Calcium Hydroxide improves epoxy sealer adhesion on root dentin / O hidróxido de cálcio melhora a adesão de selante resinoso à dentina radicular
Braz. dent. sci
;
20(2): 108-113, 2017. graf, ilus
Artículo
en Inglés
| LILACS, BBO
| ID: biblio-846441
RESUMO
Objetivo:
O intuito deste estudo é avaliar a adesão de um cimento endodôntico (AH Plus) em canais radiculares após o uso de diferentes protocolos de EDTA 17% e o uso de medicação intracanal (ICM) à base de hidróxido de cálcio em veículo aquoso. Material eMétodos:
Para isso, 72 dentes humanos unirradiculares foram instrumentadas até # 50 e divididos em seis grupos (n = 12). Grupo 1 EDTA por 3 min; Grupo 2 3 mL de EDTA + 3 min de EDTA; Grupo 3 3 ml de EDTA + 3 min de EDTA + 30 segundos de agitação ultra-sônica; Grupo 4 EDTA durante 3 min + ICM; Grupo 5 3 ml de EDTA + 3 min de EDTA + ICM; Grupo 6 3 ml de EDTA + 3 min de EDTA + 30 segundos de agitaçãosônica + ICM. Os canais radiculares foram preenchidos com cimento endodôntico após cada protocolo e, após 7 dias foram preparados para o teste de push-out. Os dados foram analisados utilizando ANOVA dois fatores (p < 0,05).Resultados:
Não foi observado diferença estatística na resistência de união nos 3 diferentes protocolos de EDTA a 17%. No entanto, o uso de ICM aumentou significativamente a resistência de adesão.Conclusão:
a medicação intracanal à base de hidróxido de cálcio melhorou a resistência de união do AH Plus às paredes dentinárias, independentemente do protocolo de EDTA. (AU)ABSTRACT
Objective:
The aim of this study is to evaluate the adhesion of an endodontic sealer (AHPlus) in root canals after the use of different protocols of 17% EDTA and the use of intracanal medication (ICM) based on calcium hydroxide in aqueous vehicle. Material andMethods:
For this, 72 single-rooted human teeth were instrumented up to #50 and divided into six groups (n = 12). Group 1 EDTA for 3 min; Group 2 3 mL of EDTA + 3 min of EDTA; Group 3 3 mL of EDTA + 3 min of EDTA + 30 seconds of ultrasonic agitation; Group 4 EDTA for 3 min + ICM; Group 5 3 mL of EDTA + 3 min of EDTA + ICM; Group 6 3 mL of EDTA + 3 min of EDTA + 30 seconds of ultrasonic agitation + ICM. The root canals were filled with endodontic sealer after each protocol and after 7 days they were prepared to the push-out test. The data were analyzed using twoway ANOVA (p< 0.05).Results:
It was observed no statistically difference in bond strength in the 3 different 17% EDTA protocols. However, the use of ICM increased significantly the resistance adhesion.Conclusion:
Intracanal medication based on calcium hydroxide improved the bond strength of AHPlus to dentin walls, regardless of the EDTA protocol. (AU)
Texto completo:
Disponible
Índice:
LILACS (Américas)
Asunto principal:
Hidróxido de Calcio
/
Ácido Edético
/
Dentina
Límite:
Humanos
Idioma:
Inglés
Revista:
Braz. dent. sci
Asunto de la revista:
Odontología
/
Sa£de Bucal
Año:
2017
Tipo del documento:
Artículo
País de afiliación:
Brasil
Institución/País de afiliación:
São Paulo State University/BR
Similares
MEDLINE
...
LILACS
LIS