Anti-erosive profile of an experimental 5% SnCl₂ varnish containing different concentrations of NaF

ABSTRACT

Abstract This in vitro study evaluated the anti-erosive effect of an experimental varnish containing 5% stannous chloride (SnCl₂) associated with different concentrations of NaF (NaF-free, 2.5% NaF, or 5.2% NaF) on bovine enamel and root dentin. One hundred samples were pre-eroded (0.3% citric acid, pH 2.6, 10 min) and randomized into five groups (n=10 for each substrate) Negative control - milli-Q water; NaF-free - Experimental varnish SnCl₂-free and NaF-free; 2.5 NaF - Experimental varnish 5% SnCl₂ associated with 2.5% NaF; 5.2 NaF Experimental varnish 5% SnCl₂ associated with 5.2% NaF and positive control - Commercial varnish containing 5% NaF (Duraphat). After the varnishes were applied, the erosive and abrasive challenges were carried out for five days. Loss of tooth structure (TSL) was determined by optical profilometry, and the loss of calcium (ΔCa2+) using atomic absorption spectroscopy. Dentin analysis was also performed by SEM. A one-way ANOVA/Bonferroni test was performed to analyze the data (α=0.05). The experimental 2.5 NaF and 5.2 NaF groups showed greater effectiveness in preventing TSL when compared to the other groups (p <0.05), regardless of the substrate. In addition, these groups showed lower loss in Ca2+ content when compared to the other groups (p <0.05), for enamel and dentin. Dentin showed greater TSL and ΔCa2+ loss when compared to enamel in all treatments (p <0.05). The 5.2% and 2.5% NaF-containing experimental varnishes showed promising results in both, the prevention of TSL and the loss of Ca2+, regardless of the substrate studied.

RESUMO

Resumo Este estudo in vitro avaliou o efeito anti-erosivo de um verniz experimental contendo 5% de cloreto estanoso (SnCl₂) associado a diferentes concentrações de NaF (sem NaF, 2,5% NaF ou 5,2% NaF) sobre esmalte e dentina radicular bovinos. Cem amostras foram pré-erodidas (ácido cítrico 0,3%, pH 2,6, 10 min) e randomizadas em cinco grupos (n=10 para cada substrato) Controle negativo - água milli-Q; Sem NaF - Verniz experimental sem SnCl2 e sem NaF; 2,5 NaF - Verniz experimental 5% SnCl2 associado a 2,5% NaF; 5,2 NaF Verniz experimental 5% SnCl2 associado a 5,2% NaF e controle positivo - Verniz comercial contendo 5% NaF (Duraphat). Após a aplicação dos vernizes, os desafios erosivos e abrasivos foram realizados por cinco dias. A perda de estrutura dentária (PED) foi determinada por perfilometria óptica e a perda de cálcio (ΔCa2+) por espectroscopia de absorção atômica. A análise da dentina também foi realizada por MEV. Um teste ANOVA/Bonferroni de uma via foi realizado para analisar os dados (α=0,05). Os grupos experimentais 2,5 NaF e 5,2 NaF apresentaram maior eficácia na prevenção de PED quando comparados aos demais grupos (p<0,05), independentemente do substrato. Além disso, esses grupos apresentaram menor perda no teor de Ca2+ quando comparados aos demais grupos (p<0,05), para esmalte e dentina. A dentina apresentou maior PED e de ΔCa2+ quando comparada ao esmalte em todos os tratamentos (p<0,05). Os vernizes experimentais contendo NaF 5,2% e 2,5% apresentaram resultados promissores tanto na prevenção de PED quanto na perda de Ca2+, independente do substrato estudado.