Estudio Histomorfométrico de la regeneración ósea utilizando sulfato de calcio bifásico combinado con alendronato en conejos / Estudo Histomorfométrico da regeneração óssea utilizando sulfato de cálcio bifásico combinado com alendronato em coelhos / Histomorfometric Study of the bone regeneration using bifasic calcium sulfate combined with alendronate in rabbits

RESUMEN

El alendronato es un bifosfonato con un amplio espectro de indicaciones cuya principal capacidad es la inhibición de la función osteoclástica. El sulfato de calcio bifásico es un injerto aloplástico que posee las ventajas del sulfato del calcio simple como biocompatibilidad, propiedades osteoconductivas y de bioreabsorción. Objetivo: Determinar la eficacia de la regeneración ósea a través de un estudio histomorfométrico utilizando sulfato de calcio bifásico sólo y combinado con Alendronato. Materiales y métodos: Se utilizaron 24 fémures de conejos machos andinos entre 1,5 a 2,5 Kg, divididos en 3 grupos G1 Regeneración ósea fisiológica, G2 Sulfato de calcio bifásico y G3 Sulfato de calcio bifásico combinado con alendronato. Se realizó una incisión de 2,5cm para crear defectos de 5mm de diámetro con una profundidad de 1.5 mm. Todos los animales fueron sacrificados a la sexta semana y se obtuvieron cortes histomorfométricos. Fueron utilizados los test estadísticos de ANOVA y Tukey con un nivel de significancia del 5%. Resultados: La regeneración ósea fue del 10.63%, 40% y 71.88% para G1, G2 y G3 respectivamente. Se encontró diferencia estadísticamente significativa entre los grupos (p<0,001). Se observó diferencia entre G1 y G3 (p<0,001), así como entre el G2 y G3 (p=0,05), siendo los mejores resultados encontrados para el G3. Conclusión: El sulfato de calcio bifásico combinado con alendronato mostró mejor regeneración ósea al compararlo con los grupos de regeneración fisiológica y sulfato de calcio en conejos.

ABSTRACT

Alendronate is a bisphosphonate with a broad spectrum of indications whose main capacity is the inhibition of osteoclastic function. Biphasic calcium sulfate is an alloplastic graft that possesses the advantages of simple calcium sulfate as biocompatibility, osteoconductive and bioreabsorption properties. Objective: To determine the efficacy of bone regeneration through a histomorphometric study using biphasic calcium sulfate alone and combined with Alendronate. Materials and methods: 24 femurs of Andean male rabbits were used between 1.5 and 2.5 Kg, divided into 3 groups G1 Physiological bone regeneration, G2 Biphasic calcium sulphate and G3 Biphasic calcium sulphate combined with alendronate. An incision of 2.5 cm was made to create defects of 5 mm in diameter with a depth of 1.5 mm. All the animals were sacrificed at the sixth week and histomorphometriccuts were obtained. The statistical tests of ANOVA and Tukey with a level of significance of 5% were used. Results: Bone regeneration was observed in 10.63%, 40% and 71.88% for G1, G2 and G3 respectively. A statistically significant difference was found between the groups (p <0.001). A difference was observed between G1 and G3 (p <0.001), as well as between G2 and G3 (p = 0.05), being the best results found for the G3. Conclusion: Biphasic calcium sulphate combined with Alendronate showed better bone regeneration when compared to physiological regeneration and calcium sulfate groups in rabbits.

RESUMO

O alendronato é um bisfosfonato com amplo espectro de indicações cuja principal capacidade é a inibição da função osteoclástica. O sulfato de cálcio bifásico é um enxerto aloplástico que possui as vantagens do sulfato de cálcio simples como biocompatibilidade, osteocondutor e biorreabsorção. Objetivo: Determinar a eficácia da regeneração óssea através de estudo histomorfométrico utilizando sulfato de cálcio bifásico isolado e associado ao alendronato. Materiais e métodos: Foram utilizados 24 fémures de coelhos machos andinos entre 1,5 e 2,5 kg, divididos em três grupos G1 Regeneração óssea fisiológica, G2 Sulfato de cálciobifásico e G3 Sulfato de cálcio bifásico combinado com alendronato. Uma incisão de 2,5 cm foi feita para criar defeitos de 5 mm de diâmetro com uma profundidade de 1,5 mm. Todos os animais foram sacrificados na sexta semana e foram obtidos cortes histomorfométricos. Os testes estatísticos de ANOVA e Tukey com nível de significância de 5% foram utilizados. Resultados: Regeneração óssea foi observada em 10,63%, 40% e 71,88% para G1, G2 e G3 respectivamente. Foi encontrada diferença estatisticamente significante entre os grupos (p <0,001). Observou-se diferença entre G1 e G3 (p <0,001), assim como entre G2 e G3 (p = 0,05), sendo os melhores resultados encontrados para o G3. Conclusão: O sulfato de cálcio bifásico associado ao alendronato apresentou melhor regeneração óssea quando comparado aos grupos regeneração fisiológica e sulfato de cálcio em coelhos.