Shear bond strengths between alumina-toughened zirconia cores and veneering ceramics and their susceptibility to aging
Asian Pacific Journal of Tropical Medicine
;
(12): 402-405, 2012.
Article
in English
| WPRIM
| ID: wpr-819663
ABSTRACT
OBJECTIVE@#To evaluate the shear bond strength (SBS) between alumina-toughened zirconia (ATZ) cores and veneering ceramics, investigate the effect of aging in artificial saliva on SBS and compare it with that of yttria-stabilized tetragonal zirconia polycrystals(Y-TZP).@*METHODS@#Bars of ATZ and Y-TZP were layered with veneering ceramics in accordance to the recommendation of the manufacturer. Half of each group (n = 10) was aged at 134 °C (under 2 bar pressure) in an autoclave for 48 h. Subsequently, all specimens were subjected to shear force in a universal testing machine. The interface and fractured surface of the specimens were evaluated using scanning electron microscopy and X-ray energy dispersive spectroscopy.@*RESULTS@#The initial mean SBS values in MPa±SD were 28.9±8.0 for ATZ and 26.2±7.6 for Y-TZP. After aging, the mean SBS values for ATZ and Y-TZP were 22.9±4.9 MPa and 22.8±6.9 MPa, respectively. Neither the differences between the SBS values of the ATZ and Y-TZP groups nor the influence of aging on all groups were statistically significant.@*CONCLUSIONS@#The SBS between the ATZ core and the veneering ceramics was not affected by aging. The SBS of ATZ to veneering ceramics was not significantly different compared with that of Y-TZP.
Full text:
Available
Index:
WPRIM (Western Pacific)
Main subject:
Pharmacology
/
Reference Standards
/
Saliva, Artificial
/
Spectrum Analysis
/
Yttrium
/
Zirconium
/
Prosthesis Failure
/
Microscopy, Electron, Scanning
/
Ceramics
/
Shear Strength
Language:
English
Journal:
Asian Pacific Journal of Tropical Medicine
Year:
2012
Type:
Article
Similar
MEDLINE
...
LILACS
LIS