Apical Sealing Efficacy of the Bioceramic Cements Bio Root and MTA Fillapex: An ex vivo Study

ABSTRACT

ABSTRACT The aim of this ex vivo study was to compare the ability of the apical sealing bioceramic cements BioRoot™ RCS (Septodont) and MTA-Fillapex (Angelus). One hundred and eighty-four vestibular canals were selected from ninety-two recently extracted maxillary molars. Canals were instrumented with the mechanized system ProTaper Next and obturated using the single cone technique. The sample was randomly divided into two groups (92) Group 1 was obturated with BioRoot ™ RCS, and Group 2 with MTA-Fillapex. Samples were processed for the leakage test by dye penetration and later cut longitudinally. The data obtained were tabulated and analyzed using Stata 15.0. The degree of leakage from BioRoot ™ RCS was 0.03 mm, and MTA-Fillapex was 0.31 mm p (0.00). BioRoot ™ bioceramic presented an adequate apical sealing, while MTA-Fillapex showed an accentuated leakage.

RESUMEN

RESUMEN El objetivo de este studio ex vivo fue comparar la capacidad de sellado apical de dos cementos biocerámicos, el BioRoot™ RCS (Septodont) y MTA-Fillapex (Angelus). 184 conductos vestibulares fueron seleccionados de 92 molares maxilares recientemente extraídos. Los conductos fueron instrumentados con el sistema de instrumentación mecanizado Protaper Next y obturados usando la técnica de cono único. Las muestras fueron divididas aleatoriamente en dos grupos (N 92) Grupo 1 fue obturado con BioRoot™ RCS, y el grupo 2 con MTA-Fillapex. Las muestras fueron procesadas para el test de filtración por penetración de tinción, y luego cortadas de manera longitudinal. Los datos obtenidos fueron tabulados y analizados usando Stata 15.0. El grado de penetración de BioRoot™ RCS fue de 0,03 mm, y de MTA Fillapex fue de 0,31 mm (P 0.00). BioRoot™ RCSpresent un sellado apical adecuado, mientras que MTA Fillapex mostró una filtración mayor.