Efeito da adição de partículas de vidro niobofosfato bioativo à guta-percha: desenvolvimento, caracterização, resistência de união à dentina e influência na formação de biofilmes microbianos / Effect of the addition of the niobophosphate bioactive glass in the gutta-percha: Development, characterization, bond strength to dentin and influence on biofilm formation

RESUMO

Os objetivos deste estudo foram desenvolver e caracterizar um compósito para obturação endodôntica à base de guta-percha e vidro niobofosfato. Foi avaliado a resistência de união à dentina radicular do compósito experimental, da guta EndoSequence BC, ambos sem o uso de cimento além do cimento AH Plus associado a guta-percha através do ensaio de push-out. A análise dos padrões de fratura foi realizada com auxílio de MEV. Análises usando EDX and MEV-EDS foram realizadas para verificar a composição e distribuição das partículas de vidro na superfície e no interior da matriz de guta-percha dos materiais testados. Os resultados foram analisados estatisticamente pelos testes ANOVA e Tukey, sendo considerado significante quando p < 0,05. Foi avaliado também a influência do compósito experimental, do vidro niobofosfatos bioativo, diferentes tipos de gutapercha e hidroxiapatita na adesão e formação de biofilme por bactérias orais com coloração Live/dead usando um microscópio confocal à laser. O biofilme multiespécies foi formado na superfície de discos de hidroxiapatita - HA, vidro niobofosfato - VNB, guta-percha Obtura - OBT, guta-percha Protaper - PTP, EndoSequence BC guta-percha - GBC e o compósito experimental guta-percha associado com o vidro niobofosfato - GNB. O biovolume total (mm3), biovolume de bacterias viáveis (mm3), e porcentagem de bactérias viáveis (%) foram quantificados...

ABSTRACT

The objectives of this study were to develop and characterize a composite for endodontic obturation based gutta-percha and niobium phosphate glass. The study evaluated the composites micropush-out bond strength to root dentine of the experimental gutta-percha and niobium phosphate glass composite applied with thermoplastic technique to the root canals without sealer in a moist environment and compare to the conventional root canal obturation Ah Plus and gutta-percha, and a commercial bioceramic gutta without sealer. Additionally, the cores materials were characterized using Scanning Electron Microscopic/Energy-dispersive X-ray (SEM/EDS) and Energy Dispersive X-ray fluorescence spectrometry (EDX) analysis. The failure mode was analyzed with SEM. Analysis using EDX and SEMEDS was carried out to verify the composition and distribution of the particles of the tested materials. Data were statistically analyzed by one-way ANOVA and Tukeys test (p < 0,05). Also was analysed the influence of different types of gutta-percha and bioactive niobium phosphate glass on the adherence and biofilm formation by oral bacteria from human dental plaque with Live/dead staining assay using confocal laser scanning microscopy (CLSM). The multispecies biofilm was grown from plaque bacteria on discs of hydroxyapatite - HA, niobium phosphate bioactive glass- VNB, Obtura pellets - OBT, Protaper gutta-percha - PTP, EndoSequence BC gutta-percha - GBC and gutta-percha associated with niobium phosphate glass - GNB in brain-heart infusion broth for 3,14 and 30 days. After the growth induction periods, specimens were stained by using Live/Dead, and the images were analyzed under a CLSM...