Comparison of the radiodensity of luting materials / Comparação da radiodensidade de materiais cimentantes
Feitosa, Fernando Alves; Oliveira, Michele de; Rodrigues, José Augusto; Cassoni, Alessandra; Reis, André Figueiredo.
  • Feitosa, Fernando Alves; Guarulhos University. Department of Restorative Dentistry. Guarulhos. BR
  • Oliveira, Michele de; Guarulhos University. Department of Restorative Dentistry. Guarulhos. BR
  • Rodrigues, José Augusto; Guarulhos University. Department of Restorative Dentistry. Guarulhos. BR
  • Cassoni, Alessandra; Guarulhos University. Department of Restorative Dentistry. Guarulhos. BR
  • Reis, André Figueiredo; Guarulhos University. Department of Restorative Dentistry. Guarulhos. BR
Rev. odontol. UNESP (Online) ; 40(6): 285-289, nov.-dez. 2011. ilus, tab
Artículo en Inglés | LILACS, BBO | ID: lil-621550
RESUMO
O objetivo desse estudo foi avaliar a radiodensidade de 7 cimentos resinosos Panavia F (PA- Kuraray Medical), Enforce (En- Dentsply Latin America), Ecolink (Ek-Ivoclar Vivadent), Rely X ARC (Re-3M ESPE), Rely X Unicem (Un-3M ESPE), Multlink (Mk-Ivoclar Vivadent) e Variolink II (Vk-Ivoclar Vivadent). Os cimentos foram manipulados de acordo com as instruções dos fabricantes e inseridos em uma matriz acrílica de 1 × 1 × 10 mm3 (n = 8) e foto ativados por 40 segundos com luz halógena (750 mW.cm elevado a -2, Optilux 501). Após 24 horas de armazenamento no escuro em umidade relativa à 37 °C por 24 horas, os espécimes foram posicionados sobre filmes radiográficos juntamente com uma escala de alumínio. Os filmes foram expostos ao raio X com 60 kV, 10 mA, com a distância foco filme de 10 cm por 0,7 segundos. Os filmes foram revelados e a radiodensidade dos espécimes foi avaliada qualitativamente por ranqueamento utilizando-se os degraus da escala de alumínio, atribuindo do escore 1 para o mais radiolucente ao escore 10 para o mais radiopaco. Os dados foram analisados pelo teste de Kruskal-Wallis e de Dunn (p < 0,05). A mediana obtida para cada cimento foi Pa= 2ª, En= 3ª; Ec= 3ª; Re= 3,5ª, Un= 4ab; Mk= 7b; Vk = 8b (medianas seguidas por diferentes letras indicam diferença estatística significante). Pôde-se concluir que os cimentos resinosos apresentam diferentes níveis de radiodensidade. O Panavia F, Enforce, Ecolink, and Rely X ARC foram os mais radiolucentes, o Unicem apresentou radiodensidade intermediária, e o Multilink e o Variolink II foram os cimentos que apresentaram maior radiopacidade.
ABSTRACT
The aim of this study was to evaluate the radiodensity of 7 resin cements Panavia F (PA- Kuraray Medical), Enforce (En-Dentsply Latin America), Ecolink (Ek-Ivoclar Vivadent), Rely X ARC (Re- 3M ESPE), Rely X Unicem (Un?3M ESPE), Multlink (Mk- Ivoclar Vivadent) and Variolink II (Vk- Ivoclar Vivadent). The cements were mixed according to manufacturer's instructions and inserted into 1 × 1 × 10 mm3 (n = 8) acrylic molds and photo-activated for 40 seconds with halogen light (750 mW.cm to the -2 power, Optilux 501). After 24 hours of storage in relative humidity at 37 °C in a dark box for 24 hours, the specimens were positioned on the X ray films with an aluminum scale. The film was exposed to 60 kV and 10 mA X ray, with a focus-film distance of 10 cm for 0.7 seconds. The films were revealed and the radiodensity of the specimens was evaluated qualitatively by ranking according to the scale steps, with rank 1 for the most radiolucent to rank 10 for the most radiopaque. The data were submitted to Kruskal-Wallis and Dunntests (p < 0.05). The median obtained for each cement was Pa= 2ª, En= 3ª; Ec= 3ª; Re= 3.5ª, Un= 4ab; Mk= 7b; Vk= 8b (medians followed by different letters differ among them). It can be concluded that resin cements showed different degrees of radiodensity. Panavia F, Enforce, Ecolink, and Rely X ARC were the most radiolucent, Unicem presented intermediary radiodensity, and Multilink and Variolink II were the most radiopaque cements.
Asunto(s)

Texto completo: Disponible Índice: LILACS (Américas) Asunto principal: Rayos X / Radiografía Dental / Estadísticas no Paramétricas / Cementos de Resina / Cementos Dentales Idioma: Inglés Revista: Rev. odontol. UNESP (Online) Asunto de la revista: Odontología Año: 2011 Tipo del documento: Artículo País de afiliación: Brasil Institución/País de afiliación: Guarulhos University/BR

Similares

MEDLINE

...
LILACS

LIS

Texto completo: Disponible Índice: LILACS (Américas) Asunto principal: Rayos X / Radiografía Dental / Estadísticas no Paramétricas / Cementos de Resina / Cementos Dentales Idioma: Inglés Revista: Rev. odontol. UNESP (Online) Asunto de la revista: Odontología Año: 2011 Tipo del documento: Artículo País de afiliación: Brasil Institución/País de afiliación: Guarulhos University/BR