Shear bond strength of metallic brackets bonded with a new orthodontic composite
Braz. j. oral sci
;
8(2): 76-80, Apr.-June 2009. tab, graf
Artículo
en Inglés
| LILACS, BBO
| ID: lil-556468
ABSTRACT
Aim:
The aim of this study was to assess the shear bond strength of orthodontic brackets in different enamel surfaces using the Transbond Plus Color Change composite (TPCC-3M Unitek), and to analyze the Adhesive Remnant Index (ARI).Methods:
Seventy-two human premolars were divided into six groups (n = 12), as follows Group 1(control) - Transbond XT conventional; in Groups 2 to 6, TPCC was used under the following enamel treatment conditions phosphoric acid and XT-primer; Transbond Plus Self-Etching Primer (TPSEP); phosphoric acid only; phosphoric acid, XT-primer and saliva; and TPSEP and saliva, respectively. Twenty-four hours after bonding, the brackets were debonded with an Instron machine at a crosshead speed of 0.5 mm/min, and ARI was evaluated by using a stereoscopic magnifying glass.Results:
The mean shear strength values (MPa) for Groups 1 to 6 were 24.6, 18.7, 17.5, 19.7, 17.5 and 14.8, respectively. Data were submitted to ANOVA and Tukey's test (α = 0.05). Group 1 had significantly higher shear bond strength values than Groups 3, 5, and 6 (p < 0.05), but did not differ significantly from Groups 2 and 4 (p > 0.05). No statistically significant differences (p > 0.05) were found between Groups 2, 3, 4, 5 and 6.Conclusions:
Bracket bonding using TPCC showed adequate adhesion for clinical use, and the type of enamel preparation had no influence.
Texto completo:
Disponible
Índice:
LILACS (Américas)
Asunto principal:
Técnicas In Vitro
/
Recubrimiento Dental Adhesivo
/
Soportes Ortodóncicos
/
Cementos de Resina
/
Resistencia al Corte
Límite:
Humanos
Idioma:
Inglés
Revista:
Braz. j. oral sci
Asunto de la revista:
Odontología
Año:
2009
Tipo del documento:
Artículo
País de afiliación:
Brasil
Institución/País de afiliación:
Universidade Estadual de Campinas (Unicamp)/BR
Similares
MEDLINE
...
LILACS
LIS