Fibrin glue,a three-dimensional scaffold for rabbit bone marrow stromal cells cultured in vitro / 中国组织工程研究

ABSTRACT

BACKGROUND: In tissue engineering, three-dimensional biodegradable scaffolds are generally used as a basic structure for cell anchorage, proliferation. Currently, no perfect scaffold is available. OBJECTIVE: To observe the growth of rabbit bone marrow stromal cells (BMSCs) cultured in different-intensity three-dimensional fibrin glue in vitro, and to discuss the feasibility of fibrin glue used as a scaffold material of bone tissue engineering. DESIGN, TIME AND SETTING: The single sample observational study was performed at the China-Japan Union Hospital of Jilin University and School of Mechanical Engineering of Tianjin University of Technology from September 2007 to January 2008. MATERIALS Fibrinogen and thrombin were mixed at various proportions, and prepared into different intensity fibrin glue. A month-old male New Zealand white rabbits, weighing 0.25 kg was used in this study. METHODS: Rabbit BMSCs were cultured and serial subcultivation in a CO2 incubator. And then the amplified BMSCs were collected and continue to be cultured in different intensity fibrin glue for 4 weeks. MAIN OUTCOME MEASURES：Observation of growing BMSCs is performed using the phase contrast microscope. The activity of BMSCs in fibrin glue at different stages was observed using hematoxylin-eosin staining. The ultrastructural changes of BMSCs were observed which had been cultivated in fibrin glue for 4 weeks. RESULTS: After growing in fibrin glue for 4 weeks, BMSCs showed strongly active status in low intensity fibrin glue and growing slowly or dying in high intensity fibrin glue. Under the electron microscope, BMSCs following 4 weeks culture in fibrin glue (proportation of fibrinogen and thrombin was 41) were found, with visible cellular organs, and BMSCs had good activities. CONCLUSION: BMSCs can spread and proliferate quickly in low intensity fibrin glue. The optimal proportion of fibrinogen and thrombin is 4 1.