Influence of zirconia content on translucency of zirconia-toughened alumina glass-infiltrated ceramic / 华西口腔医学杂志

ABSTRACT

<p><b>OBJECTIVE</b>The objective of this study is to investigate the influence of zirconia content which is 0-30.0% weight percentage of matrix on translucency of zirconia-toughened alumina glass-infiltrated ceramics.</p><p><b>METHODS</b>Seven groups were divided according to different weight percentage of zirconia (0, 2.5%, 5.0%, 7.5%, 10.0%, 20.0% and 30.0%). After sintering, infiltrating and polishing, spectral transmittance was determined with spectrophotometer under D65 standard source. Contrast ratio was also tested by whiteness colorimeter.</p><p><b>RESULTS</b>With mass fraction of zirconia increasing from 0 to 30.0%, spectral transmittance reduced from 0.406% to 0.058%, while contrast ratio value increased from 0.849 +/- 0.005 to 1.015 +/- 0.006. When zirconia content was 10.0%, contrast ratio was 0.990 +/- 0.008. When it was more than 10.0%, transmission rate of the downward trend and contrast ratio of the rising trend became flat.</p><p><b>CONCLUSION</b>Zirconia content has a direct impact on translucency of zirconia-toughened alumina glass-infiltrated ceramic, which is essentially opaque when zirconia content is 10.0%. When mass fraction of zirconia is more than 10.0%, the influence of zirconia content is reduced.</p>