a síntese das NFs de PCL, o polímero foi dissolvido em Dimetilformamida (DMF) e 1,1,2,2 Tetracloroetano (TCE), logo após foram adicionadas três concentrações de NYS (Grupos A, B e C). As amostras foram analisadas em Microscopia Eletrônica de Varredura (MEV), Espectroscopia por energia dispersiva (EDS), Análise de molhabilidade, Análise de Difratometria de Raios-X (DRX) e Espectroscopia de Infravermelho por Transformada de Fourier (FTIR). Após a análise em MEV foi realizada a média dos diâmetros das fibras com Software ImageJ. As atividades antimicrobianas foram avaliadas por meio dos testes de concentração inibitória mínima (CIM) e concentração microbicida mímica (CMM). As NFs de PCL com NYS (A) apresentaram diâmetro de 0,99µm ±0,29, o padrão do grupo B apresentou uma média de diâmetro de 1,3µm ±0,56 e o grupo C 1,24µm ±0,48. O DRX e o EDS comprovaram a presença de PCL e de NYS nas amostras. A CIM e a CMM comprovaram a ação fungicida e fungistática das NFs A, B e C(AU)

ABSTRACT

The aim of this study was to synthesize a scaffold of policaprolactane (PCL) nanofibers (NFs) with addition of nystatin (NYS), to characterize and evaluate the antimicrobial activity. NFs were synthesized by the electro-spinning technique, using pure PCL and NYS and PCL solutions. For the synthesis of PCL NFs, the polymer was dissolved in Dimethylformamide (DMF) and 1,1,2,2- Tetrachloroethane (TCE), after which three concentrations of NYS (Groups A, B and C) were added. The samples were analyzed in Scanning Electron Microscopy (SEM), Dispersive Energy Spectroscopy (EDS), Goniometer, X-ray Diffraction Analysis (XRD) and Fourier Transform Infrared Spectroscopy (FTIR). After SEM analysis, the mean fiber diameter was performed with ImageJ Software. The antimicrobial activities were evaluated through the tests of minimum inhibitory concentration (MIC) and minimum microbicidal concentration (MMC).The NFs of PCL with NYS (A) had a diameter of 0.99 µm ± 0.29, the standard of group B presented a mean diameter of 1.3 µm ± 0.56 and group C 1.24 µm ± 0.48. The DRX and the EDS verified the presence of PCL and NYS in the samples. CIM and CMM proved the fungicidal and fungistatic action of NFs A, B and C(AU)