Solvent capacity of different substances on gutta-percha and Resilon

ABSTRACT

The aim of this study was to evaluate the effectiveness of 3 solvents (eucalyptol, orange oil, and xylol) on 2 types of gutta-percha (conventional and thermoplastic) and Resilon. Specimens (10 mm diameter x 1 mm thick; n=7 per condition) were prepared and maintained at 37ºC for 48 h. Each specimen was weighed on a precision scale every 24 h until its mass was stable, at which time the initial mass was determined. Specimens (n=7) were then immersed in the solvent solutions and, after 48 h at 37ºC, they were reweighed at 24- h intervals, until stabilization (final mass). The difference between the final and the initial mass determined the solvent capacity of each solvent. Data were subjected to analysis of variance and Tukey's test at 5 percent significance level. The results demonstrated that xylol was the most effective, especially on conventional gutta-percha and Resilon (p<0.05). Eucalyptol and orange oil were more effective on thermoplastic gutta-percha than the other materials (p<0.05). It was concluded that all evaluated substances presented solvent action, but xylol was the most effective on both gutta-percha or Resilon.

RESUMO

O objetivo deste estudo foi avaliar a efetividade de 3 solventes em 2 tipos de guta-percha e no Resilon. Os materiais avaliados foram guta convencional (Endo points), guta termoplastificada (Endo points TP) e cones de Resilon (RE). Amostras circulares medindo 10 mm de diâmetro e 1 mm de espessura foram preparadas, sendo mantidas a 37°C por 48 h. Cada amostra, com o anel metálico, foi pesada em uma balança de precisão a cada 24 h até estabilização da massa, quando a massa inicial era determinada. As amostras (n=7) foram imersas, então, nas soluções solventes avaliadas (eucaliptol, óleo de laranja, e xilol). Após 48 h a 37ºC, as amostras foram pesadas outra vez a cada 24 h, até a estabilização (massa final). A diferença entre a massa final e inicial determinou a capacidade solvente de cada material. Os dados foram submetidos à análise de variância em nível de significância de 5 por cento e teste de Tukey. Os resultados demonstraram que o xylol foi mais eficaz solvente, especialmente na guta convencional e no Resilon (p<0,05). O eucaliptol e o óleo de laranja foram mais eficazes sobre a guta thermoplastificada em relação aos outros materiais obturadores (p<0,05). Conclui-se que todas as substâncias testadas apresentam ação solvente, contudo, o xilol foi o mais efetivo sobre a guta-percha ou Resilon.