Avaliação do efeito de diferentes lasers de alta intensidade no tratamento de superfície da cerâmica Y-TZP pré e pós sinterização / Effect evaluation of different high-intensity lasers on the surface treatment of Y-TZP ceramic before and after sintering

RESUMO

O objetivo deste estudo foi avaliar os efeitos dos lasers de NdYAG, CO2 e Er,CrYSGG no tratamento de superfície da cerâmica Y-TZP antes e depois da sinterização final, por meio de Microscopia Eletrônica de Varredura (MEV), mensuração da rugosidade de superfície (Ra) e teste de resistência adesiva por microcisalhamento (RAD). Para tanto, barras de Y-TZP foram confeccionadas e distribuídas entre as 3 fases do experimento, sendo as duas primeiras fases seletivas para a identificação dos parâmetros lasers a serem utilizados na fase 3 de análise da RAD. Na fase 1 MEV - foram testados parâmetros que variavam entre 50 e 100 mJ para o laser de NdYAG, 2 a 4W para o laser de CO2 e 1 a 3,5W para o laser de Er,CrYSGG, testados antes ou após a sinterização da Y-TZP. Observou-se que a maioria dos tratamentos foram capazes de promover alterações na cerâmica com diferentes intensidades dependendo do parâmetro utilizado. Para a fase 2 Ra foram selecionados apenas os tratamentos com os lasers de NdYAG e Er,CrYSGG aplicados antes da sinterização da cerâmica, sendo que cada laser foi avaliado individualmente e comparados ao tratamento de superfície com o sistema Rocatec. Os tratamentos com os maiores valores de Ra foram para o laser de NdYAG - 1,6W-20Hz (11.623±3,419) e para o laser de Er,CrYSGG - 3W (6,051±1,991).

ABSTRACT

The aim of this study was to evaluate the effects of NdYAG, CO2 and Er,CrYSGG lasers on the surface treatment of Y-TZP ceramic before and after the final sintering by means of Scanning Electron Microscope (SEM), surface roughness measurement (Ra) and microshear bond strength adhesive resistance test (RAD). In order to do so, Y-TZP bars were produced and distributed among the three experimental phases, being the two first ones selective in what regards identifying parameters for the lasers used in phase 3 of the RAD analysis. In phase 1 SEM parameters varying from 50 to 100 mJ were tested for the NdYAG laser, from 2 to 4W for the CO2 laser and from 1 to 3,5W for the Er,CrYSGG laser, either before or after the Y-TZP sintering. It was observed that most treatments were able to promote changes in the ceramic with varied intensity according to the parameter used. In phase 2 Ra only treatments with NdYAG and Er,CrYSGG lasers applied before ceramic sintering were selected, and each laser was individually evaluated and compared to the surface treatment with Rocatec system. The treatments which had the highest Ra values were 1,6W-20Hz (11.623±3,419) for the NdYAG laser and 3W (6,051±1,991) for Er,CrYSGG. Rocatec system showed the lowest roughness levels (1,297±0,026). As for phase 3 of the study RAD the highest Ra parameters for each laser were selected as well as the parameter with favorable characteristics to adherence observed in phase 1 SEM.