ABSTRACT
Abstract Objective:
To determine diametral tensile strength and water absorption ability of Carbonate-apatite blocks fabricated from gypsum precursors (CaSO4) through a dissolution-precipitation method, with different solution molarities and immersion times. Material andMethods:
Thirty-six CaSO4 gypsum specimens with 6 mm diameter; 3 mm height (Group A for diametral tensile strength) and 36 specimens of 6 mm diameter; 3 mm thickness (Group B for water absorption ability) were used. Each group was divided into 4 group treatments of 1) dissolution-precipitation in solution of 0.5mol / L Na2CO3 + 0.5mol / L Na3PO4 for 48 hours and 72 hours; 1mol / L Na2CO3 + 1mol / L Na3PO4 for 48 hours and 72 hours. The C-Ap blocks were then tested using ATR-FTIR spectrometer to identify the formation of C-Ap functional groups. Furthermore, Group A specimens were tested for diametral tensile strength using Universal Testing Machine, and Group B specimens were tested for water adsorption ability using an analytical balance by measuring initial and final weight after immersion in saline solution at 37oC for 24 hours.Results:
The formation of carbonate-apatite (C-Ap) in groups with solution molarity of 1 mol/L for 48 hours and 72 hours resulted in a lower diametral tensile strength and water absorption ability than the groups with a 0.5 mol/L solution.Conclusion:
Solution with different molarities and dissolution-precipitation duration affect the formation of carbonate-apatite blocks.Palabras clave
Texto completo:
1
Índice:
LILACS
Asunto principal:
Resistencia a la Tracción
/
Sulfato de Calcio
/
Adsorción
/
Materiales Dentales
País/Región como asunto:
Asia
Idioma:
En
Revista:
Pesqui. bras. odontopediatria clín. integr
Asunto de la revista:
ODONTOLOGIA
Año:
2020
Tipo del documento:
Article