Preparation research on mesoporous silica-coated polypyrrole nanoparticles loaded with honokiol / 中草药
Chinese Traditional and Herbal Drugs
;
(24): 2057-2062, 2018.
Article
in Chinese
| WPRIM
| ID: wpr-851999
ABSTRACT
Objective To prepare a mesoporous silica-coated polypyrrole nanoparticles loaded with honokiol (PPy@MSN-HK) and evaluate their in vitro release behavior. Methods In this study, PPy@MSN-HK was obtained in three steps:
First, prepared polypyrrole nanoparticles; Second, coated mesoporous silica shell on its surface; Third, absorbed honokiol. The TEM, particle size, zeta potential, drug loading, infrared spectroscopy, in vitro photothermal properties, and in vitro release characteristics were chosen as indexes to investigate its potential as antitumor nanocarries. The release profiles were analyzed by simulating factor (f2), and the dissolution profiles were fitted by a variety of commonly used mathematical models. Results The results showed that the prepared nanoparticles had uniform particle size and uniform size distribution. The average particle size was (220.4 ± 4.2) nm, polydispersity coefficient was 0.042 ± 0.010, zeta potential was (-21.1 ± 0.8) mV, drug loading was (2.58 ± 0.53)%, and entrapment efficiency was (75.04 ± 0.95)%, respectively. The results of in vitro photothermal experiments showed that with the constant laser power density, the temperature change value of nanoparticles suspension increased with the increase of nanoparticles concentration. This showed that PPy@MSN have a good photothermal effect. In vitro release test revealed that the two release curves were not similar, and fitting best with Ritger-Peppas eqution and Logistic eqution respectively. Conclusion The water solution method could be used to prepare PPy@MSN, which may provide a promising drug delivery strategy for tumor treatment.
Full text:
Available
Index:
WPRIM (Western Pacific)
Type of study:
Prognostic study
Language:
Chinese
Journal:
Chinese Traditional and Herbal Drugs
Year:
2018
Type:
Article
Similar
MEDLINE
...
LILACS
LIS