Influence on microstructure of dental zirconia ceramics prepared by two-step sintering / 华西口腔医学杂志
West China Journal of Stomatology
;
(6): 496-499, 2013.
Article
in Chinese
| WPRIM
| ID: wpr-315925
ABSTRACT
<p><b>OBJECTIVE</b>To investigate the microstructure of dental zirconia ceramics prepared by two-step sintering.</p><p><b>METHODS</b>Nanostructured zirconia powder was dry compacted, cold isostatic pressed, and pre-sintered. The pre-sintered discs were cut processed into samples. Conventional sintering, single-step sintering, and two-step sintering were carried out, and density and grain size of the samples were measured. Afterward, T1 and/or T2 of two-step sintering ranges were measured. Effects on microstructure of different routes, which consisted of two-step sintering and conventional sintering were discussed. The influence of T1 and/or T2 on density and grain size were analyzed as well.</p><p><b>RESULTS</b>The range of T1 was between 1450 degrees C and 1550 degrees C, and the range of T2 was between 1250 degrees C and 1350 degrees C. Compared with conventional sintering, finer microstructure of higher density and smaller grain could be obtained by two-step sintering. Grain growth was dependent on T1, whereas density was not much related with T1. However, density was dependent on T2, and grain size was minimally influenced.</p><p><b>CONCLUSION</b>Two-step sintering could ensure a sintering body with high density and small grain, which is good for optimizing the microstructure of dental zirconia ceramics.</p>
Full text:
Available
Index:
WPRIM (Western Pacific)
Main subject:
Zirconium
/
Ceramics
Language:
Chinese
Journal:
West China Journal of Stomatology
Year:
2013
Type:
Article
Similar
MEDLINE
...
LILACS
LIS