Physical properties of a new resin-based root canal sealer in comparison with AH Plus Jet
Journal of Dental Rehabilitation and Applied Science
;
: 80-87, 2017.
Article
in English
| WPRIM
| ID: wpr-80090
ABSTRACT
PURPOSE:
The aim of this study was to assess the physical properties of a novel resin-based endodontic sealer, Any-Seal, in comparison with AH Plus Jet. MATERIALS ANDMETHODS:
Flow, radiopacity and compressive strength were examined according to ISO 6876/2001. For flow test, 0.05 mL of sealer was placed between glass plate and 100 g weight were applied. Ten minutes after mixing the sealers, the load was removed and the diameters of the compressed sealer discs were measured. For radiopacity, 10 mm diameter and 1 mm thickness sample were fabricated and took radiograph with an aluminum step-wedge and analyzed using imaging program. For compressive strength test, 4 mm × 6 mm cylindrical specimen was fabricated and tested after 24 hours and 1 week using Universal testing machine.RESULTS:
Both tested sealers were consistent with ISO 6876/2001 in the flow and radiopacity test. The flow values of both sealers were not significantly different (P > 0.05). AH Plus Jet had significantly higher radiopacity (P < 0.05). AH Plus Jet showed higher compressive strength at both time intervals (P < 0.05).CONCLUSION:
Any-Seal showed low compressive strength until after 1 week, so its physical and biological aspect should be evaluated more before clinical use.
Full text:
Available
Index:
WPRIM (Western Pacific)
Main subject:
Compressive Strength
/
Dental Pulp Cavity
/
Aluminum
/
Glass
Language:
English
Journal:
Journal of Dental Rehabilitation and Applied Science
Year:
2017
Type:
Article
Similar
MEDLINE
...
LILACS
LIS