The effect of NaOCl treatment and sterilization procedures on the corrosion of endodontic files / 대한치과보존학회지

ABSTRACT

A variety files made of stainless steel (S-S) or nickel-titanium (Ni-Ti) are used during endodontic treatment. The purpose of this study was to evaluate the corrosion susceptibility of S-S and Ni-Ti endodontic files. Three brands of files were used for this study K-flex(R) S-S files (Maillefer, USA), Profile(R) Ni-Ti files (Maillefer, USA), K-3(R) Ni-Ti files (SybronEndo, USA). 120 files of each brands (21mm, ISO size #20) were divided into 12 groups according to 1) sterilization methods using Autoclave or Ethylene Oxide (E-O) gas, 2) Irrigation solutions using 5.25 % NaOCl or Saline, 3) the number of sterilization (1, 5, 10 times). After above procedures, each of the files was inspected by three examiners with a light microscope and camera at X25. Each file was judged and ranked according to the following criteria 0; no corrosion, 1; mild corrosion, 2; moderate corrosion, and 3; severe corrosion. The files of high score were examined under the Scanning Electron Microscope. Data were statistically analyzed with the Kruskal-Wallis test (p < 0.05). Most of the ten time-autoclaved files had showed mild to moderate corrosion. But, one or five time-autoclaved files did not show corrosive surface. NaOCl treatment and E-O gas sterilization did not influence on corrosion. There was a significant difference in corrosion susceptibility between sterilization methods and the number of autoclaving. However, there was no significant difference between brands and file materials.