Microshear bond strength of universal adhesives to enamel and dentin: an eighteen-month in vitro study / Resistência de união ao microcisalhamento de adesivos universais ao esmalte e dentina: estudo in vitro de dezoito meses

ABSTRACT

Objective: The aim of this study was to evaluate the microshear bond strength of Universal adhesives to enamel and dentin after one week and eighteen months of water storage. Material and Methods: Fragments from the buccal surfaces of 80 bovine teeth were prepared (12x5x1.0 mm) and ground to obtain flat surfaces of enamel and dentin. Samples were randomly assigned to 8 experimental groups (n=10), according to four adhesive systems (Adper Single Bond Plus/control ­ not a Universal adhesive/ASB; Ambar Universal/AUN; Prime&Bond Active/PBA and Scotchbond Universal/SBU) and two water-storage times (one week and eighteen months after sample preparations). Adhesives were applied according to the manufacturers' instructions and molds were positioned over bonded surfaces. A flowable composite was poured into the molds to fill up their internal diameter and obtain resin cylinder (1.0mm height/0.7mm internal diameter) after light-curing. Bond strength was determined using a testing machine (0.5 mm/min) and data were statistically analyzed by two-way analysis of variance (ANOVA) and the post-hoc Tukey's test (alpha=0.05). Failure patterns were analyzed for all resin cylinder tested. Results: For enamel, differences among adhesives were observed only at 18 months, in which SBU produced lower bond strength values (15.9±3.0 MPa) than the others universal adhesives (AUN 19.3±4.8 and PBA 21.4±2.1 MPa) (p<0.05). For dentin, there were differences among adhesives only at 7 days, with PBA showing the highest bond strength (37.4±4.9 MPa) and ASB the lowest one (19.4±3.9 MPa) (p<0.05). Enamel and dentin bond strength of all adhesives decreased significantly after 18 months and reduction percentage varied from 36.9 to 52.4 for enamel and from 35.1 to 62.8 for dentin. Adhesive and mixed failures showed high incidences. Conclusion: Results suggested that adhesives presented differences among them depending on type of hard dental tissue and evaluation time. Enamel and dentin bond strengths of control and all universal adhesives tested were not stable, decreasing at eighteen months. (AU)

RESUMO

Objetivo: O objetivo deste estudo foi avaliar a resistência de união ao microcisalhamento de adesivos universais ao esmalte e dentina após uma semana e dezoito meses de armazenamento em água. Material e Métodos: Fragmentos da superfície vestibular de 80 dentes bovinos foram preparados (12x5x1,0 mm) até o obtenção de superfícies planas de esmalte e dentina. As amostras foram distribuídas aleatoriamente em 8 grupos experimentais (n=10), de acordo com quatro sistemas adesivos (Adper Single Bond Plus / controle - não universal; Ambar Universal; Prime & Bond Active e Scotchbond Universal) e dois tempos de armazenamento em água (uma semana e dezoito meses após o preparo das amostras). Os adesivos foram aplicados de acordo com as instruções dos fabricantes e as matrizes foram posicionadas sobre as superfícies aderidas. Um compósito fluido foi aplicado nas matrizes para preencher seu diâmetro interno e obter o cilindro do compósito por fotopolimeração (1,0 mm de altura / 0,7 mm de diâmetro interno). A resistência de união foi determinada em uma máquina universal de ensaios (0,5mm/min). Os dados foram analisados estatisticamente pela análise de variância dois fatores (ANOVA) e teste de Tukey (alfa 0,05). Resultados: Para o esmalte, foram obtidas diferenças apenas aos 18 meses, em que Scotchbond Universal produziu menor média de resistência de união do que os demais adesivos universais. Para dentina, houve diferenças entre os adesivos apenas aos 7 dias, com o Prime & Bond Active apresentando a maior resistência de união e o Adper Single Bond Plus a menor. Os resultados sugeriram que os adesivos apresentaram diferenças entre si dependendo do substrato e do tempo de avaliação. Conclusão: As resistências de união em esmalte e dentina do controle e de todos os adesivos universais testados não foram estáveis, diminuindo aos dezoito meses (AU)