Comparative research for micro-push-out bond strengths of glass fiber posts treated by poly-dopamine or silane coupling agent / 北京大学学报(医学版)

ABSTRACT

Objective:To evaluate the micro-push-out bond strengths of prefabricated glass fiber posts with poly-dopamine functionalized to root dentin using resin cements, contrasted with silane treatment. Methods:In the study, 30 glass fiber posts were randomly divided into 3 groups ( 10 posts in each group) for different surface treatments. Group 1, treated with poly-dopa; Group 2, treated with silane coupling agent for 60s;Group 3, no surface treatment (Control group). The 30 extracted human, single-rooted teeth were endodontically treated and a 9 mm post space was prepared in each tooth with post drills provided by the manufacturer. Following post cementation, the specimens were stored in distilled water at 37 ℃ for 7 days. The micro-push-out bond strengths were tested using a universal testing machine (0. 5 mm/min), and the failure modes were examined with a stereomicroscope. The data of the three groups were statistically analyzed using the one-way ANOVA test(α= 0. 05). Results:The bond strengths were (7. 909 ± 1. 987) MPa for Group 1, (5. 906 ± 0. 620) MPa for Group 2, and 4. 678 ± 0. 910 MPa for Group 3 . The bond strength of poly-dopamine group was significantly higher than that of the silane group (P<0. 05). Conclusion: Contrasted with silane treatment, surface poly-dopamine functionaliza-tion was confirmed to be a more reliable method for improving the bond strength of resin luting agents to fiber posts.