Influência da ciclagem térmica na resistência à flexão de resinas laboratoriais / The effect of thermo-cycling on flexural strength of laboratorial resins
Rev. odonto ciênc
;
22(58): 364-370, out.-dez. 2007. ilus, tab, graf
Article
in Portuguese
| LILACS
| ID: lil-487219
RESUMO
Introdução:
Uma nova geração de resinas laboratoriais contendo micro-partículas cerâmicas em sua composição tem sido introduzida no mercado com a finalidade de melhorar suas propriedades mecânicas.Objetivo:
O objetivo deste estudo foi avaliar o efeito da termociclagem na resistência à flexão de três resinas laboratoriais. Materiais emétodo:
Foram confeccionadas 48 barras com medidas de 2 mm × 2 mm × 25 mm, utilizando as resinas laboratoriais G1 - RESILAB MASTER (Wilcos, Brasil), G2 - VITA VM LC (Vita Zanhfabrik, Germany), G3 - VITA ZETA LC (Vita Zanhfabrik, Germany). A metade das barras de cada grupo foi submetida a 3000 ciclos térmicos (5ºC/55ºC ± 1, com banhos de 30 s). Os ensaios mecânicos foram efetuados em máquina de ensaio universal EMIC com capacidade de carga de 100 kg e velocidade de 0,5 mm/min.Resultados:
Os dados obtidos foram analisados estatisticamente pelo teste de ANOVA (two-way) e Tukey (p < 0,05). As médias (± DP) observadas para os grupos sem ciclagem foram G1(112,6 ± 25,39), G2(116,5 ± 18,51) e G3(136,1 ± 24,34); e para os grupos com ciclagem G1(91,8 ± 18,86), G2(101,9 ± 20,61) e G3(89,9 ± 23,05).Conclusão:
Concluiu-se que a diminuição da resistência à flexão em MPa está diretamente dependente da ciclagem térmica nos grupos testados, sendo que os maiores valores foram obtidos pela resina VITA VM LC. Entretanto, na condição sem ciclagem térmica a VITA ZETA apresentou os maiores valores.ABSTRACT
Introduction:
A new laboratorial resin generation that content ceramic microparticles in its composition has been introduced in the market with the purpose to improve its mechanical properties.Objective:
The objective of this study was to evaluate the effect of the thermocycling in the flexural strength of three laboratorial resins.Method:
Forty-eight specimens with measures of 2 mm × 2 mm × 25 mm were made using laboratorial resins G1 - RESILAB MASTER (Wilcos, Brazil), G2 - VITA VM LC (Vita Zanhfabrik, Germany) and G3 - VITA ZETA (Vita Zanhfabrik, Germany). After their confection, half of each group was submitted to 3000 thermal-cycles (5ºC/55ºC ± 1, with rinse bath of 30 s). The mechanical essays were done in Universal essay machine EMIC with the loading capacity of 100 kg and the equispeed of 0,5 mm/min.Results:
The obtained data was analyzed statistically by the ANOVA test (two-way) and Turkey?s test (p < 0,05). The averages (± DP) observed for the groups without cycles were G1(112,6 ± 25,39), G2(116,5 ± 18,51) and G3(136,1 ± 24,34); and for the groups with cycles G1(91,8 ± 18,86), G2(101,9 ± 20,61) and G3 89,9 ± 23,05).Conclusion:
It was concluded that the decrease in the flexural strength in MPa is directly dependent on the thermo-cycling in the tested groups, being that the highest values were obtained by VM LC resin. However, in the group without thermo-cycling the VITA ZETA showed the highest values.UNITERMS three point bending; thermo-cycling; composite resin.
Full text:
Available
Index:
LILACS (Americas)
Main subject:
Tensile Strength
/
Thermic Treatment
/
Composite Resins
Type of study:
Evaluation studies
Language:
Portuguese
Journal:
Rev. odonto ciênc
Journal subject:
Dentistry
Year:
2007
Type:
Article
Affiliation country:
Brazil
Institution/Affiliation country:
UNESP/BR
Similar
MEDLINE
...
LILACS
LIS