Adhesion and formation of tags from MTA Fillapex compared with AH Plus® cement
RSBO (Impr.)
;
11(1): 71-76, Jan.-Mar. 2014. ilus, graf, tab
Artículo
en Inglés
| LILACS
| ID: lil-718009
ABSTRACT
Introduction and Objective:
The aim of this study was two-fold 1) to evaluate, in vitro, the shear bond strength of two sealers by push-out test and 2) to assess the failures after displacement. Additionally, the formation of tags was observed by SEM. Material andmethods:
Forty mandibular premolars were selected and the canals were subjected to biomechanical preparation with rotary instruments. These specimens were divided into two groups according to the sealer (n = 20) GI - MTA Fillapex and GII - AH Plus. All roots were filled with sealer only, without gutta-percha. After a period corresponding to three times the setting time of the sealer, the roots were sectioned transversely into slices of 1 mm thickness, to obtain one slice from the cervical third, to be used in the push-out test. Following, two slices of each group were randomly chosen for ultrastructural analysis by scanning electron microscopy (SEM). The data obtained in shear bond strength test were subjected to statistical analysis.Results:
AH Plus cement exhibited higher shear bond strength values (1.332±0.75 MPa) than MTA Fillapex (0.071±0.07 MPa), with statistically significant differences.Conclusion:
MTA Fillapex has a low bond strength with less formation of tags than AH Plus.
Texto completo:
Disponible
Índice:
LILACS (Américas)
Idioma:
Inglés
Revista:
RSBO (Impr.)
Asunto de la revista:
Odontología
Año:
2014
Tipo del documento:
Artículo
País de afiliación:
Brasil
Institución/País de afiliación:
Positivo University/BR
Similares
MEDLINE
...
LILACS
LIS