The effect of Er: YAG laser irradiation on bonding properties of IPS e.max CAD ceramics / 口腔疾病防治

ABSTRACT

Objective @#To investigate different ErYAG laser power settings on the bonding properties of IPS e.max CAD ceramics. @*Methods@# 96 IPS e.max CAD ceramics blocks (5 mm × 5 mm × 5 mm) were prepared and randomly divided into 8 groups (n = 12), the untreated blocks served as the control, while one of the experimental groups was treated with 4.5% HF for 20 seconds, six remaining test group (C、D、E、F、G、H) were treated with different Er YAG laser power settings 100 mJ、200 mJ、300 mJ、400 mJ、500 mJ and 600 mJ. Morphology of the ceramic surface was observed by atomic force microscopy and its shear bond strength (SBS) was tested. @*Results @#Higher shear bond strength values were found in group C-H compared to group B, the highest is group F (24.12 ± 1.91) MPa. The difference was statistically significant. The atomic force microscope observation of the surface structure showed that the control group was smooth and flat, and the HF-like etching group formed a uniform needle-like convex structure. The laser group gradually formed a regularly arranged cylindrical convex structure, in which the surface of the G and H groups was damaged. @*Conclusion @#The Er YAG laser power settings of 400 mJ can be used as an effective pretreatment method before bonding of IPS e.max CAD ceramic.