Comparison of surface roughness of nanofilled and microhybrid composite resins after curing and polishing / 南方医科大学学报
Journal of Southern Medical University
;
(12): 727-730, 2014.
Article
in Chinese
| WPRIM
| ID: wpr-249371
ABSTRACT
<p><b>OBJECTIVE</b>To compare the surface roughness of nanofilled dental composite resin and microhybrid composite resins after curing and polishing.</p><p><b>METHODS</b>A nanofilled composite (Z350) and 4 microhybrid composites (P60, Z250, Spectrum, and AP-X) were fabricated from the lateral to the medial layers to prepare 8 mm×8 mm×5 mm cubical specimens. The 4 lateral surfaces of each specimens were polished with abrasive disks (Super-Snap). Profilometer was used to test the mean surface roughness (Ra) after polishing.</p><p><b>RESULTS</b>P60 had the lowest Ra (0.125∓0.030 µm) followed by Z250 and Spectrum. The Ra of Z350 (0.205∓0.052 µm) was greater than that of the other 3 resins, and AP-X had the roughest surfaces. Under scanning electron microscope, the polished faces of P60 resin were characterized by minor, evenly distributed particles with fewer scratches; the polished faces of Z350 presented with scratches where defects of the filling material could be seen.</p><p><b>CONCLUSION</b>The nanofilled composite Z350 has smooth surface after polishing by abrasive disks, but its smoothness remains inferior to that of other micro-hybrid composite resins.</p>
Full text:
Available
Index:
WPRIM (Western Pacific)
Main subject:
Polyurethanes
/
Surface Properties
/
Acrylic Resins
/
Materials Testing
/
Composite Resins
/
Dental Materials
/
Dental Polishing
Language:
Chinese
Journal:
Journal of Southern Medical University
Year:
2014
Type:
Article
Similar
MEDLINE
...
LILACS
LIS