Regional bond strengths to root canal dentin of fiber posts luted with three cementation systems

ABSTRACT

This study evaluated the influence of the cementation system on the regional push-out bond strength and failure pattern of fiber posts to radicular dentin. The roots of 48 extracted human incisors were prepared and divided into 3 groups (n=16), according to the cementation system AdperScotchbond Multi-Purpose + resin cement RelyX ARC (SBMP+ARC); Adper SingleBond 2 + RelyX ARC (SB+ARC) and; RelyX U100 self-adhesive resin cement (U100). The posts were cemented as per manufacturer’s instructions for each cementation system. After 1 week, the roots were sectioned transversely into 6 discs. Two discs were obtained from the cervical, middle and apical thirds and the push-out test was carried out. The failure pattern was examined on all debonded specimens. The data were analyzed by two-way repeated measures ANOVA and Tukey’s test. When U100 was used, no statistically significant difference (p>0.05) was observed among the different root regions. Statistically higher push-out bond strength values were detected in the cervical third for SBMP+ARC and SB+ARC (p<0.05). The U100 showed significantly more mixed failures than SBMP+ARC in the apical third (p<0.05). In conclusion, the self-adhesive cement RelyX U100 was the only cement not sensitive to the root canal region.

RESUMO

Esse estudo avaliou a influência do sistema de cimentação na resistência de união regional e os padrões de fratura de pinos de fibra à dentina radicular. As raízes de 48 incisivos humanos extraídos foram preparadas e divididas em 3 grupos (n=16) de acordo com o sistema de cimentação AdperScotchbond Multi-Purpose + cimento resinoso RelyX ARC (SBMP+ARC); AdperSingle Bond 2 + RelyX ARC (SB+ARC) e cimento resinoso autoadesivo RelyX U100 (U100). Os pinos foram cimentados conforme as recomendações dos fabricantes para cada sistema de cimentação. Após uma semana, as raízes foram seccionadas transversalmente em 6 discos. Dois discos foram obtidos para os terços coronário, médio e apical e o teste de push-out foi realizado. O padrão de fratura foi avaliado em todos os espécimes. Os dados obtidos foram analisados através dos testes ANOVA dois fatores e Tukey. Quando o cimento U100 foi testado, não foram observadas diferenças significativas (p>0,05) entre as diferentes regiões radiculares. Valores de resistência de união significativamente superiores foram encontrados no terço coronário para SBMP+ARC e SB+ARC (p<0,05). O U100 apresentou significativamente mais fraturas mistas que o SBMP+ARC no terço apical (p<0,05). Conclui-se que o cimento resinoso autoadesivo RelyX U100 foi o único cimento não afetado pela região do canal radicular.