Post-curing conversion kinetics as functions of the irradiation time and increment thickness
J. appl. oral sci
;
21(2): 190-195, Mar-Apr/2013. tab, graf
Artículo
en Inglés
| LILACS
| ID: lil-674365
ABSTRACT
Objective:
This study evaluated the variation of conversion degree (DC) in the 12 hours following initial photoactivation of a low-shrinkage composite resin (Venus Diamond). Material andMethods:
The conversion degree was monitored for 12 hours using Attenuated Total Reflection (ATR) F-TIR Spectroscopy. The composite was placed in 1 or 2 mm rings and cured for 10 or 20 seconds with a LED lamp. ATR spectra were acquired from the bottom surface of each sample immediately after the initial photoactivation (P=0), 30 minutes (P=0.5) and 12 hours after photoactivation (P=12) in order to obtain the DC progression during the post-curing period. Interactions between thickness (T), irradiation time (I) and post-curing (P) on the DC were calculated through ANOVA testing.Results:
All the first order interactions were statistically significant, with the exception of the T-P interaction. Furthermore, the shift from P=0 to P=0.5 had a statistically higher influence than the shift from P=0.5 to P=12. The post-curing period played a fundamental role in reaching higher DC values with the low-shrinkage composite resin tested in this study. Moreover, both the irradiation time and the composite thickness strongly influenced the DC.Conclusions:
Increased irradiation time may be useful in obtaining a high conversion degree (DC) with a low-shrinkage nano-hybrid composite resin, particularly with 2 mm composite layers.
Texto completo:
Disponible
Índice:
LILACS (Américas)
Asunto principal:
Resinas Compuestas
/
Nanocompuestos
/
Luces de Curación Dental
Tipo de estudio:
Estudios de evaluación
Límite:
Humanos
Idioma:
Inglés
Revista:
J. appl. oral sci
Asunto de la revista:
Odontología
Año:
2013
Tipo del documento:
Artículo
País de afiliación:
Italia
Institución/País de afiliación:
University of Turin/IT
Similares
MEDLINE
...
LILACS
LIS