Evaluation of fracture strength and translucency of 3D printing resin crown for carious primary anterior tooth / 대한구강보건학회지

ABSTRACT

Objectives@#The purpose of this study was to compare the fracture strength and traslucency of 3D printing resin crowns according to different thicknesses. @*Methods@#Resin crowns were designed with CAD software and a 3D scanner, using scanned data of the #61 tooth model. Resin Crowns with different thicknesses were printed using a 3D printer, and subsequently divided into four groups according to thickness (0.3, 0.5, 0.7, and 1.0 mm). Fracture strength was compared among groups with a resin strip crown of 1.0 mm thickness. Compressive force was applied using a universal testing machine at 30° along the lingual surface at 1 mm/min cross head speed. For translucency evaluation, thin square specimens were printed of thicknesses 0.3, 0.5, 0.7, and 1.0 mm, and translucency was measured using a spectrophotometer. @*Results@#As a result of fracture strength measurement, fracture strength increased as thickness increased, and a significant difference was observed solely between thicknesses of 0.3 and 0.5 mm, and the thicknesses of 0.3 and 0.5 mm (P<0.05). Translucency decreased as thickness increased, and similarly, a significant difference was observed only between thicknesses of 0.3 and 0.5 mm and the thicknesses of 0.7 and 1.0 mm (P<0.05). @*Conclusions@#A 3D printing resin crown can be used as a clinical option for restoring a primary anterior tooth affected by caries.