Avaliação do torque de inserção, remoção e fratura de mini-implantes ortodônticos em cortical óssea / Evaluation of insertion, removal and fracture torques of orthodontic mini-implants

RESUMO

O objetivo deste trabalho foi avaliar em mini-implantes da empresa SIN - Sistema de implantes, de comprimentos diferentes para os seguintes fatores (a) torque de inserção, (b) torque de remoção, (c) torque de fratura, (d) tensão cisalhante, (e) tensão normal e (f) tipo de fratura. Foram utilizados 10 mini-implantes autoperfurantes da marca SIN, com 1,6 mm de diâmetro e com 8 mm de parte ativa. Destes 10 mini-implantes, 5 não possuíam perfil transmucoso e 5 tinham perfil de 2mm, formando 2 grupos SIN sem perfil (SSP), SIN com perfil (SCP). Todos os mini-implantes foram inseridos em cortical óssea e removidos com micromotor acoplado a um torquímetro. Os mini-implantes foram também submetidos ao ensaio de fratura. Os torques de inserção, remoção e fratura, assim como a tensão cisalhante e normal calculadas foram comparados entre todos os grupos pela ANOVA. O tipo de fratura foi avaliado em microscópio eletrônico de varredura. Não houve diferença entre os grupos para os torques avaliados e todos os mini-implantes sofreram fratura do tipo dúctil.

ABSTRACT

The purpose of this study was to evaluate mini-implants manufactured by SIN with different lengths for the following factors (a) insertion torque, (b) removal torque, (c) fracture torque, (d) shear tension, (e) normal tension and (f) type of fracture. Ten self-drilling mini-implants were used from SIN, with 1.6 mm in diameter and with 8 mm in length of active part. Out of these 10 mini-implants, 5 did not have a neck and the other 5 had a 2 mm neck, and were separated into 2 groups SIN without neck (SSP), SIN with neck (SCP). All mini-implants were inserted in bone cortex and removed with a low speed handpiece connected to a digital torquimeter. The mini-implants were also submitted to a fracture test. The insertion, removal and fracture torques, as well as the calculated shear and normal tensions were compared between all groups by ANOVA. The type of fracture was assessed by a scanning electronic microscope. There were no significant differences between groups for all evaluated torques and all mini-implants suffered ductile fracture.