Reconstruction of rat calvarial defects utilizing an ultraviolet-cured hydrogel loaded with bone marrow mesenchymal stem cells / 口腔疾病防治

ABSTRACT

Objective@#To investigate the osteogenic properties of a methacrylated gelatin (GelMA) / bone marrow mesenchymal stem cells (BMSCs) composite hydrogel applied to the skull defect area of rats and to provide an experimental basis for the development of bone regeneration biomaterials.@*Methods@#This study was approved by the Animal Ethics Committee of Nanjing University. A novel photocurable composite biohydrogel was developed by constructing photoinitiators [lthium phenyl (2,4,6-trimethylbenzoyl) phosphinate, LAP], GelMA, and BMSCs. The surface morphology and elemental composition of the gel were examined using scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX). The compressive strength of the gel was evaluated using an electronic universal testing machine. After in vitro culture for 1, 2, and 5 days, the proliferation of the BMSCs in the hydrogels was assessed using a CCK-8 assay, and their survival and morphology were examined through confocal microscopy. A 5 mm critical bone deficiency model was generated in a rat skull. The group receiving composite hydrogel treatment was referred to as the GelMA/BMSCs group, whereas the untreated group served as the control group. At the 4th and 8th weeks, micro-CT scans were taken to measure the bone defect area and new bone index, while at the 8th week, skull samples from the defect area were subjected to H&E staining, van Gieson staining, and Goldner staining to evaluate the quality of bone regeneration and new bone formation.@*Results@#SEM observed that the solidified GelMA showed a 3D spongy gel network with uniform morphology, the porosity of GelMA was 73.41% and the pore size of GelMA was (28.75 ± 7.13) μm. EDX results showed that C and O were evenly distributed in the network macroporous structure of hydrogel. The hydrogel compression strength was 152 kPa. On the 5th day of GelMA/BMSCs culture, the cellular morphology transitioned from oval to spindle shaped under microscopic observation, accompanied by a significant increase in cell proliferation (159.4%, as determined by the CCK-8 assay). At 4 weeks after surgery, a 3D reconstructed micro-CT image revealed a minimal reduction in bone defect size within the control group and abundant new bone formation in the GelMA/BMSCs group. At 8 weeks after surgery, no significant changes were observed in the control group's bone defect area, with only limited evidence of new bone growth; however, substantial healing of skull defects was evident in the GelMA/BMSCs group. Quantitative analysis at both the 4- and 8-week examinations indicated significant improvements in the new bone volume (BV), new bone volume/total bone volume (BV/TV), bone surface (BS), and bone surface/total bone volume (BS/TV) in the GelMA/BMSCs group compared to those in the control group (P<0.05). Histological staining showed continuous and dense formation of bone tissue within the defects in the GelMA/BMSCs group and only sporadic formation of new bone, primarily consisting of fibrous connective tissue, at the defect edge in the control group.@*Conclusion@#Photocuring hydrogel-based stem cell therapy exhibits favorable biosafety profiles and has potential for clinical application by inducing new bone formation and promoting maturation within rat skull defects.