Long-term bond strength of adhesive systems applied to etched and deproteinized dentin
J. appl. oral sci
;
15(6): 475-479, Nov.-Dec. 2007. tab
Article
in English
| LILACS
| ID: lil-471102
ABSTRACT
The aim of this study was to evaluate the early and 12-month bond strength of two adhesive systems (Single Bond-SB and One Step-OS) applied to demineralized dentin (WH) and demineralized/NaOCl-treated dentin (H). Twenty flat dentin surfaces were exposed, etched, rinsed and slightly dried. For the H groups, a solution of 10 percent NaOCl was applied for 60 s, rinsed (15 s) and slightly dried. The adhesives were applied according to the manufacturer's instructions and composite resin crowns were incrementally constructed. After 24 h (water-37ºC), the specimens was sectioned in order to obtain resin-dentin sticks (0.8 mm²). The specimens were tested in microtensile (0.5 mm/min) immediately (IM) or after 12 months of water storage (12M). The data (MPa) were subjected to ANOVA and Tukey's test (a=0.05). Only the main factors adhesive and time were significant (p=0.004 and p=0.003, respectively). SB (42.3±9.1) showed higher bond strengths than OS (33.6±11.6). The mean bond strength for IM-group (42.5±8.7) was statistically superior to 12M (33.3±11.8). The use of 10 percent NaOCl, after acid etching, did not improve the immediate and the long-term resin-dentin bond strength.
Full text:
Available
Index:
LILACS (Americas)
Language:
English
Journal:
J. appl. oral sci
Journal subject:
Dentistry
Year:
2007
Type:
Article
/
Project document
Affiliation country:
Brazil
Institution/Affiliation country:
University of Oeste Santa Catarina/BR
/
University of São Paulo/BR
Similar
MEDLINE
...
LILACS
LIS