Efeito da termociclagem sobre a rugosidade de reembasadores resilientes / Effect of thermocycling on surface roughness of soft denture liners
Rev. odontol. UNESP (Online)
;
39(4): 213-218, jul.-ago. 2010. tab
Artículo
en Portugués
| LILACS, BBO
| ID: biblio-874544
RESUMO
Objetivo:
Este estudo buscou avaliar o efeito do armazenamento em água e da termociclagem sobre a rugosidade de reembasadores resilientes. Material emétodo:
Quatro reembasadores resilientes (Ufi-gel P, Dentuflex, Trusoft e Dentusoft) foram selecionados. Os materiais foram preparados de acordo com as instruções dos fabricantes e colocados em matrizes vazadas com 20 mm de diâmetro e 5 mm de espessura. Cinco corpos de prova de cada resina foram fabricados e a rugosidade superficial (Ra) foi avaliada de acordo com os seguintes grupos experimentais GC (grupo controle) imediatamente após a confecção das amostras; GA após armazenamento em água destilada a 37 °C por 24 horas; GT após termociclagem. Os resultados foram submetidos à análise de variância de dois fatores, seguida do teste de Tukey (a = 0,05).Resultado:
A resina Ufigel P apresentou menores valores de rugosidade (p = 0,000368) em relação aos outros materiais. No período inicial de avaliação (GC) e após 24 horas de armazenamento em água (GA), não houve alteração da rugosidade para todos os materiais testados (p > 0,05). Após a termociclagem, houve aumento significativo da rugosidade apenas para o reembasador Dentusoft (p = 0,000368).Conclusão:
A ciclagem térmica aumentou os valores de rugosidade para a resina Dentusoft, não havendo qualquer alteração para os demais materiais.ABSTRACT
Purpose:
This study evaluated the effect of storage in water and thermocycling on roughness of reline materials. Material andmethod:
Four reline materials (Ufi-gel P, Dentuflex, Trusoft and Dentusoft) were selected. The materials were prepared according to the manufacturers' instructions and were placed in stainless steel moulds (20 mm in diameter and 5 mm thick). Five samples of each resin were made (n = 5) and roughness (Ra) analyses according to the following experimental conditions GC (control group) immediately after specimen preparation; GA after storage in distilled water at 37 °C for 24 hours; GT after thermocycling. Data were submitted to 2-way ANOVA followed by Tukey's test (a = 0.05).Result:
Ufigel P resin had smaller surface roughness values (p = 0.000368) than the other ones. The initial period of evaluation (GC) and storage in water (GA) did not change roughness of the tested materials (p > 0.05). There was a significant increase in roughness after thermocycling only for Dentusoft (p = 0.000368).Conclusion:
Thermocycling increased the roughness of the Dentusoft, with no change to the other materials.
Texto completo:
Disponible
Índice:
LILACS (Américas)
Asunto principal:
Resinas Acrílicas
/
Resorción Ósea
/
Técnicas In Vitro
/
Análisis de Varianza
/
Alineadores Dentales
Idioma:
Portugués
Revista:
Rev. odontol. UNESP (Online)
Asunto de la revista:
Odontología
Año:
2010
Tipo del documento:
Artículo
País de afiliación:
Brasil
Institución/País de afiliación:
Universidade Estadual de Ponta Grossa/BR
Similares
MEDLINE
...
LILACS
LIS