Effects of electrolyte's concentration at micro-arc oxide treatment on the bonding strength of titanium to porcelain / 实用口腔医学杂志
Journal of Practical Stomatology
;
(6): 833-837, 2009.
Article
in Chinese
| WPRIM
| ID: wpr-405668
ABSTRACT
Objective; To evaluate the influence of electrolyte's concentration at micro-arc oxide treatment on the bonding strength of titanium to porcelain. Methods; CP titanium specimens with size of 25 mm ×3 mm ×0. 5 mm were treated with micro-arc oxidation (MAO) in Na_2SiO_3 solution of three different concentrations. After ultra-low-fusing porcelain was applied, a three-point-flexure-test was used to evaluate the bonding strength of titanium to porcelain. The surface of the specimens was observed by SEM and EDS, as well as the interface between titanium and porcelain. Results; The bonding strength values between titanium treated with MAO and porcelain was significantly higher then the control groups, Croup 20 g/L has the highest bonding strength values. SEM/EDS suggested that a porous thin layer of oxide which contains Si element is created by MAO, and higher concentration of Na_2SiO_3 leads to more Si element in oxide. Conclusion; MAO treating can improve the bonding strength between titanium and ceramic. Electrolyte's concentration has an effect on the bond strength between titanium and porcelain.
Full text:
Available
Index:
WPRIM (Western Pacific)
Language:
Chinese
Journal:
Journal of Practical Stomatology
Year:
2009
Type:
Article
Similar
MEDLINE
...
LILACS
LIS