Effect of surrounded shade and specimen`s thickness on color adjustment potential of a single-shade composite

ABSTRACT

Abstract This study evaluated the effect of surrounded shade and specimens` thickness on the color adjustment potential (CAP) of a single-shade composite. The composite Vittra APS Unique was surrounded (dual specimens) or not (simple specimens) by a control composite (shade A1, A2, or A3). Simple specimens of the control composite were also confectioned. Opacity and whiteness index for dentistry (WID) were calculated for simple specimens. Color differences between the simple (ΔE*SIMPLE)/ dual specimens (ΔE*DUAL) and the controls were calculated. CAP was calculated based on the ratio between ΔE* SIMPLE and ΔE* DUAL. The tested composite presented lower opacity (53 to 62% vs. 80 to 93%) and higher WID (≈ 42 vs. 18 to 32) than controls. Irrespective of the specimens' thickness (1.0/ 1.5 mm), the lowest values of ΔE* SIMPLE (11.1/ 10.8) and ΔE*DUAL (7.2/ 6.1) were observed using the surrounding shade A1. The shade A3 yielded higher ΔE*SIMPLE (16.4/ 17.1) and ΔE* DUAL (11.3/ 12.3) than the A2 (ΔE*SIMPLE = 13.4/ 14.6; and ΔE* DUAL = 9.7/ 10.3). The specimen`s thickness significantly affected the CAP (0.35 and 0.44 for 1.0 and 1.5 mm, respectively) only for shade A1, which had the highest CAP values. The shade A3 resulted in higher CAP values (0.31) than A2 (0.27) when 1.0-mm thick specimens were used, but similar values were observed for 1.5 thick specimens (≈ 0.29). In conclusion, both surrounding shade and specimen thickness can affect the CAP of a single-shade resin composite.

RESUMO

Resumo Este estudo avaliou o efeito da cor circundante e da espessura da amostra no potencial de ajuste de cor (PAC) de uma resina monocromática. O compósito Vittra APS Unique foi circundado (amostras duplas) ou não (amostras simples) com um compósito controle (cor A1, A2 ou A3). Amostras simples do compósito controle também foram confeccionadas. A opacidade e o índice de brancura para odontologia (IBO) foram calculados para as amostras simples. As diferenças de cor entre amostras simples (ΔE*SIMPLE) / duplas (ΔE*DUAL) e os controles foram calculados. PAC foi calculado baseado na razão entre ΔE* SIMPLE e ΔE* DUAL. O compósito testado apresentou menor opacidade (53 a 62% vs. 80 a 93%) e maior IBO (≈ 42 vs. 18 a 32) que os controles. Independente da espessura da amostra (1,0/ 1,5 mm), os valores mais baixos de ΔE* SIMPLE (11,1/ 10,8) e ΔE*DUAL (7,2/ 6,1) foram observadas quando a resina circundante era A1. A cor A3 resultou em maior ΔE*SIMPLE (16,4/ 17,1) e ΔE* DUAL (11,3/ 12,3) do que A2 (ΔE*SIMPLE = 13,4/ 14,6; e ΔE* DUAL = 9,7/ 10,3). A espessura das amostras afetou significativamente o PAC (0,35 e 0,44 para 1,0 e 1,5 mm, respectivamente) apenas para a cor A1, que teve os maiores valores de PAC. A cor A3 resultou nos maiores valores de PAC (0,31) que A2 (0,27) quando amostras de 1,0 mm de espessura foram usadas, mas valores similares foram observados para amostras de 1,5 mm (≈ 0,29). Como conclusão, tanto a cor circundante como a espessura das amostras podem afetar o PAC de um compósito resinoso monocromático.