BiocompatibiIity of a noveI caIcium-magnesium phosphate composite cement in dentistry / 中国组织工程研究

ABSTRACT

BACKGROUND: In our preliminary experiments, calcium phosphate cement, magnesium phosphate cement, calcium silicate and bismuth were mixed to manufacture a novel inorganic composite material, which would be used to repair furcal perforation. This novel composite cement has been confirmed to have excellent physiochemical and mechanical properties. OBJECTIVE: To study the biocompatibility of calcium phosphate-magnesium phosphate-calcium silicate-bismuth cement (CMSBC). METHODS: Cytotoxicity test Relative growth rate of L929 cells cultured in CMSBC extract was analyzed using cell counting kit-8 assay. Acute hemolysis test The leaching solution of test samples, saline and distilled water were added into the rabbit anti-clotting, to detect the rate of hemolysis.Acute systemic toxicity testCMSBC lead liquor and normal saline were respectively injected via the tail vein into the mice in experimental group and control group, respectively. The general situation of mice was observed at 24, 48, 72 hours respectively and body weight change was valued. Ames test In the flat-plate incorporation test of Salmonella typhimurium, the average number of spontaneous revertants of TA97, TA98, TA100 and TA102 of CMSBC leaching liquor was calculated after incubation at 37 ℃ for 72 hours. S-9 mixture was added to the plates as an in vitro activation system. RESULTS AND CONCLUSION:The cytotoxicity of CMSBC in vitro was grade 0.Negative results from the acute hemolytic test,acute systemic toxicity test and Ames test of CMSBC indicate that this novel inorganic composite material has good biocompatibility and biosecurity.